Empirical examination of the impact of the cycle asymmetry coefficient of the load on the fatigue life of S355J0 steel

• Autorzy: Szala G.
• Języki publikacji: EN

Abstrakty

EN

In the calculations of the fatigue life of structural components subjected in service load conditions to stochastic loads the load spectra being a set of sinusoidal cycles of different asymmetry occur. The cycle asymmetry is characterized by the asymmetry coefficient R=Smin/Smax In the case of load mentioned above, R coefficient changes in wide limits. In the work the empirical examinations of the impact of the cycle asymmetry coefficient of the load on the fatigue limit of S355J0 steel are presented.

Słowa kluczowe

EN

fatigue life; two-parametric characteristics; S355J0 steel

• Wydawca: Faculty of Ocean Engineering and Ship Technology, Gdańsk University of Technology
• Czasopismo: Journal of Polish CIMAC
• Rocznik: 2010
• Tom: Vol. 5, no 3
• Strony: 207--214
• Opis fizyczny: Bibliogr. 2 poz., rys., tab.

Twórcy

autor

Szala G.

• University of Technology and Life Sciences in Bydgoszcz ul. Prof. Kaliskiego 7 85-789 Bydgoszcz, Poland tel.: [phone], fax: [phone],

Bibliografia

• [1] Ligaj, B., Wpływ wybranych programów obciążeń wygenerowanych na podstawie tablicy korelacyjnej na trwałość zmęczeniową stali 18G2A, Problemy Eksploatacji – Zeszyty Naukowe 3/2007 (66), ss. 129-146.
• [2] Ligaj, B., Szala, G., Uogólnienie wykresu zmęczeniowego Goodmana na zakres wysokocyklowego zmęczenia, Materiały XXIII Sympozjum Zmęczenia i Mechaniki Pękania, Bydgoszcz – Pieczyska, 2010.