Leaching of nickel from spent catalysts in hydrochloric acid solutions

• Autorzy: Miazga B. , Mulak Wł.

Warianty tytułu

PL

Ługowanie niklu z zużytych katalizatorów w roztworze kwasu solnego

• Języki publikacji: EN

Abstrakty

EN

The results of hydrochloric acid leaching of nickel from spent catalysts used for methanation of small quantities of carbon oxide from hydrogen and ammonia synthesis gases (RANG-19), as well as for hydrogenation of benzene to cyclohexane (KUB-3) are reported. The effects of acid concentration, temperature, solid-to-liquid ratio and reaction time on nickel and aluminium leaching were examined. The leaching of nickel is more affected by temperature in the case of KUB-3 catalyst than RANG-19. After one hour leaching at 60 C in 3.0M HCl solution the extraction of nickel from RANG-19 catalyst amounts to 74%, whereas for KUB-3 after 45 min of leaching extraction of nickel is 99%. The highest leaching efficiency of nickel from both the catalysts are found to be: 3.0M HCl solution, tem perature 60C, solid to liquid ratio of 1/10, particle size 3-8 mm. In these conditions 99% of nickel is extracted from KUB-3 catalyst after 3 hours of leaching, and 98% of nickel from RANG-19 after 4 hours of leaching, respectively.

PL

Przedstawiono wyniki ługowania niklu z dwóch zużytych katalizatorów: katalizatora metalizacji (RANG-19) oraz katalizatora uwodornienia benzenu (KUB-3), stosując roztwory kwasu solnego. Określono wpływ stężenia HCl, temperatury, stosunku fazy stałej do ciekłej oraz intensywności mieszania na wydajność ługowania niklu. Wykazano, że temperatura znacznie bardziej wpływa na szybkość ługowania niklu z katalizatora KUB-3 aniżeli z RANG-19. Po 1 godzinie ługowania w temperaturze 60C w 3.0M HCl ekstrakcja niklu z katalizatora RANG-19 wynosi 74%, podczas gdy z katalizatora KUB-3 po 45 min wyługowania niklu wynosi 99%. Najwyższą wydajność ługowania niklu z obu katalizatorów bez dodatkowego rozdrobnienia (granulki 3-8 mm) uzyskano w 3.0M roztworze HCl, w temperaturze 60C przy stosunku fazy stałej do ciekłej 1/10. W powyższych warunkach ekstrakcja niklu z katalizatora KUB-3 wynosi 99% po 3 godzinach ługowania, natomiast 98% niklu wyługowano z katalizatora RANG-19 po 4 godzinach ługowania.

Słowa kluczowe

EN

spent catalyst; nickel; leaching; hydrochloric acid

PL

zużyty katalizator; nikiel; ługowanie; kwas solny

• Wydawca: Oficyna Wydawnicza Politechniki Wrocławskiej
• Czasopismo: Physicochemical Problems of Mineral Processing
• Rocznik: 2008
• Tom: Vol. 42
• Strony: 179--186
• Opis fizyczny: Bibliogr. 9 poz.

Twórcy

autor

Miazga B.

autor

Mulak Wł.

• University of Wroclaw, Institute of Archeology, Koszarowa 3, 51-149 Wrocław, Poland

Bibliografia

• AL-MANSI N.M., ABDEL MONEM N.M., 2002, Recovery of nickel oxide from spent catalyst. Waste Management 22, 85-90.
• CHAUDHARY A.J., DONALDSON J.D., BODDINGTON S.C., GRIMES S.M., 1993, Heavy metals in environment. Part II: a hydrochloric acid leaching process for the recovery of nickel value from a spent catalyst. Hydrometallurgy 34, 137-150.
• FURIMSKY E., 1996, Spent refinery catalysts: environment, safety and utilization. Catalysis Today 30, 223-286.
• IVASCAN S., ROMAN O., 1975. Nickel recovery from spent catalyst. Bul. Inst. Politeh. Iasi, Sect. 2, 21,47-51
• KOLOSNITSYN V.S., KOSTERNOVA S.P., YAPRYNTSEVA O.A., IVASHCHENKO A.A., ALEKSEEV S.V., 2006, Recovery of nickel with sulfuric amid solutions from spent catalysts for steram conversion of methane. Russian Journal of Applied Chemistry, 79, 539-543.
• MULAK W., MIAZGA B., SZYMCZYCHA A., 2005, Kinetics of nickel leaching from spent catalyst in sylphuric amid solution. Int.J.Miner.Process., 77, 131-235.
• MULAK W., MIAZGA B., SZYMCZYCHA A., 2005, Hydrometalurgiczny odzysk niklu z materiałów odpadowych. Rudy Met. Nieżelaz. 50, 114-119.
• THOMAS C.L.; 1970, Catalytic Process and Proven catalysts. Academic Press, New York and London.
• SUŁEK B., SZYMCZYCHA A., MULAK W., 2004, Sulphuric acid leaching of nickel from a spent catalysts. Proceedings of Global Symposium on Recycling, Waste Managment and Clean Technology, Madryt, 2081&2090.