Badania hybrydowych kompozytów warstwowych typu FML (Fibre Metal Laminate)

• Autorzy: Godzimirski J. , Pietras A.

Warianty tytułu

EN

Research of laminar hybrid composite sort FML (Fibre Metal Laminate)

• Języki publikacji: PL

Abstrakty

EN

Laminar hybrid composites sort FML are laminates made of adhesively bonded thin metal sheets and layers of polymer composite reinforced by fibers. These materials show an intermediate property between metals and polymer composite reinforced by fibers. Limited application of these new materials is motivated by narrow expertise of their strength. The purpose of the research was to estimate the failure that might influence the FML material loading method. The numerical calculations were provided in this experiment with the elastic-plastic properties of metal component and orthotropic of composite components. It was pointed out that laminar hybrid composite may be damaged due to not only the strength exceed of components, but also as results of delamination because of the adhesive bonds failure.

Słowa kluczowe

PL

kompozyt warstwowy; laminaty metalowo-włókniste; FML; spojenie adhezyjne; delaminacja

EN

laminar composite; fibre metal laminate; FML; adhesive bonding; delamination

• Wydawca: Oficyna Wydawnicza Politechniki Rzeszowskiej ; Sieć Badawcza Łukasiewicz - Warszawski Instytut Technologiczny
• Czasopismo: Technologia i Automatyzacja Montażu
• Rocznik: 2012
• Tom: nr 2
• Strony: 52--56
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Godzimirski J.

autor

Pietras A.

• Wojskowa Akademia Techniczna, Warszawa

Bibliografia

• 1. Surowska В.: Materiały funkcjonalne i złożone w transporcie lotniczym. Maintenance and Reliability nr 3, 2008 Polska.
• 2. Vlot Α.: Glare history of the development a new aircraft material. Kluwer Academic Publishers, 2004 New York.
• 3. Reyes Villanueva G., Cantwell W.J.: The high velocity impact response of composite and FML-reinforced sandwich structures. Composites Science and Technology 64, The University of Liverpool, Wielka Brytania 2004, pp. 35-54.
• 4. Po-Yu Chang, Po-Ching Yeh, Jenn-Ming Yang: Fatigue crack initiation in hybrid boron/glass/aluminum fiber metal laminates. Materials Science and Engineering A 496, University of California, USA 2008, pp. 273-280.
• 5. Vlot Α.: Fibre Metal Laminats; an introduction. Kluwer Academic Publishers, 2001 Dordrecht.
• 6. Khan S.U., Alderliesten R.C., Benedictus R.: Delamination in Fiber Metal Laminates (GLARE) during fatigue crack growth under variable amplitude loading. International Journal of Fatigue, Delft University of Technology, Holandia 2011.
• 7. Kuczmaszewski J.: Fundamentals of Metal-Metal Adhesive Joint Design. Oddział PAN, Lublin 2006.
• 8. Godzimirski J., Komorek Α., Rośkowicz Μ., Smal T., Tkaczuk S.: Tworzywa adhezyjne - zastosowanie w naprawach sprzętu technicznego. WN-T, Warszawa 2010.
• 9. Godzimirski J., Pietras Α.: Identyfikacja stałych materiałowych hybrydowych kompozytów typu Fibre Metal Laminat z wykorzystaniem metody homogenizacji. Problemy Mechatroniki, Wojskowa Akademia Techniczna, Warszawa, (przyjęty do druku).
• 10. Ochelski S.: Metody doświadczalne mechaniki kompozytów. WN-T, Warszawa 2004.