Hydrolytic degradation of poly(ester-ether-ester) terpolymers containing hydrophilic peg and hydrophobic dimer fatty acid

• Autorzy: Zdebiak P. , EL Fray M.
• Języki publikacji: EN

Abstrakty

EN

The aim of the work was preparation and investigation of new multiblock terpoly(cster-cthcr cster)s (TEEE) containing phthalic acid units as in poly(butylenc tercphthalate) (PBT) (hard segments) and hydrogenated dimer fatty acid, namely dilinoleic acid sequences (DLA) as hydrophobic ester soft segments, and poly(cthylenc glycol) (PEG) as hydrophilic ether soft segments. PEG of different molar mass (1000 and 4600 g/mol) was used. Synthesis was performed in a presence of a-tocopherol as non-toxic thermal stabilizer since these materials are targeted for biomedical applications. In this work, the hydrolytic degradation process of TEEE and its influence on mechanical properties is discussed.

Słowa kluczowe

EN

hydrolityc degradation; polyesters; mechanical properties

PL

hydrolityczna degradacja; poliestry; właściwości mechaniczne

• Wydawca: Centrum Materiałów Polimerowych i Węglowych PAN
• Czasopismo: Polish Journal of Applied Chemistry
• Rocznik: 2009
• Tom: Vol. 53, nr 2
• Strony: 203--207
• Opis fizyczny: Bibliogr. 8 poz., rys., tab.

Twórcy

autor

Zdebiak P.

autor

EL Fray M.

• Szczecin University of Technology, Polymer Institute, Division of Biomaterials and Microbiological Technologies, Pułaskiego 10, 70-322 Szczecin, Poland

Bibliografia

• [1] Buckwalter, J.A., Lohmander, S., J. Bone Joint Surg,. 1994, 74 A9, 1405.
• [2] Młynarski, K.. Ortopedia Traumatologia Rehabilitacja, 2000, 3.
• [3] Zheng-Qin, G., Jin-Me, i X., Xiang-Hong, Z. Biomed. Mater. Eng. 1998, 8, 75.
• [4] El Fray, M., Wpływ budowy segmentów giętkich na wybrane właściwości segmentowych kopolimerów blokowych, Praca Doktorska, Szczecin, 1996.
• [5] Kim, M., Kim, K, Jin, H., Park, J., Yoon, J., Eur. Polym. J., 2001, 37, 843.
• [6] Jin, H., Lee, B., Kim, M., Yoon, J., J. Appl. Polym. Sci., 2000, 38, 1504.
• [7] Zdebiak, P., El Fray, M., Przemyśl Chemiczny, 2006, 85 (8-9), 986.
• [8] Zdebiak P., El Fray M., Polimery, 2008, 53 (10), 764.