Shape memory properties of poly(methyl methacrylate-co--2-hydroxyethyl methacrylate)/poly(ethylene glycol) complexes

• Autorzy: Liu G. , Xie D. , Li Y. , Zhang Y. , Huang F.

Warianty tytułu

PL

Pamięć kształtu kompleksów poli(metakrylan metylu-co-metakrylan 2-hydroksyetylu)/poli(glikol etylenowy)

• Języki publikacji: EN

Abstrakty

EN

Poly(methyl methacrylate-co-2-hydroxyethyl methacrylate) [P(MMA-co-HEMA)] networks and linear poly(ethylene glycol) (PEG) can form complexes, which show shape memory properties due to a large difference in storage modulus (E') below and above its glass transition temperature (Tg). The morphology of prepared samples was analyzed using transmission electron microscopy (TEM) and X-ray diffraction (XRD) analysis. Differential scanning calorimetry (DSC) was used to investigate the thermal properties and dynamic mechanical analysis (DMA) to determine the effect of temperature on the mechanical properties. It was found that the shape recovery ratio could reach 98 %.

PL

W matrycę, którą był poli(metakrylan metylu-co-metakrylan 2-hydroksyetylu) [P(MMA-co-HEMA)] wbudowano liniowy poli(glikol etylenowy) (PEG) w ilości 10—20 % mas. Próbka tak utworzonego kompleksu, ze względu na dużą różnicę składowej rzeczywistej modułu zespolonego (E') charakteryzującej materiał w temperaturze niższej i wyższej od temperatury zeszklenia (Tg), wykazywała zdolność do zapamiętania nadanego kształtu (rys. 4). Otrzymane próbki poddano badaniom morfologicznym za pomocą transmisyjnej mikroskopii elektronowej (TEM) i dyfrakcji rentgenowskiej (XRD) (rys. 1 i 2). Użyto również różnicowej kalorymetrii skaningowej (DSC) do zbadania właściwości termicznych (rys. 3) oraz dynamicznej analizy mechanicznej (DMA) w celu określenia wpływu temperatury na właściwości mechaniczne (rys. 5). Stwierdzono, że wskaźnik odzyskiwania kształtu może osiągać 98 %.

Słowa kluczowe

EN

poly(methyl methacrylate-co-2-hydroxyethyl methacrylate); poly(ethylene glycol); glass transition temperature; shape memory properties

PL

poli(metakrylan metylu-co-metakrylan 2-hydroksyetylu); poli(glikol etylenowy); temperatura zeszklenia; pamięć kształtu

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2013
• Tom: T. 58, nr 4
• Strony: 304--307
• Opis fizyczny: Bibliogr. 19 poz.

Twórcy

autor

Liu G.

autor

Xie D.

autor

Li Y.

autor

Zhang Y.

autor

Huang F.

• Henan University of Technology, College of Material Science and Engineering, Zhengzhou, 450001, China,

Bibliografia

• 1. Lendlein A., Kelch S.: Angew. Chem. Int. Ed. 2002, 41, 2034.
• 2. Lendlein A., Langer R.: Science 2002, 296, 1673.
• 3. Samra B. K., Galaev I. Y., Mattiasson B.: Angew. Chem. Int. Ed. 2000, 39, 2364.
• 4. Hu Z., Zhang X., Li Y.: Science 1995, 269, 525.
• 5. Osada Y., Matsuda A.: Nature 1995, 376, 219.
• 6. Liu C., Qin H., Mather P. T.: J. Mater. Chem. 2007, 17, 1543.
• 7. Gunes I. S., Cao F., Jana S. C.: Polymer 2008, 49, 2223.
• 8. Yang B., Huang W. M., Li C., Li L.: Polymer 2006, 47, 1348.
• 9. Behl M., Lendlein A.: Mater. Today 2007, 10, 20.
• 10. Rousseau I. A., Mather P. T.: J. Am. Chem. Soc. 2003, 125, 15 300.
• 11. Liu C., Chun S. B., Mather P. T., Zheng L., Haley E. H., Coughlin E. B.: Macromolecules 2002, 35, 9868.
• 12. Lendlein A., Schmidt A. M., Langer R.: PNAS 2001, 98, 842.
• 13. Lee B. S., Chun B. C., Chung Y. C., Sul K. I., Cho J. W.: Macromolecules 2001, 34, 6431.
• 14. Liu C., Mather P. T.: Proceedings of the annual technical conference — society of plastics engineers, 61st, vol. 2. Brookfield, CT, USA: Society of Plastics Engineers 2003, pp. 1962—1966.
• 15. Behl M., Bellin I., Kelch S.,WagermaierW., Lendlein A.: Adv. Funct. Mater. 2009, 19, 102.
• 16. Grodzinski J. J.: Polym. Adv. Technol. 2010, 21, 27.
• 17. Tomić S. L., Micić M. M., Dobić S. N., Filipović J. M., Suljovrujić E. M.: Radiat. Phys. Chem. 2010, 79, 643.
• 18. Keller A.: J. Polym. Sci. 1959, 39, 151.
• 19. Kim B. K., Lee S. Y., Xu M.: Polymer 1996, 37, 5781.