Damage problems in glued laminated timber

• Autorzy: Vanya C.

Warianty tytułu

PL

Problemy uszkodzeń w tarcicy klejonej warstwowo

• Języki publikacji: EN

Abstrakty

EN

On a number of occasions glued laminated timber breaks apart before the end of their service life. Examples in Germany (Frese M., Blaß H. J. [2011]) and Denmark (Hansson, Larsen [2005] ) show that this problem is real. In order to find the causes of the problem, extensive tests were conducted: 16 buildings with glued laminated timber were examined on the spot, calculations and laboratory work were carried out. These examinations told us that not only did the properties of the wooden material cause the damage, but the problems were also due to the wood used and the method of construction. In the calculations, the external load and residual stresses occurring in the glued laminated timber were included. Residual tensions in this timber were generated by climatic stresses and also due to the method of construction. These stresses also accumulated along with the stresses of the external load. Laboratory work was carried out to measure the delamination. We examined whether these analyses and calculations prove or disprove the results of the on- the- spot examinations.

PL

Wyniki obliczeń potwierdzają obserwacje dokonane w warunkach naturalnych. Naprężenia wewnętrzne spowodowane właściwościami klimatycznymi muszą być uwzględniane przy projektowaniu, w procesie produkcyjnym oraz użytkowaniu. Badania laboratoryjne potwierdzają zjawiska widoczne w rzeczywistej konstrukcji budowlanej. Badania powinny być kontynuowane w celu uzyskania większej ilości informacji na temat rozwarstwiania oraz opracowania rozwiązań dla projektantów, producentów drewna typu glulam lub właścicieli budynków.

Słowa kluczowe

EN

stresses in glued laminated timber; internal stresses; manufacturing stresses; climatic stresses; damage of glued laminated timber; reasons for damage

PL

naprężenia w tarcicy klejonej warstwowo; naprężenia wewnętrzne; naprężenia podczas procesu produkcyjnego; naprężenia klimatyczne; uszkodzenia tarcicy klejonej warstwowo; przyczyny uszkodzeń

• Wydawca: Sieć Badawcza Łukasiewicz - Poznański Instytut Technologiczny
• Czasopismo: Drewno : prace naukowe, doniesienia, komunikaty
• Rocznik: 2012
• Tom: vol. 55, nr 188
• Strony: 115--128
• Opis fizyczny: Bibliogr. 28 poz., rys., tab.

Twórcy

autor

Vanya C.

