The influence of ball milling conditions on the mechanical decomposition of Cu-hydroxycarbonate

• Autorzy: Powałka E. , Jagosz M. , Gamrat K. , Janicka E. , Wieczorek-Ciurowa K.

Warianty tytułu

PL

Wpływ warunków mielenia kulowego na rozkład hydroksowęglanu miedzi

• Konferencja: Międzynarodowa Konferencja Młodych Naukowców "Środowisko, Rozwój, Inżynieria, Modelowanie" (5 ; 2004 ; Kraków)
• Języki publikacji: EN

Abstrakty

EN

The quantity of copper oxide formed from Cu2(OH)2CO3 during mechanical activation using planetary ball mill (FRITSCH Pulverissette 6) was calculated on the basis of TG/DTG-DTA curves of milling products. The effects of different milling circumstances such as: ball size and ball-to-powder mass ratio are presented. For obtaining the highest level of degree decomposition of Cu2(OH)2CO3 the following parameters can be recommended: 10-mm balls, BPR = 10:1 milling time - 180 min at maximum speed of 600 rpm.

PL

Ilości tlenku miedzi powstającego z rozkładu Cu2(OH)2CO3 podczas mechanicznej aktywacji przy użyciu młynka planetarnego (FRITSCH Pulverissette 6) były określone na podstawie analizy krzywych TG/DTG-DTA produktów mielenia. Wykazano różne efekty mielenia w zależności od zastosowanychwarunków, takich jak: średnica mielników, stosunek mas mielników do materiału mielonego. Dla uzyskania najwyższego stopnia rozkładu Cu2(OH)2CO3 zalecane jest użycie: mielników 10 mm, BPR = 10:1, czasu mielenia - 180 min i maksymalnej liczby obrotów = 600 rpm.

Słowa kluczowe

EN

Cu-hydroxycarbonate; decomposition; mechanical activation; planetary ball mill

PL

Cu-hydroksowęglan; mechaniczna aktywacja; młynek planetarny; rozkład

• Wydawca: Wydawnictwo Politechniki Krakowskiej im. Tadeusza Kościuszki
• Czasopismo: Czasopismo Techniczne. Środowisko
• Rocznik: 2004
• Tom: R. 101, z. 9-Ś
• Strony: 70--76
• Opis fizyczny: Bibliogr. 9 poz., wykr., tab.

Twórcy

autor

Powałka E.

• student, Faculty of Chemical Engineering and Technology, Cracow University of Technology, Warszawska 24, 31-155 Cracow, Poland

autor

Jagosz M.

• student, Faculty of Chemical Engineering and Technology, Cracow University of Technology, Warszawska 24, 31-155 Cracow, Poland

autor

Gamrat K.

• Institute of Inorganic Chemistry and Technology, Cracow University of Technology, Warszawska 24, 31-155 Cracow, Poland

autor

Janicka E.

• Institute of Inorganic Chemistry and Technology, Cracow University of Technology, Warszawska 24, 31-155 Cracow, Poland

autor

Wieczorek-Ciurowa K.

• Institute of Inorganic Chemistry and Technology, Cracow University of Technology, Warszawska 24, 31-155 Cracow, Poland

Bibliografia

• [1] Balaž P., Mechanical activation in hydrometallurgy, Int. J. Miner. Process., 72, 2003, 341.
• [2] Suryanarayana C., Ivanov E., Boldyrev V.V., The science and technology of mechanical alloying, Mater. Sci. Eng., A151, 2001, 304.
• [3] Kwon Y.S., Gerasimov K.B., Yoon S.K., Ball temperatures during mechanical alloying in planetary mills, J. Alloys Compounds, 346, 2002, 276.
• [4] Avvakumov E., Senna M., Kosova N., Sofi Mechanochemical Synthesis: a Basis for New Chemical Technologies, Kluver Acad. Publ., Boston 2001.
• [5] Drzymała Z., Badania i podstawy konstrukcji młynów specjalnych, Wyd. Naukowe PWN, Warszawa 1992.
• [6] Wieczorek-Ciurowa K., Shirokov Ju.G., Paryło M., The use of thermogravimetry to assess the effect of mechanical activation of selected inorganic salts, J. Therm. Anal. Cal., 60, 2000, 59.
• [7] Jagosz M., Powałka E., Wpływ warunków mechanicznej aktywacji na rozkład hydroksowęglanu miedzi w młynku planetarnym, Cracow University of Technology, Cracow 2004 (in Polish).
• [8] Delogu F., Schiffini L., Cocco G., The invariant laws of the amorphization processes by mechanical alloying, I. Experimental findings, Philos. Mag., A, 81, 2001, 1917.
• [9] Murty B.S., Ranganathan S., Nowel materials synthesis by mechanical alloying/milling, Intern. Mater. Rev., A, 43, 1998, 101.

Uwagi

The study was supported by the KBN Project No. 4T09B07024.