The influence of burnishing on surface texture of regenerative NIAL-15%AL2O3 plasma sprayed coatings

• Autorzy: Starosta R.
• Języki publikacji: EN

Abstrakty

EN

The purpose of this study was the selection of roller- burnishing parameters of surface Ni-Al-15%Al2O3 composite coatings obtained by "PN 120" plasma torch. Coatings with low surface roughness could be applied as layers increase the service life of torque pumps shaft used on vessels in the sea water systems. After turning, the average surface roughness of plasma sprayed Ni-5%Al-15%Al2O3 coatings was Ra = 1.06 mikro-m. Their average hardness was equal to the 272 HV 2. After pre-treatment, plasma sprayed Ni-Al- 15%Al2O3 coatings were burnishing. Burnishing parameters were as follows: Vn=28,26 m/min, Fn=700N, fn=0,044 m/rev. Burnishing reduces the surface roughness of coatings as compared to machining. After the plastic working, the Ra parameter was reduced to a value of 0.77 m. Total height of waviness profile of machined coatings was 6.23 m. After burnishing, the value of Wt decreased by 0.22 m, to the value of 6.01 m. Studies burnished surface topography of coatings of Ni-5% Al15%Al2O3 overlaid by "PN 120" torch revealed the presence of defects stereometric structure. There are the spalling. After plastic working of plasma coatings, decrease of parameters of the material ratio curve values were observed. For example, the reduced peak height of cut coatings were 1.11 m, after burnishing Rpk value fell to 0.64 mikrom.

Słowa kluczowe

EN

plasma spraying; burnishing; Ni-Al-15%Al2O3 coatings; regenerative coatings; torque pump

• Wydawca: Faculty of Ocean Engineering and Ship Technology, Gdańsk University of Technology
• Czasopismo: Journal of Polish CIMAC
• Rocznik: 2012
• Tom: Vol. 7, no 3
• Strony: 275--283
• Opis fizyczny: Bibliogr. 11 poz., rys., tab.

Twórcy

autor

Starosta R.

• Gdynia Maritime University, Department of Marine Maintenance Morska Street 81-87, 81-225 Gdynia, Poland tel.[phone], fax [phone],

Bibliografia

• [1] Kung-Hsu, H., Ming-Chang, J., Ming-Der, G., A study on the wear resistance characteristics of pulse electroforming Ni–P alloy coatings as plated, Wear, Vol. 265, pp. 833-844, 2007.
• [2] Bolelli, G., Cannillo V., Lusvarghi L., Ricco S. Mechanical and tribological properties of electrolytic hard chrome and HVOF-sprayed coatings, Surface and Coatings Technology, Vol. 200, pp. 2995 – 3009, 2006.
• [3] DuraSpindle, Increasing performance, Information materials MAN B&W, 2005.
• [4] Franzen, V., Trompeter, M. Brosius, A., Tekkaya A. E., Finishing of thermally sprayed tool coatings for sheet metal forming operations by roller burnishing, Int J Mater Form, Vol. 3, pp. 147-150, 2010.
• [5] Franzen, V., Witulski, J., Brosius, A., Trompeter, M., Tekkaya, A.E., Thermally sprayed coatings as effective tool surfaces in sheet metal forming applications, Journal of Thermal Spray Technology, Vol. 20, pp. 939 -947, 2011.
• [6] Dyl, T., Starosta, R., Skoblik, R., The effect of the unit pressure on the NiAl and Ni3Al intermetallic coatings selection parameters after plastic working, Solid State Phenomena, Vol. 165, pp.19-24, 2010.
• [7] Szczepanik, S., Przeróbka plastyczna materiałów spiekanych z proszków i kompozytów, Uczelniane Wydawnictwa Naukowo-Dydaktyczne Akademii Gorniczo-Hutniczej, Krakow 2003.
• [8] Szczepanik, S., Polowski, W., Czechowski, K., Wojtaszek, M., Krawiarz, J., Badania możliwości zastosowania nagniatania tocznego do obróbki wykańczającej kompozytów Al-SiC. Kompozyty, Vol. 7: 2, pp. 87-92, 2007.
• [9] Nadasi, E., Nowoczesne metody metalizacji natryskowej, Wydawnictwa Naukowo-Techniczne, Warszawa 1975.
• [10] Starosta, R., Wądołowski, D., Wpływ nagniatania na wybrane własności powłok natryskiwanych metodą „ROTO-TECK”. Zeszyty Naukowe. Akademia Marynarki Wojennej. Vol. 178A, pp. 275-280, 2009.
• [11] Sandvik Coromant. Katalog główny. Toczenie –frezowanie –wiercenie –wytaczanie –systemy narzędziowe, Sandviken, pp. A39-A40, 2007.