• University of Pécs, Hungary,

Bibliografia

• 1. Angst V., Malo A. K. [2012]: Moisture-induced stresses in glulam cross sections during wetting exposures. Wood Science Technology, DOI 10.1007/s00226-012-0493-8
• 2. Bartal és Rabb Kft. [2010]: Kutatási jelentés a baross rrtarto1 omfb-00398/2010 számú pályázathoz, 118
• 3. D’Amico S., Hrabalova M., Müller U., Berghofer E. [2012]: Influence of ageing on mechanical properties of wood to wood bonding with wheat flour glue. European Journal of Wood and Wood Products, DOI 10.1007/s00107-012-0595-x
• 4. Frese M., Blaß H. J. [2011]: Statistics of damage to timber structures in Germany, Contents lists available at SciVerse ScienceDirect. Engineering Structures [33]: 2969–2977
• 5. Häglunk M. [2009]: Parameter influence on moisture induced eigen-stresses in timber. European Journal of Wood and Wood Products [68]: 397–406, DOI 10.1007/s00107-009--0377-2
• 6. Heimeshoff B. [1973]: Spannungsberechnung für den gekrümmten Träger mit einfach-symmetrischem Querscnitt. Stress Calculations for Curved Trusses with Single-Symmetry Crosscuts. Holz als Roh- und Werkstoff [31]: 475–480
• 7. Garab J., Tóth Á., Szalai J., Bejó L., Dívós F. [2010]: Evaluating glued laminated beams using a nondestructive testing technique. Transactions of Famena 34 [4]: 33–46
• 8. Gustafsson P. J., Hoffmeyer P., Valentin G. [1998]: DOL behaviour of end-notched beams. Holz als Roh- und Werkstoff [56]: 307–317
• 9. Hansson M., Larsen H.J. [2005]: Recent failures in glulam structures and their causes. Engineering Failure Analysis [12]: 808–818
• 10. Kánnár A. [2012]: Szakmai zárójelentés A Baross Rrtarto1 Omfb-00398/2010 számú pályázathoz, 22
• 11. Möhler K. [1976a]: Zur Berechnung von Brettschichtholz-Konstruktionen. Holzbau-Statik-Aktuell [1]: 2–8
• 12. Möhler K. [1976b]: Spannungsberechnung von gekrümmten Brettschichtträgern it konstanter und veränderlicher Querschnittshöhe. Bauen mit Holz, 5–8
• 13. Möhler K. und Hemmer Kl. [1980]: Spannungskombination bei Brettschichtträgern mit geneigten Rändern. Holzbau-Statik-Aktuell [5]: 6–8
• 14. Niemz P., Bärtschi H., Howald M. [2005] Untersuchungen zur Feuchteverteilung und Spannungsausbildung in Holzbauteilen bei Wechselklimalagerung. Schweiz. Z. Forstwes.156 [3–4]: 92–99
• 15. Noack D. und Roth W. [1972]: Berechnung gekrümmter Brettschichtträger unter Belastung durch Momente, Normal- und Querkräfte. Holz als Roh- und Werkstoff [30]: 220–233
• 16. Olejniczak P., Gustafsson P. J. [1994]: Rate effect in tangential tension fracture softening performance, Cost 508- Wood mechanics, Workshop on service life assessment of wooden structures with special emphasis on the effect of load duration in various environments. Technical Research Centre of Finland, 137–147
• 17. Roth W. [1975]: Festigkeitsuntersuchungen an gekrümmten Brettschicht trägern unter statischer und dynamischer Belastung, Dissertation. Von der für Bauingenieur-und Vernessungswesen der Universität Karlsruhe (TH), 1–51
• 18. Roth W., Epple A. [1981a]: Vergleichende isotrope und orthotrope Berechnung gekrümmter Brettschichtträger, Teil 1: Theoretische Grundlagen. Holz als Roh- und Werkstoff[39]: 25–31
• 19. Roth W., Epple A. [1981b]: Vergleichende isotrope und orthotrope Berechnung gekrümmter Brettschichtträger, Teil 2: Anwendungsbeispiel und Versuchsergebnisse. Holz als Roh- und Werkstoff [39]: 113–117
• 20. Schelling W. [1981]: Berechnung gekrümmter Brettschichtträger mit Biegebeanspruchung. Holz als Roh- und Werkstoff [39]: 4/158–4/160
• 21. Szalai J. [1985]: Rétegelt ragasztott íves fatartók gyártása során, valamint klimaváltozás következtében fellépő sajátfeszültségeinek és alakváltozásának meghatározása, Kandidátusi értekezés. Sopron, 151
• 22. Szalai J. [1997]: A faanyag anizotrop szilárdsági jellemzői, az MTA Doktori tudományos cím megszerzéséért benyújtott disszertáció. Sopron, 248
• 23. Szalai J. [1984-85]: Rétegelt-ragasztott íves fatartók gyártása során, valamint klímaváltozás következtében fellépő sajátfeszültségeinek és alakváltozásainak meghatározása, Kandidátusi értekezés tézisei, 11
• 24. Szalai J. [2001]: A faszerkezetek méretezését és gyártását befolyásoló sajátosságok. (Wittmann Gy. szerk.) Mérnöki faszerkezetek II., Mezőgazdasági Szaktudás Kiadó, Budapest, 143–258
• List of standards
• 25. EN 386:2001 Glued laminated timber. Performance requirements and minimum production requirements
• 26. ISO 554:1976 Standard atmospheres for conditioning and/or testing. Specifications
• 27. MSZ EN 386:2002 Rétegelt-ragasztott fa. Teljesítménykövetelményének és a gyártás alapkövetelményei
• 28. MSZ 2370:2003 Vizsgálati normák légterek