Role of Li+ on the pitting corrosion of copper in LiBr solutions

Meleigy, A. E.; Shehata, M. F.; Youssef, G. I.; Elhamid, S. E.; Warraky, A. A. F.

Artykuł - szczegóły

Tytuł artykułu

Role of Li+ on the pitting corrosion of copper in LiBr solutions

Autorzy

Meleigy A. E. , Shehata M. F. , Youssef G. I. , Elhamid S. E. , Warraky A. A. F.

Wybrane pełne teksty z tego czasopisma

http://www.ochronaprzedkorozja.pl/

Identyfikatory

Warianty tytułu

Wpływ jonów Li+ na korozję wżerową miedzi w roztworach LiBr

Języki publikacji

Abstrakty

The pitting corrosion of copper in both LiBr and NaBr solutions has beens studeid using potentiodynamic measurements and surface analysis techniques. It was found that pitting of Cu was evident only after the formation of a protective film of CuO and/or Cu(OH)2, depending on the bromide content. In case of NaBr the hysteresis loop of pitting corrosion started to appear at 3.1-10-2M while in case of LiBr it started at 7.4-10-2M bromide content. These results, togheter with the current - time trend and the surface analysis, confirm the role of Li+ on the passivation and pitting attack on copper metal.

Przeprowadzono badania korozji wżerowej miedzi w roztworach LiBr i NaBr metodami polaryzacji potencjodynamicznej i analizy powierzchni. Stwierdzono, że wżery pojawiają się po utworzeniu się ochronnej warstwy CuO i/lub Cu(OH)2 w zależności od zawartości bromku. W przypadku NaBr pętla histerezy korozji wżerowej zaczyna się pojawiać przy zawartości bromku 3,1ź10-2 M, a w przypadku LiBr – przy 7,4ź10-2 M. Te wyniki, jak również przebieg krzywej prądu w czasie i analiza powierzchni, potwierdzają wpływ jonów Li+ na pasywację i korozję wżerową miedzi.

Słowa kluczowe

copper lithium bromide sodium bromide passivation pitting corrosion

miedź bromek litu pasywacja korozja wżerowa

Wydawca

Wydawnictwo SIGMA-NOT

Czasopismo

Ochrona przed Korozją

Rocznik

2012

Tom

nr 10

Strony

427--431

Opis fizyczny

Bibliogr. 43 poz., rys.

Twórcy

autor

Meleigy A. E.

autor

Shehata M. F.

autor

Youssef G. I.

autor

Elhamid S. E.

autor

Warraky A. A. F.

Department of Electrochemistry and Corrosion, National Research Center, Cairo, Egypt

Bibliografia

1. E.S. Bustos et al., Corros. Sci„ 51, 5 (2009) 1107.
2. M.A. Igual-MiTnoz et. al., Corros. Sei., 46, 12(2004)2955.
3. V, Oleinik, [.K. Yu, A.R. Yartapetyan, Pro-tect. Metals, 39, l (2003)12.
4. D M. Garcia-Garcia et al., Conos. ScL, 48, 2 (2006) 2380.
5. T.M.H. Saber, A.A. El Warraky, Br. Corros. J.,26,4(1991)279.
6. T.M.H. Saber, A.A. El Warraky, Desalination,93(1993)473.
7. T.M.H. Saber, A.A. El Warraky, 16 Annual Conf. Corros i on Problems in Industry, Hurghada, Egypt(1997)V(ll), 29.
8. T.M.H. Saber, A.A.El Warraky, 17th AnnualConf. Corrosion Problems in Industry, Zafarana, Egypt(1998)V(l), 19.
9. A.A. El Warraky, Br. Corros. J., 32, l (1997) 57.
10. A.E. El Meleigy, A.A. El Warraky, Corros. Eng.Sci. Tech., 38,3(2003)218.
11. A.A. El Warraky, A.E.El Meleigy, Br. Corros. J., 37(4), 305(2002).
12. A.A. El Warraky, A.M. El-Aziz, Kh.A. Soliman, Anti-Corros. Methods Mater., P. l, 54, 3, (2007) 163.
13. A.A. El Warraky, A.M. El-Aziz, Kh.A. Soliman, Anti-Corros. Methods Mater, P.2, 54,3, (2007) 163.
14. A.A. El Warraky. A.E. El Meleigy, Steel Grips, 5, 4 (2007) 297.
15. A.E. El Meleigy et al., Egypt. J.Chem., 93 (2009).
16. M.A. Igual-Munoz et al., Corrosion, 58,(2002) 560.
17. M.A. Igual-Munoz et al., Corrosion, 59, (2003)32.
18. M.J. Munoz-Portero et al., Corrosion, 61,(2005) 464.
19. M.A. Igual-Munoz et al., Corrosion, 58, (2002) 995.
20. D. Itzhak, T. Greenberg. Corrosion, 55, 795(1999).
21. V. Perc ?.-Hęetran z et al., Corrosion, 57, 835 (2001).
22. R. Leiva-Garcia, M.J. Munoz-Portero. J. Garcia-Amon, Corros. Sci., 52, 950 (2010).
23. M.T. Montanes et al.. Corros. Sci., 51, (2009) 2733.
24. M.J. Munoz-Portero et al., Coirosion, 62 (2006)1018.
25. R. Sanchez-Tovar, M.T Montanes. J. Garcia- Anton, Corros. Sci., 52 (2010) 722.
26. A. Valero-Gomez. A. Igual-Munoz, J. Garcia- Amon, Corrosion, 62 (2006) 1117.
27. A. Valero-Go mez. J. Garcia-Anto n. A. Igual- Munoz, Corrosion, 62 (2006) 751.
28. M.T. Montańes et al., Corrosion, 62 (2006) 64.
29. M.A. lgual-Mu'noz et al., Corrosion, 57 (2001)516.
30. A.A. El Warraky et al., Anli-Corros. Methods Mater., 51, l (2004)52.
31 H.M. Shalaby, F.M. Al Kharafi, A.J. Said, Brit. Conos. J., 25(1990)292.
32. J.N. Al Hajji, M.R. Reda, Brit. Corros. J., 31 (1996)125.
33. R. Alkire, A. Cangellan, J. Eleclrochem. Soc., 136(1989)913.
34. C. Deslouis et al.. J. Appl. Elecirochem., 18 (1988)374.
35. A.M. Shams El Din, F.M. Abd El Wahab, Electrochem.Acta,9(1964) 113.
36. A.A. El Warraky, H.A. El Shayeb, E.M. Sherif, Egypt. J. Chem., 47,6 (2004) 609.
37. B. Omay, J. Electrochem. Soc., 136 (1989) 1578.
38. D.W. Shoesmith, T.E. Rummery, D. Owen, and W. Lee, J. Electrochem. Soc., 123,790(1976).
39. W, Jeffrey et al., J. Electiochem. Soc., 146, 2(1999)448,
40. K. Sailo et al., Solid State Communications, 125(2003)23.
41. L. Rao et al., Solid State Scie., 11, 11(2009) 578.
42. G. A El-Shobaky, Th. E!-Nabarawy, G.A. Fagal, Thermochim. Acta., 150(1989) 111.
43. J.C.S. Fernandes, M.G.S. Ferreira, Electrochim. Acta. 37. 14 (1992) 2659.

Typ dokumentu

Bibliografia

Identyfikator YADDA

bwmeta1.element.baztech-article-BPB2-0072-0019