Azot jako dodatek stopowy zwiększający odporność erozyjno-korozyjną staliwa chromowo-niklowo-molibdenowego. Cz. 2, Badania własności odlanych stopów.
Języki publikacji
Abstrakty
Laboratory tests were carried out on specimens of a Cr-Ni-Mo cast steel containing nitrogen in the range of 0.1-0.5 %. The procedure of manufacturing this alloy was described in Part I of the present study. In Part II the hardness was measurend, metallographic examinations were made, the volume fraction of ferrite delta and the ferrite/matrix phase boundary were determined, and finally the erosive-corrosion wear in the medium of chloride ions was investigated. In the alloy in as-cast condition a strong relationship between the rate of wear, chemical composition and the measured parameters of structure was observed to exist. The favourable role of nitrogen in increasing the erosion resistance of the examined cast steel was proved.
Przeprowadzono badania laboratoryjne próbek staliwa Cr-Ni-Mo z zawartością azotu w zakresie 0,1-0,5 %. Sposób uzyskania tych stopów omówiono w części 1. Obecnie dokonano pomiarów twardości, poczyniono obserwacje metalograficzne, określono objętościowy udział ferrytu delta i powierzchnię rozdziału faz ferryt/osnowa oraz przeprowadzono badania zużycia erozyjno-korozyjnego w środowisku jonów chlorkowych. Stwierdzono, że stopy w stanie lanym wykazują silną zależność tego zużycia od składu chemicznego i mierzonych parametrów struktury. Wykazano korzystną rolę azotu w zwiększeniu odporności erozyjnej badanego staliwa.
Wydawca
Czasopismo
Rocznik
Tom
Strony
89--106
Opis fizyczny
Bibliogr. 13 poz.,Fot., tab., wykr.,
Twórcy
autor
Bibliografia
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BAT2-0001-1018
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.