Synthesis and characterisation of precipitated copper(II) silicates

• Autorzy: Modrzejewska-Sikorska A. , Ciesielczyk F. , Krysztafkiewicz A. , Jesionowski T.

Warianty tytułu

PL

Synteza i charakterystyka wytrąconych krzemianów miedzi(II)

• Języki publikacji: EN

Abstrakty

EN

The study was undertaken to obtain a blue inorganic pigment of copper(II) silicate of high degree of dispersion. The process of precipitation of synthetic copper(II) silicates was optimised. The effect of the direction of dosing, percent concentration and volume ratio of the reagents, temperature and type of copper salt used on the physico-chemical properties of the products was studied. The copper(II) silicate obtained was characterised by satisfactory parameters; bulk density of 198 g/dmł, water absorbing capacity of 225 cmł/100g and paraffin oil absorbing capacity of 300 cmł/100g. The diameters of the precipitated silicates varied from 0.955 – 120.2 ěm, with a dominant presence of larger particles making secondary agglomerates.

PL

Przeprowadzone badania miały na celu otrzymanie niebieskiego nieorganicznego pigmentu krzemianu miedzi(II). Badano wpływ sposobu dozowania, stężenia procentowego, stosunku objętości reagentów, temperatury procesu oraz rodzaju użytej soli miedzi na fizykochemiczne właściwości otrzymywanych produktów końcowych. Otrzymany krzemian miedzi charakteryzował się zadawalającymi parametrami, takimi jak: gęstość 198/dm3, pojemność absorbowanej wody 225 cm3/100g, pojemność absorbowanego oleju parafinowego 300cm3/100g. Średnice wytrąconych cząstek krzemianów zmieniały się od 0,55 do 120,2 žm, z dominacją dużych cząstek tworzących wtórne agregaty.

Słowa kluczowe

EN

copper silicate; precipitation process; particle size distribution; wettability; colorimetric data

PL

krzemian miedzi; precypitacja, skład ziarnowy; zwilżalność; dane alorymetryczne

• Wydawca: Oficyna Wydawnicza Politechniki Wrocławskiej
• Czasopismo: Physicochemical Problems of Mineral Processing
• Rocznik: 2010
• Tom: Vol. 44
• Strony: 157--168
• Opis fizyczny: Bibliogr. 18.poz.

Twórcy

autor

Modrzejewska-Sikorska A.

autor

Ciesielczyk F.

autor

Krysztafkiewicz A.

autor

Jesionowski T.

• Poznan University of Technology, Institute of Chemical Technology and Engineering M. Sklodowskiej-Curie 2 Sq, 60-965 Poznan, Poland,

Bibliografia

• 1. ANASTASIADIS S., CHRISSOPOULOUA K., FRICKC B., 2008, Structure and dynamics in polymer/layered silicate nanocomposites, Materials Science and Engineering B, 152, 33–39.
• 2. EL-NAHHAL Y.Z., LAGALY G., 2005, Salt effects on the adsorption of a pesticide on modified bentonites, Colloid Polym. Sci., 283, 968–974.
• 3. ERFURTH U., 1998, Farby na bazie żywic silikonowych – mity i rzeczywistość, Renowacje, 3, 17–23.
• 4. JOHNSTON J., MCFARLANE A., BORRMANN T., MORAES J., 2004, Nano–structured silicas and silicates – new materials and their applications in paper, Current Applied Physics, 4, 411–414.
• 5. KLAPISZEWSKA B., KRYSZTAFKIEWICZ A., JESIONOWSKI T., 2003, Highly dispersed green silicate and oxide pigments precipitated from model systems of postgalvanic waste, Environ. Sci. Technol., 37, 4811–4818.
• 6. KLAPISZEWSKA B., KRYSZTAFKIEWICZ A., JESIONOWSKI T., 2005, Nickel(II) silicates and oxides–highly dispersed green pigments, Pigment Resin Technol., 34, 139–147.
• 7. KRYSZTAFKIEWICZ A., RAGER B., JESIONOWSKI T., 1997, Otrzymywanie barwnych krzemianów–pigmentów o dużym stopniu rozdrobnienia, Fizykochemiczne Problemy Mineralurgii, 31, 165–173.
• 8. KRYSZTAFKIEWICZ A., MICHALSKA I., JESIONOWSKI T., BOGACKI M., 1999, Highly dispersed synthetic zinc silicates as future pigments for ecological silicate paints, Physicochemical Problems of Mineral Processing, 33, 83–92.
• 9. KRYSZTAFKIEWICZ A., MICHALSKA I., JESIONOWSKI T., WIECZOREK W., 1998, Odpady chromowe i żelazowe – potencjalne źródło do otrzymywania pigmentów, Fizykochemiczne Problemy Mineralurgii, 32, 77–85.
• 10. KRYSZTAFKIEWICZ A., KLAPISZEWSKA B., JESIONOWSKI T., 2008, Precipitated green pigments: Products of chromate postgalvanic waste utilization, Environ. Sci. Technol., 42, 7482–7488.
• 11. LEE S., YOUN J., 2008, Properties of polypropylene/layered-silicate nanocomposites and melt-spun fibers, Journal of Applied Polymer Science, 109, 1221–1231.
• 12. ROTHE B., ELAS A., MICHAELI W., 2009, In situ polymerisation of polyamide-6 nanocompounds from caprolactam and layered silicate, Macromol. Mater. Eng., 294, 54–58.
• 13. VARGHESE S., KARGER-KOCSIS J., GATOS K.G., 2003, Melt compounded epoxidized natural rubber/layered silicate nanocomposites: Structure-properties relationships, Polymer, 44, 3977–3983.
• 14. WANG Z., WANG B., QI N., ZHANG H., ZHANG L., 2005, Influence of fillers on free volume and gas barrier properties in styrene-butadiene rubber studied by positrons, Polymer, 46, 719–724.
• 15. WERNER J., Podstawy technologii malarstwa i grafiki, 1985, PWN, Warszawa
• 16. WIECZOREK M., KRYSZTAFKIEWICZ A., JESIONOWSKI T., 2003, Comparative characteristics of local and foreign bentonites, Macromolecular Symposium, 194, 345–350.
• 17. XUENING F., TIANYONG Z., CHUNLONG Z., 2000, Modification study involving a naphthol as red pigment, Dyes and Pigments, 44, 75–80.
• 18. YUAN J., ZHOU S., GU G., 2005, Encapsulation of organic pigment particles with silica via sol-gel process, Journal of Sol-Gel Science and Technology, 36, 265–274.