Modification of styrene-isoprene-styrene triblock copolymer with a core-shell filler

• Autorzy: Jakuczek L. , Gutmann J. S. , Herrmann Ch. , Żuchowska D.

Warianty tytułu

PL

Trójblokowy kopolimer styren-izopren-styren modyfikowany napełniaczem o strukturze rdzeń-otoczka

• Języki publikacji: EN

Abstrakty

EN

Mechanical properties of composite materials based on triblock poly(styrene-b-isoprene-b-styrene) copolymers (SIS) and modified with two different grades of core-shell fillers (core - silsesquioxane microgel, shell - grafted polystyrene, particle diameters 15.7 and 17.7nm, respectively). Significant improvement - almost 60% increase in tensile strength, relative elongation at break reaching 700% - was observed in case of a high molecular weight (Mw) copolymer at the maximal filler concentration of about 2 wt. % and longer chains of the polystyrene-shell. The rheological properties of nanocomposites differed with respect to the non-modified copolymer - softening of the material at higher temperatures was noticed.

PL

Zbadano właściwości mechaniczne kompozytów trójblokowych kopolimerów poli(styren-b-izopren-b-styren) (SIS) modyfikowanych dwoma różnymi napełniaczami o strukturze rdzeń-otoczka (rdzeń - mikrożel polisilseskwioksanowy, powłoka - zaszczepiony polistyren, średnice nanocząstek, odpowiednio 15,7 lub 17,7nm). Zaobserwowano poprawę właściwości badanych materiałów na skutek napełniania, zwłaszcza w przypadku kopolimerów o dużym ciężarze cząsteczkowym (Mw) (tabela 1), zawartości napełniacza nieprzekraczającej 2 % mas. i dłuższych łańcuchach w polistyrenowej otoczce (tabela 3, rys. 1 i 2). Stwierdzono wystąpienie różnic we właściwościach reologicznych nanokompozytów w stosunku do wyjściowych kopolimerów (rys. 3). W podwyższonej temperaturze zaobserwowano mięknienie materiału.

Słowa kluczowe

EN

thermoplastic elastomers; nanocomposites; microgels grafted with polymers; rheological properties; mechanical properties

PL

elastomery termoplastyczne; nanokompozyty; mikrożele zaszczepione polimerem; właściwości reologiczne; właściwości mechaniczne

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2008
• Tom: T. 53, nr 11-12
• Strony: 888--892
• Opis fizyczny: Bibliogr. 21 poz.

Twórcy

autor

Jakuczek L.

autor

Gutmann J. S.

autor

Herrmann Ch.

autor

Żuchowska D.

• Wrocław University of Technology, Faculty of Chemistry, ul. Wybrzeże Wyspiańskiego 27, 50-370 Wrocław, Poland,

Bibliografia

• 1. Hamley L W.: 'The physics of block copolymers", Oxford University Press, Oxford 2003.
• 2. "Handbook of organic-inorganic hybrid materials and nanocomposites", vol. I and II, (Ed. Nalwa H. S.), American Sci. Publ., Valencia CA 2003.
• 3. Kasperski M.: Polimery 2002, 47, 801.
• 4. Hsieh H. L., Quirk R. P: "Anionie Polymerization: principles and practical applications", Mar cel Dek-ker Inc., New York 1996.
• 5. Ganguly A., De Sarkar M., Bhomwick A. K.: /. App. Polym. Sci. 2006,100,2040.
• 6. Jakuczek L., Żuchowska D., Jesionowski T., Krysz-tafkiewicz A.: Ann. Poi. Chem. Soc. 2004, 975.
• 7. Żuchowska D., Meissner W., Jakuczek L., Kowalska D.: Inżynieria Materialowa 2006, 6,1303.
• 8. Matyjaszewski K., Xia S.: Chem. Rev. 2001,101, 2921.
• 9. Tsujii Y., Ohno K., Yamamoto S., Goto A., Fukuda T.:, Adv. Polym. Sci. 2006,197,1.
• 10. Bockstaller M., Mickiewicz R., Thomas E.: Adv. Mater. 2005,17,1331.
• 11. Balazs A. C., Singh C., Zhulina E., Chern S., Lyats-kaya J., Pickett G.: Próg. Surf. Sci. 1997, 553 181.
• 12. Mori H., Lanzendórfer M. G., Miiller A. E. H., Klee J. E.: Macromolecules 2004, 37, 5228.
• 13. Loy D., Rahimian K.: "Building hybrid organic-inorganic materials using silsesquioxanes", in "Handbook of organie- inorganic hybrid materials and nanocomposites", vol. 1., (Ed. Nalwa H. S.), American Sci. Publ. 2003, p. 81.
• 14. Baumann F., Schmidt M., Deubzer B., Geck M., Dauth J.: Macromolecules 1994, 27, 6102.
• 15. Jakuczek L., Gutmann J. S., Miiller B., Rosenauer C., Żuchowska D.: Polymer 2008,49, 843.
• 16. Fu B. X., Lee A., Haddad T. S.: Macromolecules 2004, 37,5211.
• 17. Lindenblatt G., Schartl W., Pakuła T., Schmidt M.: Macromolecules 2000, 33, 9340.
• 18. Pyun J., Jia S., Kowalewski T., Patterson G. D., Matyjaszewski K.: Macromolecules 2003, 36, 5094.
• 19. Ward I. M., Sweeney J.: "Ań introduction to the me-chanical properties of solid polymers", 2nd edition, John Wiley & Sons, Ltd., Chichester 2004.
• 20. Lindenblatt G., Schartl W., Pakuła T, Schmidt M.: Macromolecules 2001, 34,1730.
• 21. Jakuczek L., Gutmann J. S., Żuchowska D., in preparation.