Changes of properties of Co66Ni12Si9B13 metallic glass in process devitryfication

• Autorzy: Jakubczyk E. , Jakubczyk M. , Kapuśniak J.
• Konferencja: XIth International Seminar on Physics and Chemistry of Solids (11 ; 2005 ; Polska)
• Języki publikacji: EN

Abstrakty

EN

Isochronal annealing during 4h at different temperatures (573 ÷ 823 K) of samples of Co66Ni12Si9B13 metallic glass leads to the creation in the amorphous matrix three crystalline phases, i.e. at the temperature 673K phases α -(Co,Ni) and at the temperature 773K phase (Co,Ni)3B and (Co,Ni)2B. The result of the applied thermal treatment of the samples was their complete crystallization. The process of the annealing of the alloy leads to the systematic decrease of the electrical resistivity, Hall resistivity and the spontaneous Hall coefficient, and the creation of the crystalline phase is related to abrupt value decrease of these parameters. The calculations by quantum chemistry method confirm sequence and verify the composition of the created phases. The growth of gram sice of formed phases were observed by the optical microscope.

Słowa kluczowe

EN

devitryfication; Co66Ni12Si9B13; metallic glass

• Wydawca: Wydawnictwo Uniwersytetu Humanistyczno-Przyrodniczego im. Jana Długosza w Częstochowie
• Czasopismo: Prace Naukowe. Chemia i Ochrona Środowiska / Akademia im. Jana Długosza w Częstochowie
• Rocznik: 2005
• Tom: Vol. 10
• Strony: 149--156
• Opis fizyczny: Bibliogr. 14 poz., fig., tab.

Twórcy

autor

Jakubczyk E.

• Institute of Physics, Jan Długosz University, Al. Armii Krajowej 13/15, 42-200 Częstochowa, Poland

autor

Jakubczyk M.

• Institute of Chemistry and Environmental Protection, Jan Długosz University, Al. Armii Krajowej 13/15, 42 - 200 Częstochowa, Poland

autor

Kapuśniak J.

• Institute of Chemistry and Environmental Protection, Jan Długosz University, Al. Armii Krajowej 13/15, 42 - 200 Częstochowa, Poland

Bibliografia

• 1. A. van den BEUKEL and S. RADELAAR, Acta metall., 31 (1983) 419.
• 2. A. van den BEUKEL, Key Eng. Mater., 81-83 (1993) 3.
• 3. T. KOMATSU, Res. Mech., 31 (1990) 263.
• 4. A. INOUE, H.S. CHEN, J.T. KRAUSE, T. MASUMOTO, M. HAGIWARA, J. Mater Sci., 18 (1983) 2743.
• 5. YU. B. KUZMA, N. F. CHABAN, Dwojnyje i trojnyje sistiemy sodierżaszczije bor, Moskwa, Metallurgija, 1990.
• 6. P. VILLARS, Pearson's Handbook Desk Edition, Crystallographic Data for Intermetallic Phases, ASM International, Materials Park, OH 44073, 1997.
• 7. B. ARONSSON, G. LUNDGREN, Acta Chem. Scand., 13 (1959) 433.
• 8. E. JAKUBCZYK, Z. MANDECKI, M. JAKUBCZYK, J. Non-Cryst. Solids, 232-234 (1998) 453.
• 9. C. M. HURD, The Hall Effect in Metals and Alloys, Plenum Press, New York - London, 1972, p. 153.
• 10. K. HEINEMANN, K. BARNER, J. Magn. Magn. Mater., 42 (1984) 291.
• 11. R. MALMHÄL, S. M. BHAGAT, K.V. RAO and G. BÄCKSTRÖM, Phys. Stat. Sol. (a), 53 (1979) 641.
• 12. E. JAKUBCZYK and Z. MANDECKI, Phase Transit., 51 (1996) 31.
• 13. R. MALMHÄL, G. BÄCKSTRÖM, K. V. RAO, S. M. BHAGAT, M. MEICHLE,
• 14. M. B. SALAMAN, J. Appl. Phys., 49 (1978) 1727.
• 15. T. KOMATSU, K. MATUSITA, R. YOKALA, J. Mater. Sci., 20 (1985) 3271.

Uwagi

Bibliografia: poz. 13 razem z poz. 14 bibliografii, tworzą jeden opis bibliograficzny.