Morphology, mechanical and viscoelastic properties of rubbery-epoxy/organoclay mica nanocomposites

• Autorzy: Boukerrou A.
• Konferencja: Seminarium Tworzywa Sztuczne w Budowie Maszyn (11 ; 2006 ; Kraków)
• Języki publikacji: EN

Abstrakty

EN

Morphology, mechanical, and viscoelastic properties of rubbery epoxy/organoclay MICA (MICA) nanocomposites were investigated by wide angle X-ray scattering (WAXS), transmission electron microscopy (TEM), tensile testing, and dynamic mechanical thermal analysis (DMTA). Ultrasonicator was used as a means of applying external shearing forces to disperse the silicate clay layers in the epoxy matrix. The study showed that the addition of 5 phr of MICAC18 into the epoxy matrix resulted in finer dispersion as evidenced by both the disappearance of the diffraction peak in the WAXS pattern and TEM images. The mechanical and viscoelastic properties were improved for both MICA and MICAC18 nanocomposites, however more pronounced for the modified ones.

PL

W pracy przedstawiono właściwości mechaniczne i dynamiczne oraz mikrostrukturę nanokompozytów na osnowie żywic epoksydowych modyfikowanych nanocząstkami.

Słowa kluczowe

EN

epoxy; mechanical and viscoelastic properties; MICA; morphology; nanocomposites

PL

MICA; nanokompozyty; właściwości mechaniczne; żywica epoksydowa

• Wydawca: Wydawnictwo Politechniki Krakowskiej im. Tadeusza Kościuszki
• Czasopismo: Czasopismo Techniczne. Mechanika
• Rocznik: 2006
• Tom: R. 103, z. 6-M
• Strony: 65--70
• Opis fizyczny: Bibliogr. 16 poz.,Wykr., il., tab.,

Twórcy

autor

Boukerrou A.

• Laboratoire des Materiaux Organiques, Universite Abderrahmane Mira, Bejaia 06000, Algeria,

Bibliografia

• [1] Kornman X.; Lindberg H., Berglund L.A.: Polymer 2001, 42, 4493.
• [2] Chin I.J., Thurn-Albrecht T., Kim,H. C., Russel T.P., Wang J.: Polymer 2001, 42, 5947.
• [3] Evora, V.M.F.; Shukla, A. Mater Sci Eng 2003, A363, 358.
• [4] Kornamn X.; Lindberg H., Berglund R.A.: Polymer 2001, 42, 1303.
• [5] Nigam V., Setua D. K., Matur G. N., Kar K. K.: J Appl Polym Sci 2004, 93, 2201.
• [6] Mascia, L.; Prezzi, I.; La Vormia, M. Polym Eng Sci 2005, 45, 1039.
• [7] Alexandre, M., Dubois P.: Mater Sci Eng 2000, 28, 1.
• [8] Asma Y., Jandro L.A., Issac M. D.: Scripta Materialia 2003, 40, 81.
• [9] Vaia R. A., JandtK. D., Kramer E. J. Giannelis E. P.: Chem Mater 1996, 8, 2628.
• [10] Ryu J.G., Kim H., Lee J.W.: Polym. Eng. Sci. 2004, 44, 1198.
• [11] Le Pluart L.: Doctorat thesis presented at INSA, Villeurbanne-LYON (France), 2002.
• [12] Le Pluart L., Duchet J., Sautereau H., Gerard J.F. J.: Adhesion. 78, 2002, 645-662.
• [13] Lee K.Y., Goettler L.A.: Polym. Eng. Sci. 2004, 44, 1103.
• [14] Pinnavaia T. J., Lan T., Karavatina P. D., Wang Z., SHI H.: ACS Polym Mater Sci Eng 1996, 74, 117.
• [15] Wang Z.: Pinnavaia, T. J. Chem Mater 1998, 10, 1820.
• [16] Wang M.J.: Rub Chem Technol 1998, 71, 520.