Influence of UV irradiation and temperature on polyamides PA6, PA6,6 and polypropylene PP

• Autorzy: Brzozowska-Stanuch A. , Rabiej S. , Sarna E. , Maślanka A.
• Języki publikacji: EN

Abstrakty

EN

In outdoor applications, all polymer materials weather which causes deterioration of their mechanical properties and has a negative influence on their appearance. In this article, the influence of UV irradiation and high temperature on polyamides PA6, PA6.6 and polypropylene PP and influence of aging parameters on their appearance (the state of surface) and chemical crystal structure have been shown. Microscopic examination of samples has shown that the biggest destruction in the surface of PP occurred in a short time after the beginning of the exposure. The examination of the surface and crystal structure of the materials clearly indicated that during exposure to UV irradiation and temperature degradation in PP materials occurred. Polyamides showed longer reaction time but after some time they also underwent radical changes in their supermolecular structure and they lost their esthetic appearance.

Słowa kluczowe

EN

degradation; weathering; crystal structures; polyamides; polypropylene

PL

degradacja; wietrzenie; struktury krystaliczne; poliamidy; polipropylen

• Wydawca: Centrum Materiałów Polimerowych i Węglowych PAN
• Czasopismo: Polish Journal of Applied Chemistry
• Rocznik: 2011
• Tom: Vol. 55, nr 3-4
• Strony: 115--122
• Opis fizyczny: Bibliogr. 16 poz., rys., tab.

Twórcy

autor

Brzozowska-Stanuch A.

autor

Rabiej S.

autor

Sarna E.

autor

Maślanka A.

• BOSMAL Automotive Research and Development Institute Ltd., Sami Stok 93, 43-300 Bielsko-Biała, Poland,

Bibliografia

• [1] Shah V., „Handbook of Plastics Testing Technology", chapter 5, John Wiley & Sons, inc., Canada 1998.
• [2] Wypych G., „ Weathering of Plastics. Testing to Mirror Real Life Performance ”, Basic Parameters in Weathering Studies, 1-3, William Andrew and SPE, Norwich 1999.
• [3] Wypych G., „Handbook of material weathering "3-rd Ed. chapter 3, and chapter 6, ChcmTec Publishing, Toronto-New York 2003.
• [4] Rongfu L„ Xingzhou H., J. Polym. Degrad. Stab., 1998, <52, 523.
• [5] Majewski J., Tworzywa Sztuczne i Chemia, 2005, 2(21), 38.
• [6] Nie H.Y., Walzak M.J., Berno B., Appl. Surf. Sci., 1999,144/145, 627.
• [7] Girois S, Delprat P, Audouin L. Verdu J., J. Polym. Degrad. Stab.. 1997, 56, 169.
• [8] Allen N.S., Edge M, Corrales T, Catalina F., J. Polym. Degrad. Stab., 1998. 61, 139.
• [9] Yakimets I., Lai D., Guigon M., J. Polym. Degrad. Stab., 2004, 86, 59.
• [10] Castejón M.L., Tiemblo P., Gomez-Elvira J.M, J. Polym. Degrad. Stab., 2000, 70, 357.
• [11] Rymarz G., Tworzywa Sztuczne i Chemia. 2008, 5(42), 35.
• [12] Rabiej M., Rabiej S., „Analiza rentgenowskich krzywych dyfrakcyjnych polimerów za pomocą programu komputerowego WAXSFIT", Wydawnictwo ATH, 2006. Bielsko-Biała.
• [13] Urbańczyk G.W., „Fizyka włókna", chapter 2, Wydawnictwo Politechniki Łódzkiej, 2002. Łódź.
• [14] Murthy N.S., J. Appl. Polym. Sci., Part B: Polym. Phys., 2006, 44, 1763.
• [15] Broją J., „Struktura barwionych włókien polipropylenowych ", chapter 1, Wydawnictwo Akademii Techniczno-Humanistycznej w Bielsku-Białej, 2003, Bielsko-Biała
• [16] Shen L„ Phang Y.I., Liu T., Polymer Testing, 2006. 25, 249.