Atmospheric corrosion of structural materials in Poland.

• Autorzy: Kobus J.
• Konferencja: XVIth Physical Metallurgy and Materials Science Conference on Advanced Materials and Technologies AMT'2001, Gdańsk-Jurata, 16-20 September, 2001
• Języki publikacji: EN

Abstrakty

EN

The paper presents investigations of the effects of aggressive atmospheric corrosion agents on the progress of corrosion of metal structure materials: carbon steel, zinc, copper and aluminium. The tests were performed at the corrosion stations according standards: ISO 9223:1992, ISO 9224:1992, ISO 9225:1992, ISO 9226:1992, ISO 8565:1992 [1-5]. In the result of 8 years of experience were determined main atmospheric factors influencing corrosion rates of the several standard metals. It was shown that except factors discussed in the standard ISO 9223:1992 [1] (sulphur dioxide, time of wetness and chloride ion deposition) ozone plays a main part in corrosion rates. Ozone accelerates particularly the corrosion of copper, however steel and aluminium too.

PL

Artykuł prezentuje badania wpływu agresywnych atmosferycznych czynników korozyjnych na szybkość korozji metalowych materiałów konstrukcyjnych: stali węglowej, cynku, miedzi i aluminium. Badania prowadzone są na stacjach korozyjnych zgodnie z normami ISO. W wyniku 8-letnich ekspozycji określono główne czynniki atmosferyczne wpływające na szybkość korozji poszczególnych metali. Okazało się, że oprócz dwutlenku siarki, czasu zwilżania i stężenia chlorków w opadach dużą rolę w wielkości ubytków korozyjnych odgrywa ozon. Wpływa on zwłaszcza na przyspieszenie korozji miedzi, ale także stali i aluminium.

Słowa kluczowe

EN

atmospheric corrosion; metal structure materials; carbon steel; zinc; copper; aluminium; aggresive atmospheric corrosion agents; corrosion

PL

korozja atmosferyczna; metalowe materiały konstrukcyjne; stal węglowa; cynk; miedź; aluminium; agresywny atmosferyczny czynnik korozyjny; korozja

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2001
• Tom: R. XXII, nr 4
• Strony: 450--453
• Opis fizyczny: Bibliogr. 11 poz., tab., rys.

Twórcy

autor

Kobus J.

• Institute of Precision Mechanics, Warsaw, Poland

• Institute of Precision Mechanics, Warsaw

Bibliografia

• [1] ISO 9223: 1992: Corrosion of metals and alloys-Corrosivity of atmosphercs-Classification
• [2] ISO 9224: 1992: . Corrosion of metals and alloys - Corrosivity of atmospheres - Guiding values for the corrosivity categories
• [3] ISO 9225: 1992: Corrosion of metals and alloys-Corrosivity of atmospheres - Measurement of pollution
• [4] ISO 9226: 1992: Corrosion of metals and alloys . Corrosivity of atmospheres - Determination of corrosion rates of standard specimens for the evaluation of corrosivity
• [5] ISO 8565:1992: Metal and alloys - Atmosphering corrosion testing - General requirements for field tests.
• [6] ISO 8407:1992 Corrosion of metals and alloys. Removal of corrosion products from corrosion test specimens
• [7] Oesch S.; Environmental effects on materials. Effect of SO2 on the corrosion of unalloyed steel and weathering steel-an attempt to simulate atmospheric corrosion. Materials and Corrosion 47 (1996) 505-510
• [8] Tidbald J., Kucera V.: The role of NO2 and O3 in the corrosion and degradation of materials, Swedish Corrosion Institute, KI Report No 1996:6E
• [9] Svennsson J.E. , Johansson L.-G.: A laboratory study of the initial stage of the atmospheric corrosion of zinc in the presence of NaCl, influence of SO2 and NO2, Corrosion Science 34 (1993) 721-740
• [10] Feliu S., Morcillo M., Feliu S. Jr. The prediction of atmospheric corrosion from meteorological and pollution parameters-1. Annual corrosion . Corrosion Science 3, (1993) 403-414
• [11] Feliu S., Morcillo M., Feliu S. Jr. The prediction of atmospheric corrosion from meteoroiogical and pollution parameters-II. Long term forecasts. Corrosion Science 3, (1993) 415-422