Nanocrystalline powders of the Al-Ti intermetallic phases.

• Autorzy: Michalski A. , Świderska-Środa A. , Sobczak S. , Pudło J.
• Konferencja: AMT'98 XVth Physical Metallurgy and Materials Science Conference 'Advanced materials & technologies' 17-21 May, 1998, Kraków-Krynica, Poland.
• Języki publikacji: PL

Abstrakty

EN

Nanocrystalline, monodispersive powders of Al3Ti with a average particle size of about 13 nm and Ti3Al with a average particle size of about 17 nm were produced by crystallization from pulse plasma. The reactants of the plasmo-chemical reaction in this process were the ionized vapours of aluminium and titanium generated by evaporating aluminium and titanium electrodes in a heavy -current electrical discharge (the electric current was about 60 kA and the discharge pulse duration - about 100 microseconds).

Słowa kluczowe

PL

faza międzymetaliczna; monodyspersyjny proszek; aluminium; tytan; nanokrystaliczny proszek; dyfrakcja promieniowania rentgenowskiego; wielkość ziarna

EN

intermetallic phase; monodispersive powders; aluminium; titanium; nanocrystalline powders; X-ray diffraction; grain size

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 1998
• Tom: R. XIX, nr 4
• Strony: 917--920
• Opis fizyczny: Bibliogr. 8 poz., tab., rys.

Twórcy

autor

Michalski A.

• Warsaw University of Technology, Department of Material Science, Warsaw

autor

Świderska-Środa A.

• Warsaw University of Technology, Department of Material Science, Warsaw

autor

Sobczak S.

• Warsaw University of Technology, Department of Material Science, Warsaw

autor

Pudło J.

• Warsaw University of Technology, Department of Material Science, Warsaw

• Warsaw University of Technology, Department of Material Science

Bibliografia

• [1] C. Suyanarayana, Guo-Hao Chen, Abdulbaset Frefer, F.H. Froes, Mater. Sci. Eng., A158 (1992) 93.
• [2] H. Gleiter, Nano Struc. Mater., 2 (199).
• [3] R.Bohn, H. Gleiter, Scripta Metall. Matr., 25 (1991) 811.
• [4] R. W. Siegel, Annu. Rev. Mater. Sci., 21 (1991) 559.
• [5] M. Gell, Mater. Sci. Eng. A204 (1995) 246.
• [6] S. T. Schwab, P.P. Paul, Yi-Ming Pan, Mater. Sci. Eng., A204 (1995) 197.
• [7] D. Oleszak, H. Garbacz, H. Matyja, Prace Naukowe Politechniki Warszawskiej, Inżynieria Materiałowa, (1995), z. 1. s.7.
• [8] E. Szewczak, D. Oleszak, A. Świderska-Środa, H. Matyja, Prace Naukowe Politechniki Warszawskiej, Inżynieria Materiałowa, (1995), z. 3. s.7.