Recrystallization of the rolled Cu-5% Al single crystal with the (110)[001] orientation.

• Autorzy: Krawczyk J. , Wróbel M. , Marcisz J. , Dymek S. , Blicharski M.
• Konferencja: XVth Physical Metallurgy and Materials Science Conference on Advanced Materials & Technologies AMT'98, 17-21 May 1998, Kraków-Krynica, Poland
• Języki publikacji: EN

Abstrakty

EN

A CuA15 single crystal with the initial orientation of (110)[001] was rolled with 80% reduction in thickness and subsequently recrystallized. First recrystallized grains appeared in the sample annealed at 335 degrees centigrade while the sample annealed at 385 degrees centigrade was fully recrystalized. The recrystallization texture showed following components: {112}<238>, {135}<479> and {125}<259>. Only the strongest component {112}<238> could be produced according to the oriented growth theory.

Słowa kluczowe

EN

recrystallization; single crystal; microstructure; deformation; annealing; cold-rolling

PL

rekrystalizacja; monokryształ; mikrostruktura; odkształcenie; wyżarzanie; walcowanie na zimno

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 1998
• Tom: R. XIX, nr 3
• Strony: 488--489
• Opis fizyczny: Bibliogr. 4 poz., rys.

Twórcy

autor

Krawczyk J.

• University of Mining and Metallurgy, Faculty of Metallurgy and Materials Science, Kraków, Poland

autor

Wróbel M.

• University of Mining and Metallurgy, Faculty of Metallurgy and Materials Science, Kraków, Poland

autor

Marcisz J.

• University of Mining and Metallurgy, Faculty of Metallurgy and Materials Science, Kraków, Poland

autor

Dymek S.

• University of Mining and Metallurgy, Faculty of Metallurgy and Materials Science, Kraków, Poland

autor

Blicharski M.

• University of Mining and Metallurgy, Faculty of Metallurgy and Materials Science, Kraków, Poland

• University of Mining and Metallurgy, Faculty of Metallurgy and Materials Science, Kraków

Bibliografia

• [1] W. Ratuszek, Tekstury odkształcenia i rekrystalizacji w stopach na osnowie miedzi, Rozprawy- Monografie nr 27, wyd. AGH, Kraków 1995.
• [2] J. Krawczyk, M. Wróbel, S. Dymek and M. Blicharski, Archives of Metallurgy, 42 (1997) 79.
• [3] B. Libmann, K. Lücke and G. Masing, Z. Metallkd., 47 (1956) 74.
• [4] A. Berger, P. Wilbrant, F. Ernst, D. Klement and P. Haasen, Progress in Materials Science 32 (1987) 1.