Influence of temperature and total strain on the fatigue damage of cast steel

• Autorzy: Mroziński S. , Skocki R.
• Języki publikacji: EN

Abstrakty

EN

The paper presents test results of the course of fatigue damage of the GX12CrMoVNbN9 in conditions of the constant-amplitude loadings. As the parameter of fatigue damage there was assumed the change of mechanical properties which was determined in various stages of fatigue life. Three stages with a different rate of growth of the fatigue damage parameter were distinguished in the course of fatigue damage. It was stated that the critical value for the fatigue damage parameter depends on the level of loading and temperature.

Słowa kluczowe

EN

cyclic properties; fatigue life; fatigue damage; martensitic cast steel

• Wydawca: Faculty of Ocean Engineering and Ship Technology, Gdańsk University of Technology
• Czasopismo: Journal of Polish CIMAC
• Rocznik: 2012
• Tom: Vol. 7, no 1
• Strony: 167--173
• Opis fizyczny: Bibliogr. 12 poz., rys., tab.

Twórcy

autor

Mroziński S.

autor

Skocki R.

• University of Technology and Life Sciences in Bydgoszcz, Faculty of Mechanical Engineering, Al. Prof. S. Kaliskiego 7, 85-789 Bydgoszcz,

Bibliografia

• [1] Chakraborti, P.C.; Mitra, M.K., Room temperature low cycle fatigue behaviour of two high strength lamellar duplex ferrite–martensite (DFM) steels. International Journal of Fatigue, Volume: 27, Issue: 5, 2005, pp. 511-518.
• [2] Colins J.A., Failure of Materials In Mechanical Design. Analysis, Prediction, Prevention. John Wiley & Sons, New York 1993.
• [3] Fatemi A., Yang L., Cumulative Fatigue Damage and Life Prediction Theories: A Survey of the State of the Art for Homogeneous Materials. International Journal of Fatigue 20(1), 1998, pp. 9-34,
• [4] Lemaitre J., A Course on Damage Mechanics, Springer Verlag, 1996.
• [5] Kukla D., Dietrich L., Ciesielski M., Ocena stopnia uszkodzenia eksploatacyjnego materiału rurociągu parowego na podstawie analizy zmian właściwości zmęczeniowych i mikrostruktury. VI Międzynarodowe Sympozjum Mechaniki Materiałów i Konstrukcji, Augustów, 2011.
• [6] Socha G., Prediction of the fatigue life on the basis of damage progress rate curves. International Journal of Fatigue. Vol. 26, No 4. 2004, pp. 339-347.
• [7] Kurzydłowski J., Spychalski W. oraz inni., Research on possibilities of application of nondestructivetesting in degradation evaluation of materials used in infrastructure working under the influence of aggressive hydrogen environment. 3rd International Conference on Environmental degradation of Engineering Materials. Gdańsk Jastrzębia Góra, 2007.
• [8] Cheng Y. S, Huang Y., Measurement of Continuous Damage Parameter, Engineering Fracture Mechanics, Vol 31(6), 1988, pp. 985-992,
• [9] Piechnik S., Pachla H., Law of Continuous damage Parameter for Non-Ageing Materials, Engineering Fracture Mechanics, Vol. 12, 1979, pp. 199-209.
• [10] Mroziński S., Skocki R., Wrażliwość parametrów pętli histerezy na zmiany właciwości cyklicznych. XXIV Sympozjum Zmęczenia i Mechaniki Pękania, Bydgoszcz –Pieczyska 2012, pp. 105-106.
• [11] Mroziński S., Stabilizacja własności cyklicznych metali i jej wpływ na trwałość zmęczeniową. Wydawnictwo Uczelniane Uniwersytetu Technologiczno-Przyrodniczego, Rozprawy Nr 128, Bydgoszcz, 2008.
• [12] PN-84/H-04334 Badania niskocyklowego zmęczenia metali.