A comparative study of the mechanical, dielectical and thermal behavior of polyvinyl chloride (PVC) filled with calcium carbonate and wood flour

• Autorzy: Djidjelli H.
• Konferencja: Seminarium Tworzywa Sztuczne w Budowie Maszyn (11 ; 2006 ; Kraków)
• Języki publikacji: EN

Abstrakty

EN

Two types of PVC formulations with calcium carbonate and olive wood flour content respectively (PVC/CaCO3 and PYC/WF) were prepared by calendering at 180[degrees]C temperature with a 8- minute sojourn. 0.3 mm thick films obtained in this manner are cut into dumbbell-shaped test specimen which would serve there after in the study of mechanical, thermal and dielectrical characteristics. The results obtained have shown that calcium carbonate filled PVC test specimen has better mechanical, thermal and dielectric insulation properties. On the other hand, wood flour filled PVC formulations are cheaper, lighter, more esthetic, and biodegradable and have higher dielectric losses which can find applications other than in insulation.

PL

Próbki dwóch typów kompozytów na osnowie PVC z dodatkiem węglanu wapnia i mączki drzewa oliwnego zostały wytworzone metodą kalandrowania w tem. 180[stopni]C przez 8 min. Pobrano próbki o grubości 3 mm do badań właściwości mechanicznych, termicznych i dielektrycznych. Rezultaty wskazują, że dodatek węglanu wapnia poprawia badane właściwości. Z drugiej strony dodatek mączki drzewnej do PCV daje możliwość uzyskania tańszych, lżejszych, bardziej estetycznych i częściowo biodegradowalnych o wyższej przewodności dielektrycznej elementów.

Słowa kluczowe

EN

calcium carbonate; dielectrical proprieties; polymer composite; weedflour

PL

kompozyty polimerowe; mączka drzewna; węglan wapnia; właściwości dielektryczne

• Wydawca: Wydawnictwo Politechniki Krakowskiej im. Tadeusza Kościuszki
• Czasopismo: Czasopismo Techniczne. Mechanika
• Rocznik: 2006
• Tom: R. 103, z. 6-M
• Strony: 139--148
• Opis fizyczny: Bibliogr. 14 poz.,Wykr., il., tab., wz

Twórcy

autor

Djidjelli H.

• Laboratoire des Materiaux Organiques, Univeriste A. Mira, Bejaia, Algerie,

Bibliografia

• [1] Oksman K., Lindberg H., J. Applied Polymer Science, 68, 1998, 1845-1855.
• [2] Liano B., Huang Y., Cong G., J. Applied Polymer Science, 66, 1997, 1561-1568.
• [3] Zaini M.J., Fuad M.Y.A, Ismail Z., Mansor M.S., Mustafah J., Polymer International, 40, 1, 1996, 51-56.
• [4] Nitz H., Reichert P., Römling H., Mülhaupt R., Macrol. Mat. Eng., 276-277, Issue 1, 2000, 51-58.
• [5] Xu B., Simonsen J., (Skip) Rochefort W.E, J. Applied Polymer Science, 79, 2001, 418-425.
• [6] Matuana L.M., Mengeloglu F., J. Vinyl & Additive Technology 2001, 7, 67.
• [7] Pedro B.M.A., Monteiro E.E.C., Dweck J., Polymer Testing, 20, 2001, 269-273.
• [8] Sain M.M., Balatinecz J., Law S., J. Applied Polymer Science, 77, 2000, 260-268.
• [9] Jakubowicz I., Yarahmadi N., Gevert T., Polymer Degradation and Stability, 66, 1999, 415-421.
• [10] Celina M., Ottesen D.K., Gillen K.T., Clough R.L, Polymer Degradation and Stability, 58, 1997, 15-31.
• [11] Okieimen F.E., Eromonsele O.C., J. Appl. Polym. Sc., 77, 2000, 1432-1438.
• [12] Brebu M., Vasile C., Antonie S.R., Chiriac M., Precup M., Yang J., Roy C., Polym. Degrad. and Stab., 67, 2000, 209-221.
• [13] Matuschek G., Milanov N., Kettrup A., Thermochimica Acta, 361, 2000, 77-84.
• [14] Gondard C., Scherrenberg R., Reynaers H., Polymeric Materials Encyclopedia, 1996, CRC Press, INC.