Influence of tungsten content on magnetization processes in nanocomposite Nd2Fe14B/alpha-Fe magnets.

• Autorzy: Przybył A. , Wysłocki J. J. , Kaszuwara W. , Leonowicz M.
• Języki publikacji: EN

Abstrakty

EN

The nanocomposite Nd2Fe14B/alpha-Fe magnets with different tungsten content (from 0 to 33 at. %) produced by mechanical alloying were examined. It was found that the magnetization process changes with increase of tungsten content in the material. In the alloy without tungsten coercivity mechanism is connected with the nucleation and growth of domains with opposite magnetization. With increase tungsten content in the alloy, pinning of the domain walls plays a more important role in the magnetization processes. Moreover, the changes in magnetic properties, such as coercive force jHc, remanence Br and energy product (BH)max depending on tungsten content in Nd2Fe14B/alpha-Fe magnets are reported.

Słowa kluczowe

EN

tungsten; magnetization; nanocomposites; magnetic properties; nucleation; coercitivity

PL

wolfram; magnesowanie; nanokompozyty; właściwości magnetyczne; powstawanie zarodków krystalizacji; koercyjność

• Wydawca: Komitet Nauki o Materiałach PAN
• Czasopismo: Archives of Materials Science
• Rocznik: 2005
• Tom: Vol. 26, nr 3
• Strony: 221--229
• Opis fizyczny: Bibliogr. 12 poz., rys.

Twórcy

autor

Przybył A.

• Częstochowa University of Technology, Institute of Physics, Faculty of Materials Processing Technology and Applied Physics, al. Armii Krajowej 19, 42-200 Częstochowa

autor

Wysłocki J. J.

• Częstochowa University of Technology, Institute of Physics, Faculty of Materials Processing Technology and Applied Physics, al. Armii Krajowej 19, 42-200 Częstochowa

autor

Kaszuwara W.

• Faculty of Materials Science and Engineering, Warsaw University of Technology, ul. Wołoska 141, 02-507 Warszawa, Poland

autor

Leonowicz M.

• Faculty of Materials Science and Engineering, Warsaw University of Technology, ul. Wołoska 141, 02-507 Warszawa, Poland

Bibliografia

• [1] K.H.J. Buschow, D.B. De Mooij, R. Coehoorn,J. Less-Common Met., 145,601 (1988).
• [2] M. Leonowiсz, Arch, nauki o mater., 3, 171 (1997).
• [3] J. Bernardi, J. Fidler, F. Födelmayг, IEEE Trans. Magn. 28, 2127 (1992).
• [4] A. Yan, X. Sоng, M. Song, X. Wang, J. Alloys and Comp., 257, 273 (1997).
• [5] A. Przуbуł, Wpíyw dodatku wolframu na mikrostrukturę, właściwości magnetyczne i procesy przemagnesowania nanokompozytowych magnesów Nd-Fe-B, Politechnika Częstochowska, Częstochowa 2002, (doctoral thesis).
• [6] M. Seeger, H. Kronmüller, Z. Metallkunde, 87, 923 (1996).
• [7] M. Leonowiсz, Nowoczesne materiały magnetyczuie twarde. Wybrane zagadnienia, Oficyna Wydawnicza Politechniki Warszawskiej, Warszawa 1996.
• [8] Х.С. Кou, F.R. de Вoer, R. Grössinger, G. Wiesinger, H. Suzuki, H. Кitazawа, Т. Tаkamasu, G. Кido, J. Magn. Magn. Mat., 177-181, 1002 (1998).
• [9] Р. Paw1ik, J.J. Wysłocki, M. Baran, Acta Phys. Polon. A 100, 905 (2001).
• [10] K. Kobayashi, D. Givord, J.M.D. Соeу, J. Magn. Magn. Mat., 157-158, 97 (1996).
• [11] R.M. Вozогth, Ferromagnetism, IEEE Press (Classic Reissue), New York 1993.
• [12] M. Leonowicz, J.J.Wysłocki, Współczesne magnesy. Technologie, mechanizmy koercji, zastosowania. Wyd. Naukowo-Techniczne, Warszawa 2005.