Hydrogen embrittlement and delayed failure

• Autorzy: Szklarska-Śmiałowska Z.

Warianty tytułu

PL

Kruchość wodorowa i opóźnione pękanie

• Konferencja: Advances in Corrosion Science and Application ( 09-13.09.2003 ; Zakopane, Poland)
• Języki publikacji: EN

Abstrakty

EN

Examples of hydrogen embrittlement (HE) at high and low temperatures are given. The hydrogen induced cracking of Alloy 600 in a condition simulating that existing in a pressurized water reactor environment (350oC) and delayed fracture of an alloy at ambient temperatures are reported. The HE of bolts used in the automotive industry at ambient temperatures is discussed. In particular, a note has been taken to correlate the content of hydrogen in metals with their propensity to failure.

PL

Podano przykłady kruchości wodorowej w wysokich i niskich temperaturach. Opisano pękanie wodorowe stopu Alloy 600 w warunkach symulu- jących środowisko ciśnieniowego wodnego reaktora jądrowego (350oC), a także opóźnione pękanie tego stopu w temperaturze otoczenia. Omówiono kruchość wodorową stalowych śrub używanych w przemyśle motoryzacyjnym. Zwrócono uwagę na zależność między zawartością wodoru w metalach a ich skłonnością do pękania.

Słowa kluczowe

EN

hydrogen cracking; nuclear reactor

PL

kruchość wodorowa; wodny reaktor jądrowy; pękanie wodorowe

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Ochrona przed Korozją
• Rocznik: 2005
• Tom: nr 9
• Strony: 290--294
• Opis fizyczny: Bibliogr. 14 poz., il.

Twórcy

autor

Szklarska-Śmiałowska Z.

• Fontana Corrosion Center, The Ohio State University, Columbus, Ohio, USA

Bibliografia

• 1. Ford F.P., Andersen P.L.: in Proc. 3th Int. Symp.on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Traverse City, Michigan.,The Metallurgical Soc. Warendale, Pa (1988) p.789.
• 2. Scott P.M. and Le Calvar M.: in Proc. 6th Int. Symp.on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, San Diego, Cal., The Minerals, Metals and Materials Society, Warrendale, PA (1993) p. 657.
• 3. Galvele J.R.: Corr. Sci.V.27, l (1987).
• 4. Shen C.H., Shewman P.G.: Metall.Trans. 21A, (1991)1261.
• 5. Rios R., Magnin T., Noel D., Bouvier O.: Metali. Mat. Trans. Y.26A (1995) 925p.
• 6. Oriani R.A., in "Hydrogen Embrittlement and Stress Corrosion Cracking" Ed. R.Gibala, R.F.Hehemann, ASM, 1984, p.43.
• 7. Totsuka N., Lunarska E., Cragnolino G., Szklarska-Smialowska Z.: Corrosion, V.43, 505 (1987).
• 8. Totsuka N., Szklarska-Smialowska Z.: Corrosion, V.43, 734 (1987).
• 9. Troiano A.R.: Trans.ASM, V.52, 54 (1960).
• 10. Xia Z., Lai W.-K., Szklarska-Smialowska Z.: Corrosion, V.47, 173 (1991).
• 11. Pond B.G.: Acta Metali.V.38, 2373 (1990); B.G.Pound. R.M.Sharp, G.A. Wright, Acta Metali. V.35, 263 (1987).
• 12. Lukito H., Szklarska-Smialowska Z.: Corr. Sci. V.39, 2151 (1997).
• 13. Rebak R.B., Muchlin L., Szklarska-Smialowska Z.: Corrosion, V.53, 481 (1997)
• 14. Hong G.W., Lee J.Y.: Mat.Sci.Eng. V.61, 219 (1983).