Characteristics of sulphide scale and internal sulphur-rich precipitates in carbon steel by SEM and TEM.

• Autorzy: Hucińska J.
• Konferencja: XVIth Physical Metallurgy and Materials Science Conference on Advanced Materials and Technologies AMT'2001, Gdańsk-Jurata, 16-20 September, 2001
• Języki publikacji: EN

Abstrakty

EN

Characteristics of sulphide scale and internal sulphur-rich precipitates in K18 carbon steel after 11 years of service in a refinery furnace environment have been examined in order to beter understand the mechanism of damage to the steel under the influence of sulphur at elevated temperatures. Scanning and transmission electron microscope techniques have been involved in the study. Diffusion paths of the sulphur in the steel have been indicated and two kinds of sulphur-rich precipitates have been presented: degraded cementite particles, additionally enriched in manganese, chromium and silicon, and iron sulphide inclusions that formed after the former particles had completely disappeared.

PL

Badano charakterystyczne cechy zgorzeliny siarczkowej i wewnętrznych wydzieleń zawierających siarkę w stali węglowej K18 po 11 latach pracy w piecu rafineryjnym w celu lepszego poznania mechanizmu niszczenia stali pod wpływem siarki w podwyższonych temperaturach. W badaniach wykorzystano technikę elektronowej mikroskopii - skaningowej i transmisyjnej. Wskazano drogi dyfuzji siarki w stali oraz przedstawiono dwa rodzaje wydzieleń zawierających siarkę: zdegradowane cząstki cementytu, dodatkowo wzbogacone w mangan, chrom i krzem oraz wtrącenia siarczków żelaza utworzone po całkowitym zaniku cząstek wymienionych w pierwszej kolejności.

Słowa kluczowe

EN

sulphide scale; internal precipitates; sulphur-rich precipitates; carbon steel; damage; scanning electron microscopy; transmission electron microscopy

PL

zgorzelina siarczkowa; wydzielenia wewnętrzne; wydzielenia zawierające siarkę; stal węglowa; uszkodzenie; elektronowa mikroskopia skaningowa; elektronowa mikroskopia transmisyjna

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2001
• Tom: R. XXII, nr 4
• Strony: 384--387
• Opis fizyczny: Bibliogr. 6 poz., tab., rys

Twórcy

autor

Hucińska J.

• Technical University of Gdańsk, Poland

• Technical University of Gdańsk, Poland

Bibliografia

• [1] Gutzeit J., in: Process industry corrosion - the theory and practice, NACE, Houston, 1986.
• [2] Couper A.S., Gorman J.W.: Computer correlations to estimate high temperature H2S corrosion in refinery strearns. Materials Protection and Performance 10 (1971), pp. 31-37.
• [3] Lai G.Y.: High-temperature corrosion of engineering alloys. ASM Int., Materials Park, OH, 1997.
• [4] McCoy J.D.: Corrosion rates for H2S at elevated temperatures in refinery hydrodesulfurization processes. Materials Performance 13 (1974), pp. 19 -25.
• [5] McCoy J.D., Hamel F.B.: Effect of hydrodesulfurizing process variables on corrosion rates. Materials Protection and Performance 10 (1971), pp. 17-22.
• [6] Couper A. S.: High temperature mercaptan corrosion of steel. Corrosion 19 (1963), pp. 396t-40lt