Correlation between magneto-acoustic effect, mechanical properties and microstructure of 2Cr - 1Mo steel in service.

• Autorzy: Augustyniak B. , Piotrowski L. , Chmielewski M. , Głowacka M. , Ćwiek J. , Łabanowski J.
• Konferencja: XVIth Physical Metallurgy and Materials Science Conference on Advanced Materials & Technologies AMT'2001, Gdańsk-Jurata, 16-20 September 2001
• Języki publikacji: EN

Abstrakty

EN

Results of magneto-acoustic emission (MAE) measurements for 10H2M steel after service at power plant and at as-received stage are presented. Creep damage stage was evaluated from microstructure and mechanical properties (hardness HV, yield strength R0,2 and ultimate tensile strength Rm). It was revealed that MAE intensity decreases monotonically with creep damage stage degree and that relative change of MAE intensity is much higher than change of any other mechanical parameter. Such result reveals that MAE is very useful for evaluation of quality of ferrous steel.

PL

Przedstawiono wyniki badań efektu emisji magnetoakustycznej stali 10H2M o różnym stopniu degradacji i w stanie dostawy. Stopień degradacji stali oceniono na podstawie zmian mikrostruktury i własności mechanicznych R0,2, Rm oraz HV. Stwierdzono, iż natężenie emisji magneto-mechanicznej zmniejsza się w sposób monotoniczny ze wzrostem stopnia degradacji, przy czym względna zmiana natężenia tego efektu znacznie przewyższa zmianę twardości a także zmianę R0,2 i Rm. Ten wynik dowodzi, iż zjawisko emisji magneto-akustycznej jest szczególnie przydatne dla oceny jakości stali ferromagnetycznych.

Słowa kluczowe

EN

magneto-acoustic effect; magnetoacoustic emission; steel; microstructure; mechanical properties; quality; ferrous steel; MAE

PL

efekt emisji magnetoakustycznej; emisja magnetoakustyczna; stal; mikrostruktura; własności mechaniczne; jakość; stal ferromagnetyczna; MAE

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2001
• Tom: R. XXII, nr 4
• Strony: 185--188
• Opis fizyczny: Bibliogr.12 poz., rys.

Twórcy

autor

Augustyniak B.

• Physics Department, Technical University of Gdańsk

autor

Piotrowski L.

• Physics Department, Technical University of Gdańsk

autor

Chmielewski M.

• Physics Department, Technical University of Gdańsk

autor

Głowacka M.

• Mechanics Department, Technical University of Gdańsk

autor

Ćwiek J.

• Mechanics Department, Technical University of Gdańsk

autor

Łabanowski J.

• Mechanics Department, Technical University of Gdańsk

• Technical University of Gdańsk, Physics Department

Bibliografia

• [1] James P. J.; The role of non-destructive testing in the control of boiler tube failures; Insight – non – Destructive Testing & Condition Monitoring; 37, no.3, 1995,p. 179
• [2] Devine M. K., Jiles D.: Effects of high temperaturę creep on magnetic properties of steels (pipeline inspection); IEEE Transactions on Magnetics; 28, no.5, Pt. 2.1992, p. 2465
• [3] Chen Z. J., Govindaraju M, R., Jiles D. C., Sablik M. J,: Assessment of Creep Damage of Ferromagnetic Materials Using Magnetic Inspection; EEE Transactions on Magnetics; 30, no.6,1994,p. 4596
• [4] Chen Z. J., Mitra A., Biner S. B., Jilcs D. C.: Detection of creep in Cr- Mo steel by magnetic hysteresis measurement; Review of Progress in Quantitative Nondestructive Evaluation; 14, 1995, p. 1701
• [5] Mitra A., Chen Z. J., Laabs F., Jiles D. C.: Micromagnetic Barkhausen emissions in 2.25 wt% Cr-l wt% Mo steel subjected to creep; Philosophical Magazine A-Physics of Condensed Matter Defects & Mechanical Properties; 75, no. 3, 1997,p. 847
• [6] Sablik M. J., Augustyniak B.: Magnetic Methods of Nondestructive Evaluation; Wiley Encyclopedia of Electrical and Electronics Engineering; 12 (Ma-Mi), I999,p. 12
• [7] Augustyniak B., Chmielewski M., Sablik M. J.: Multiparameter Magnetomechanical NDE; IEEE Trans on Magnetics; 36, no.5, 2000, p. 3624
• [8] Augustyniak B., Chmielewski M., Piotrowski L., Głowacka M.: Assesment of 15HM steel quality with three methods based on Barkhausen effect; 9th International Scientific Conference AMME 2000, Sopot 2000; ed.:Dobrzański L. A.;Silesian Univ. of Technology; Gliwice, 2000,p. 23
• [9] Badania zmian struktury materiałów w warunkach eksploatacji urządzeń energetycznych ze stali żarowytrzymałych typu Cr-Mo - Skala wzorców struktury stali I5HM i 10H2M; Instytut Energetyki, Warszawa; 1975,
• [10] Sablik M. J., Augustyniak B.: Modeling the magnetic field dependence of magnetoacoustic emission and its dependence on creep damage. Review of Progress in Quantitative Nondestructive Evaluation; 19B, no.CP 509, 2000.p. 1557
• [11] Augustyniak B., Piotrowski L., Chmielewski M : Efekt Emisji magnetoakustycznej i jego wykorzystanie w badaniach nieniszczących jakości materiału na przykładzie stali 15HM; Zeszyły Problemowe -Badania Nieniszczące; 5, 2000, p. 105
• [12] Augustyniak B., Piotrowski L., Chmielewski M., Ćwiek J., Łabanowski J.: Badanie emisji magneto-akustycznej oraz własności mechanicznych i mikrostruktury stali 10H2M o różnym stopniu degradacji; Proc.II Pomorska Konferencja Naukowa Inżynieria Materiałowa 2001, Gdańsk-Sobieszewo; ed.:Głowacka M., Serbiński W.: Politechnika Gdańska; Gdańsk, 200l, p. 7