The Cu-10 wt %Co melt spun ribbons with giant magneto-resistance (GMR) properties were aged at 773 K for 0.5, 1, 2, 4, 16 and 32 hours. Quantitative transmission electron microscopy (TEM) microstructural analysis have been carried out to determine size distributions of beta -Co precipitates. The results of magnetisation, coercitivity and electrical magneto-resistivity measurements were correlated with the mean diameters of coherent beta-Co particles. It was shown, that the maximum GMR is achieved for the mean diameters of beta-Co particles less than 10 nm, whereas for larger particles the GMR effect is strongly reduced.
Otrzymane metodą krystalizacji z ciekłej strugi taśmy stopu Cu-10% wag.Co, wykazującego gigantyczny magnetoopór, wyżarzono w temperaturze 773 K przez 0,5, 1, 2, 4, 16 i 32 godziny. W celu określenia rozkładów wielkości wydzieleń beta--Co po różnych wariantach wyżarzania przeprowadzono ilościową analizę mikrostruktury metodami transmisyjnej mikroskopii elektronowej. Wyniki pomiarów namagnesowania, koercji i magnetooporu skorelowano z wartościami średniej średnicy koherentnych wydzieleń beta-Co. Wykazano, że stop wykazuje maksymalny magnetoopór, gdy średnia średnica wydzieleń jest mniejsza niż 10 nm. Wzrost średniej wydzieleń powyżej 10 nm sprawia, że efekt magnetooporu wyraźnie maleje.
Wydawca
Czasopismo
Rocznik
Tom
Strony
286--289
Opis fizyczny
Bibliogr. 10 poz., rys.
Twórcy
autor
- University of Mining and Metallurgy, Kraków, Poland
autor
- University of Mining and Metallurgy, Kraków, Poland
autor
- University of Mining and Metallurgy, Kraków, Poland
autor
- University of Mining and Metallurgy, Kraków, Poland
- University of Mining and Metallurgy, Kraków
Bibliografia
- [1] Baibich M.N., Broto J.M., Fert A., Nguyen van Dau F., Petroff F., Etienne P. , Creuzet G. , Friedrich A. , Chazeles J. : Giant magnetoresistance of (00 I) Fe/(00 I )Cr magnetic superlattices. Phys. Rev. Lett. Vol.. 61, 1988, p. 2472.
- [2] Berkowitz E. , Mitchell J.R., Carey M.J., Young A. P. , Shang S.,Spada F.E, Parker F.T.. Hutten A., Thomas G.: Giant magnetorcsistance in heterogeneous Cu-Co alloys. Phys. Rev. Lett .. Vol. 68, 1992, p. 3745.
- [3] Xiao J.Q., Jiang J.S., Chien C.L.: Giant magnetoresistance in nonmultilayer magnetic systems. Phys. Rev. Lett., Vol. 68, 1992, p.3749.
- [4] Allia P., Knobel M., Tibeno P., Vinai F.: Magnetic propenies and giant magnetoresistance of melt-spun granular Cu10xCox alloys. Phys. Rcv. 8 ., Vol. 52 , 1995, p. I 5398.
- [5] Kuźmiński M., Ślawska-Waniewska A., Lachowicz H.K., Knobel M.: The effect of partcle size and surface-to-volume ratio distribution on giant magnetoresistance (GMR) in melt spun Cu-Co alloys. J. Magn . Mat. , Vol. 205, 1999, p.7.
- [6] Krop K., Mizia J., Korbel A.: Size distribution function of precipitate Co particles in Cu-1%Co solid solution. Acta Met, Vol. 15, 1967, p.463
- [7] Ciura F., Figiel H., Wosik J., Knobel M.: Microstructure of annealed Cu-Co alloy bands produced by meli-spinning method. Inżynieria Materiałowa, Vol. 3(104), 1998, p.564.
- [8] Ciura F, Dubiel B., Figiel H., Czyrska-Filemonowicz A.: Quanlitive TEM studies on thermal ageing effects in Cu-Co giant magnetoresistance materials. Proc. X Conf on Electron Microscopy of Solids, Warsaw-Serock, E. Jezierska, J.Kozubowski (eds), Fotobit 1999, Sept. 20-23 , 1999, p. 219.
- [9] Howson M.A., Musa S.O., Walker M.J., Hickey B.J., Cohrane R., Stevens R. : Giant magnetoresistance in melt-spun Cu87Co13. J.Appl. Phys., Vol.78, 1994, p.6546.
- [10] Zhang S., Levy P.M.: Conductivity and magnetoresistance in magnetic granular films. J.Appl. Phys. Vol.73, 1993, p.5315.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BOS5-0002-0001