Estimation of safety of straight segments of pipelines for heat and power generating plants according to SINTAP procedures.

• Autorzy: Dzioba I.

Warianty tytułu

PL

Ocena bezpieczeństwa prostoliniowych elementów rurociągów ciepłowniczych wg procedur SINTAP.

• Języki publikacji: EN

Abstrakty

EN

In the paper the assessment of safety of the pipelines elements from the heat and power generating plants of Ukraine made of 12Kh1MF steel has been presented. The SINTAP procedures for failure assessment have been performed assuming two shapes of hypothetical cracks along the straight segments of pipeline. The thermal stresses during the cooling process have been taken into account in the analysis. The analysis has been performed at the first level of SINTAP procedures. Two stages: a) before pipeline operation, and b) after 156000 hours of service work have been analyzed. The comparison of results obtained by other assessment method has been made.

PL

W pracy przeprowadzono ocenę bezpieczeństwa prostoliniowych elementów rurociągów ciepłowniczych wykonanych ze stali 12Kh1MF. Obliczenia wykonano według metodyki SINTAP dla prostoliniowych odcinków rurociągów, zawierających hipotetyczne szczeliny powierzchniowe półeliptyczne i o nieskończonej długości, ulokowane na wewnętrznej ściance rury oraz szczeliny przechodzące na wskroś przez ściankę rury. W artykule analizowano sytuacje podczas stacjonarnego okresu eksploatacji, a także dla przypadku niestacjonarnej eksploatacji - rozgrzewania oraz chłodzenia rurociągu. Analizę przeprowadzono dla materiału w stanie nie eksploatowanym i dla materiału po 156000 godzinach pracy rurociągu. Pokazano, że rezultaty obliczeń dobrze zgadzają się z wynikami uzyskanymi wg innej wcześniej zaproponowanej metodyki.

Słowa kluczowe

EN

SINTAP; failure assessment analysis; material ageing process; pipeline

PL

SINTAP; ocena bezpieczeństwa; starzenie się materiału; rurociąg

• Wydawca: Komitet Budowy Maszyn PAN
• Czasopismo: Archive of Mechanical Engineering
• Rocznik: 2004
• Tom: Vol. LI, nr 3
• Strony: 317--333
• Opis fizyczny: Bibliogr. 21 poz., fot., rys.

Twórcy

autor

Dzioba I.

• Kielce University of Technology, Aleja 1000-lecia Państwa Polskiego 7, 25-314 Kielce, Poland

Bibliografia

• [1] R6: Assessment of the integrity of structures containing defects. British Energy Generation Ltd, 1999.
• [2] British Standard BS7910: Guide on methods for assessing the acceptability of flaws in fusion welded structures, 1999.
• [3] American Petroleum Institute, API579: Recommended practice for fitness for service.
• [4] SINTAP: Structural integrity assessment procedures for European industry. Final Report, July 1999, Contract No BRPR-CT95-0024, Project No BE95-1426, Report No BE95_1426/FR/7.
• [5] Schwalbe K-H., Kim Y-J., Hao S., Cornec A., Kocak M.: EFAM, ETM-MM 96: the ETM method for assessing the significance of crack-like defects in joints with mechanical heterogeneity (strength mismatch). GKSS Report 97/E/9, 1997.
• [6] Schwalbe K-H., Zerbst U., Kim Y-J., Brocks W., Cornec A., Heerens J., Amstutz H.: EFAM ETM 97: the ETM method for assessing crack-like defects in engineering structures. GKSS Report GKSS 98/E/6, 1998.
• [7] Vainman A.B., Melekhov R.K., Smiyan O.D.: Hydrogen embrittlement of high pressure boilers. Kiev, „Scientific Think", 1990 (in Russian).
• [8] Krutasova E.I.: The assessment of the reliability for metal of the energetics equipment. (Nadiożnośt metala energeticzeskogo oborudowania.) Moscow, „Energy", 1981 (in Russian).
• [9] Nakhalov V.A.: The assessment of reliability for the bend segments of the pipelines for the energetics equipment. (Nadiożnośt gibow trub energeticzeskogo oborudowania.) Moscow, „Energy", 1983 (in Russian).
• [10] Dobrzanski J., Hernas A.: Correlation between phase composition and lifetime of lCr-0.5Mo steel during long-term service at elevated temperature. J. Mat. Proc. Tech., 1995, Vol. 53, pp. 101-108.
• [11] Tkach A.N., Dzioba I.R., Islamov A.A., Siminkovich V.N.: Influence of direction of specimens cutting-in and loading rate on static resisting of metal of steam lines. Soviet Materials Science, 1989, No 3, pp. 102-105.
• [12] Romaniv O.M., Nykyforchyn H.M., Student O.Z., Dzioba I.R., Loniuk B.P.: The influence of service damaging on the crack growth resistance characteristics of 12Kh1MF steam pipe-line steel. Physicochemical mechanics of materials. 1998, No 1, pp. 101-104.
• [13] Dzioba I.: The influence of the structural, technological and service parameters on fracture resistance of the 12KhlMF steel. Proc. XVII National Symposium: Fatigue and Fracture Mechanics, Bydgoszcz, 1998, pp.85-91 (in Polish).
• [14] Dzioba I.: Application of the fracture toughness parameters to the estimation of the power pipelines durability. Ph.D. Thesis, Kielce University of Technology, Kielce, 1998 (in Polish).
• [15] Stakhiv Т., Dzioba I., Lonyuk В., Student O.: Structural degradation of the heat resistance steels and its effect on the crack growth peculiarity. Physicochemical Mechanics of Materials, 2002, No 3, pp.67-72.
• [16] Fett Т., Munz D., Neumann J.: Local stress intensity factor for surface cracks in plate under power shaped stress distributions. Eng. Fr. Mech., 1990, Vol. 36, pp.647-651.
• [17] Raju S., Neumann J.: Stress intensity factors influence coefficients for internal and external cracks in cylindrical vessels. ASME PVP, 1978, Vol. 58, pp.37-48.
• [18] Neimitz A.: Fracture mechanics, PWN, 1998 (in Polish).
• [19] Wu X.R., Carlsson A.J.: Weight function and stress intensity factor solution. Pergamon Press, Oxford U.K., 1991.
• [20] Carter A.J.: A library of limit loads for fracture. Two. Nuclear Electric Report TD/SID/REP/091, 1992.
• [21] Wigak V.M.: Optimum controlling of the non-stationary temperature regimes. Kiev, „Scientific Think", 1979 (in Russian).