Thixotropic compositions: unsaturated polyester resins/ modified bentonites

• Autorzy: Oleksy M. , Heneczkowski M. , Galina H.

Warianty tytułu

PL

Kompozycje tiksotropowe: nienasycone żywice poliestrowe/modyfikowane bentonity

• Języki publikacji: EN

Abstrakty

EN

Nearly 40 quaternary ammonium chlorides were tested as modifiers of a bentonite (smectic clay). The modified bentonite was used as thixotropic agent for a general purpose unsaturated polyester resin. The modification changed the thermal characteristic of bentonites (DSC) and led to increased distance between layers in bentonite grains (X-ray diffraction). The structure of ammonium salt, namely the kind and size of substituents, had a significant effect on thixotropic properties of unsaturated resin compositions. The thixotropic properties were measured by recording viscosity hysteresis by rotary rheometer and evaluating the absolute and standard thixotropic indices. From the point of view of thixotropic properties of unsaturated polyester compositions, the best quaternary ammonium salt modifier had one benzyl and one slightly branched aliphatic hydrocarbon substituent.

PL

Na przykładzie kilkudziesięciu IV-rzędowych soli amoniowych jako modyfikatorów bentonitu oceniono wpływ różnego rodzaju podstawników przy atomie azotu na ich efektywność jako środków tiksotropowych do nienasyconych żywic poliestrowych (tabela 1). Modyfikowane próbki betonitu zastosowano w charakterze środków tiksotropujących konstrukcyjną nienasyconą żywicę poliestrową. Taka organofilizacja spowodowała zmianę termochemicznej charakterystyki bentonitów (badanej metodą DSC, rys. 1) i doprowadziła do zwiększenia odległości pomiędzy warstwami glinki (mierzonej metodą dyfrakcji promieni X, rys. 2). Rodzaj i wymiary podstawników w soli amoniowej w istotny sposób wpływają na obserwowane polepszenie tiksotropowych właściwości uzyskiwanych kompozycji (tabela 2). Właściwości te określano mierząc pętlę histerezy lepkości za pomocą reometru obrotowego oraz wyznaczając bezwzględny i standardowy wskaźnik tiksotropii a także indeks tiksotropii (rys. 3-5). Najkorzystniejszymi modyfikatorami bentonitu okazały się sole amoniowe zawierające podstawnik benzylowy i alkilowy o długim, słabo rozgałęzionym łańcuchu.

Słowa kluczowe

EN

unsaturated polyester resin; bentonite; modification quaternary ammonium salts; rheological properties; thixotropic indexes; viscosity hysteresis

PL

żywica poliestrowa nienasycona; bentonit; czwartorzędowe sole amoniowe; właściwości reologiczne; bezwzględny i standardowy wskaźnik tiksotropii

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2007
• Tom: T. 52, nr 5
• Strony: 345--350
• Opis fizyczny: Bibliogr. 28 poz.

Twórcy

autor

Oleksy M.

autor

Heneczkowski M.

autor

Galina H.

• Rzeszow University of Technology, Faculty of Chemistry, 35-959 Rzeszow, Poland,

Bibliografia

• 1. Kembłowski Z.: “Rheometry of Non-Newtonian Fluids” (in Polish), WNT, Warsaw 1973.
• 2. Cheng D. C. H., Evans F.: Brit. J. Appl. Phys. 1965, 16, 1599.
• 3. Cheng D. C. H.: Rheol. Acta 1973, 12, 228.
• 4. Ferguson J., Hodson N. E.: J. Phys. E. 1975, 8, 526.
• 5. Hodson N. E., Ferguson J.: Trans. Soc. Rheol. 1976, 20, 265.
• 6. Kembłowski Z., Petera J.: Rheol. Acta 1979, 18, 702.
• 7. Kembłowski Z., Petera J.: Rheol. Acta 1980, 19, 529.
• 8. Pignon F., Magnin A., Piau J. M.: J. Rheol. 1998, 42, 1349.
• 9. Quemada D.: Eur. Phys. J. Appl. Phys. 1999, 2, 191.
• 10. O’Brien V. T., Mackay M. E.: J. Rheol. 2002, 46, 557.
• 11. Bharadwaj R. K., Mehrabi A. R., Hamilton, C., Trujillo C., Murga M., Fan R., Chavira A., Thompson A. K.: Polymer 2002, 43, 3699.
• 12. Barthelmes G., Pratsinis S. E., Buggisch H.: Chem. Eng. Sci. 2003, 58, 2893.
• 13. Dullert K., Mewis J.: Rheol. Acta 2005, 45, 23.
• 14. Jawahar P., Gnanamoorthy R., Balasubramanian M.: Wear 2006, 7--8, 835.
• 15. Galindo-Rosales F. J., Rubbio-Hernandez F. J.:Appl. Clay Sci. 2006, 33, 109.
• 16. Mao C. F., Chen J. C.: Food Hydrcoll. 2006, 20, 730.
• 17. Brzozowska T., Zieliński J.: Polimery 2006, 51, 212.
• 18. Oleksy M.: “Thixotropic compositions of unsaturated polyester resins of improved stability with modified smectites” (in Polish), PhD Thesis, 2000, Silesian University of Technology, Gliwice.
• 19. Oleksy M., Galina H.: Polimery 1999, 44, 430.
• 20. Oleksy M., Galina H.: Polimery 2000, 45, 541.
• 21. Galina H., Oleksy M.: in “Quaternary ammonium salts and their applications” (in Polish), Wyd. Inst. Techn. Drewna, Poznań 2001, str. 133--146.
• 22. Oleksy M., Heneczkowski M.: Polimery 2004, 49, 806.
• 23. Oleksy M., Heneczkowski M.: Polimery 2005, 50, 143.
• 24. Oleksy M., Heneczkowski M., Galina H.: Polimery 2006, 51, 799.
• 25. Polish Pat. PL 178 899 (2000).
• 26. Polish Pat. PL 178 900 (2000).
• 27. Pigłowski J., Kiersnowski A., Dołęga J.: Polimery 2006, 51, 704.
• 28. Gołębiewski J., Różański A., Gałęski A.: Polimery 2006, 51, 374.