The influence of a microstructure on magnetic properties and electric resistivity of Cu-Co GMR stripes

• Autorzy: Dubiel B. , Figiel H. , Ciura F. , Czyrska-Filemonowicz A.
• Konferencja: XVIth Physical Metallurgy and Materials Science Conference on Advanced Materials and Technologies AMT'2001, Gdańsk-Jurata, 16-20 September 2001
• Języki publikacji: EN

Abstrakty

EN

The Cu-10 wt %Co melt spun ribbons with giant magneto-resistance (GMR) properties were aged at 773 K for 0.5, 1, 2, 4, 16 and 32 hours. Quantitative transmission electron microscopy (TEM) microstructural analysis have been carried out to determine size distributions of beta -Co precipitates. The results of magnetisation, coercitivity and electrical magneto-resistivity measurements were correlated with the mean diameters of coherent beta-Co particles. It was shown, that the maximum GMR is achieved for the mean diameters of beta-Co particles less than 10 nm, whereas for larger particles the GMR effect is strongly reduced.

PL

Otrzymane metodą krystalizacji z ciekłej strugi taśmy stopu Cu-10% wag.Co, wykazującego gigantyczny magnetoopór, wyżarzono w temperaturze 773 K przez 0,5, 1, 2, 4, 16 i 32 godziny. W celu określenia rozkładów wielkości wydzieleń beta--Co po różnych wariantach wyżarzania przeprowadzono ilościową analizę mikrostruktury metodami transmisyjnej mikroskopii elektronowej. Wyniki pomiarów namagnesowania, koercji i magnetooporu skorelowano z wartościami średniej średnicy koherentnych wydzieleń beta-Co. Wykazano, że stop wykazuje maksymalny magnetoopór, gdy średnia średnica wydzieleń jest mniejsza niż 10 nm. Wzrost średniej wydzieleń powyżej 10 nm sprawia, że efekt magnetooporu wyraźnie maleje.

Słowa kluczowe

EN

stripes; GMR effect; magnetic properties; electric resistivity; magnetization; coercitivity; electrical magneto-resistivity; measurement

PL

taśma stopu; efekt magnetronu; właściwości magnetyczne; opór właściwy; namagnesowanie; koercja; magnetoopór; pomiar

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2001
• Tom: R. XXII, nr 4
• Strony: 286--289
• Opis fizyczny: Bibliogr. 10 poz., rys.

Twórcy

autor

Dubiel B.

• University of Mining and Metallurgy, Kraków, Poland

autor

Figiel H.

• University of Mining and Metallurgy, Kraków, Poland

autor

Ciura F.

• University of Mining and Metallurgy, Kraków, Poland

autor

Czyrska-Filemonowicz A.

• University of Mining and Metallurgy, Kraków, Poland

• University of Mining and Metallurgy, Kraków

Bibliografia

• [1] Baibich M.N., Broto J.M., Fert A., Nguyen van Dau F., Petroff F., Etienne P. , Creuzet G. , Friedrich A. , Chazeles J. : Giant magnetoresistance of (00 I) Fe/(00 I )Cr magnetic superlattices. Phys. Rev. Lett. Vol.. 61, 1988, p. 2472.
• [2] Berkowitz E. , Mitchell J.R., Carey M.J., Young A. P. , Shang S.,Spada F.E, Parker F.T.. Hutten A., Thomas G.: Giant magnetorcsistance in heterogeneous Cu-Co alloys. Phys. Rev. Lett .. Vol. 68, 1992, p. 3745.
• [3] Xiao J.Q., Jiang J.S., Chien C.L.: Giant magnetoresistance in nonmultilayer magnetic systems. Phys. Rev. Lett., Vol. 68, 1992, p.3749.
• [4] Allia P., Knobel M., Tibeno P., Vinai F.: Magnetic propenies and giant magnetoresistance of melt-spun granular Cu10xCox alloys. Phys. Rcv. 8 ., Vol. 52 , 1995, p. I 5398.
• [5] Kuźmiński M., Ślawska-Waniewska A., Lachowicz H.K., Knobel M.: The effect of partcle size and surface-to-volume ratio distribution on giant magnetoresistance (GMR) in melt spun Cu-Co alloys. J. Magn . Mat. , Vol. 205, 1999, p.7.
• [6] Krop K., Mizia J., Korbel A.: Size distribution function of precipitate Co particles in Cu-1%Co solid solution. Acta Met, Vol. 15, 1967, p.463
• [7] Ciura F., Figiel H., Wosik J., Knobel M.: Microstructure of annealed Cu-Co alloy bands produced by meli-spinning method. Inżynieria Materiałowa, Vol. 3(104), 1998, p.564.
• [8] Ciura F, Dubiel B., Figiel H., Czyrska-Filemonowicz A.: Quanlitive TEM studies on thermal ageing effects in Cu-Co giant magnetoresistance materials. Proc. X Conf on Electron Microscopy of Solids, Warsaw-Serock, E. Jezierska, J.Kozubowski (eds), Fotobit 1999, Sept. 20-23 , 1999, p. 219.
• [9] Howson M.A., Musa S.O., Walker M.J., Hickey B.J., Cohrane R., Stevens R. : Giant magnetoresistance in melt-spun Cu87Co13. J.Appl. Phys., Vol.78, 1994, p.6546.
• [10] Zhang S., Levy P.M.: Conductivity and magnetoresistance in magnetic granular films. J.Appl. Phys. Vol.73, 1993, p.5315.