Dispersion properties of colloidal silica were studied at subsequent stages of silica sols preparation. Dilute sols were obtained from solutions of sodium silicate by ion exchange method. In them SiO2 particles were built up and next the sols were concentrated. The concentrations of the sols in which SiO2 particles were built-up ranged from 5.89 to 6.44 wt. % SiO2, while the mean concentrations of the sols which were added into the heel sols were 3.28 and 6.20 wt. % SiO2. The particle size distributions were measured by DLS, while the contribution of the ionic form of silica was determined by the colorimetric method on the basis of the intensity of the yellow colour coming from the heteropolycomplexes of silicomolybdic acid.

PL

W pracy badano charakterystykę dyspersyjną krzemionki koloidalnej w kolejnych etapach otrzymywania zolu kwasu krzemowego. Rozcieńczone zole otrzymywano z roztworów krzemianu sodu metodą wymiany jonowej, nabudowywano w nich cząstki SiO2 i następnie zatężano. Stężenia zoli, w których nabudowywano cząstki zawierały się w przedziale 5,89÷6,44 % wag. SiO2, a zole stosowane do nabudowania miały średnie stężenia 3,28 i 6,20 % wag. SiO2. Rozkłady wielkości cząstek mierzono techniką DLS, a udział formy jonowej krzemionki oznaczano kolorymetrycznie mierząc intensywność żółtego zabarwienia heteropolikompleksu kwasu molibdenowo–krzemowego.

Słowa kluczowe

EN

silicic acid sol; colloidal silica; sodium silicate; water solutions of silicates

PL

zol kwasu krzemowego; krzemionka koloidalna; krzemian sodu

• Wydawca: Oficyna Wydawnicza Politechniki Wrocławskiej
• Czasopismo: Physicochemical Problems of Mineral Processing
• Rocznik: 2010
• Tom: Vol. 44
• Strony: 143--150
• Opis fizyczny: Bibliogr. 8 poz.

Twórcy

autor

Malewski W.

autor

Jesionowski T.

autor

Ciesielczyk F.

autor

Krysztafkiewicz A.

• Poznan University of Technology, Institute of Chemical Technology and Engineering M. Sklodowskiej-Curie 2 Sq, 60-965 Poznan, Poland,

Bibliografia

• 1. ALEXANDER G.B., 1956, Process For Producing Sols Of 5 – 8 Milimicrons Silica Particles, And Product, U.S. Pat. 2,750,345 (Du Pont).
• 2. BIRD P.G., 1941, Colloidal Solutions Of Inorganic Oxides, U.S. Pat. 2,244,325 (National Aluminate Co.).
• 3. BECHTOLD M.F. and SNYDER O.E., 1951, Chemical Processes And Composition, U.S. Pat. 2,574,902 (Du Pont).
• 4. DIRNBERGER L.A., 1955, Process Of Preparing An Aqueous Silica Sol, U.S. Pat. 2,703,314 (Du Pont).
• 5. DIRNBERGER L.A. and NELSON R.T., 1961, Preparation Of Silica Sols Of Minimum Turbidity, U.S. Pat. 2,974,109 (Du Pont).
• 6. ILER R.K., 1979, The Chemistry of Silica, J. Wiley & Sons, New York, p. 315.
• 7. ILER R.K. and WOLTER F.J., 1953, Silica Sol Process, U.S. pat. 2,631,134 (Du Pont).
• 8. MINDICK M. and REVEN L.E., 1969, Method Of Producing Acid Silica Sols, U.S. Pat. 3,468,813 (Nalco Chemical Co.).