Ocena możliwości rozszerzenia zakresu stosowania blach wysokowytrzymałych ulepszanych cieplnie o granicy plastyczności min. 890 MPa i analiza zapotrzebowania na blachy walcowane i bezpośrednio chłodzone z zastosowaniem technologii MULPIC

• Autorzy: Gawor J. , Woźniak D. , Garbarz B. , Ujma J.

Warianty tytułu

EN

Evaluation of opportunities for extending the range of use of high-strength quenched and tempered steel plates with yield strength of min 890 MPa and analysis of demand for plates rolled and directly cooled using "MULPIC" technology

• Języki publikacji: PL

Abstrakty

PL

Celem pracy było wskazanie możliwości rozszerzenia zakresu stosowania blach wysokowytrzymałych w polskim przemy śle przetwórczym i przeprowadzenie analizy rynku blach walcowanych termomechanicznie dla potrzeb opracowania programu aplikacyjnego uruchomienia produkcji blach z zastosowaniem regulowanego chłodzenia bezpośrednio po walcowaniu w systemie MULPIC (Multi-Purpose Interrupted Cooling). Wykonano analizę produkcji przedsiębiorstw wykorzystujących wysokowytrzymałe blachy grube ulepszane cieplnie i walcowane termomechanicznie oraz analizę możliwości zastosowania blach o granicy plastyczności powyżej 890 MPa w miejsce blach o granicy plastyczności 690MP. Analiza rynku blach wysokowytrzymałych w Polsce wykazała, że większość tych blach zużywanych w krajowym przemyśle maszyn i urządzeń pochodzi z importu. Przyczyną tego jest sytuacja polskich producentów będących jedynie poddostawcami elementów urządzeń dla wyrobów finalnych produkowanych przez firmy zagraniczne, które wymagają dodatkowych własnych certyfikatów jakości blach i dopuszczeń oraz wpisów na listę uznanych dostawców.

EN

The objective of the work was to show possibilities for extending the range of use of high-strength steel plates in the Polish processing industry and carrying out the analysis of the market for thermomechanically rolled plates for the needs of development of the research programme to start up the production of steel plates with use of controlled cooling directly after rolling in the MULPIC (Multi -Purpose Interrupted Cooling) system. .The analysis of production programme of the enterprises using high-strength quenched and tempered and thermomechanically rolled steel plates and the analysis of opportunities for using steel plates with yield strength of above 890 MPa rather than those with yield strength of690 MPa were carried out. The analysis of the market for high-strength plates in Poland showed that most of the plates used in the domestic machine-building industry were imported. The reason for that is the situation of Polish manufacturers who are only the sub-suppliers of the equipment components for final products manufactured by foreign companies that require the additional own quality certificates for steel plates as well as permits and entries into the list of recognised suppliers.

Słowa kluczowe

PL

blacha wysokowytrzymała; obróbka cieplna; blacha walcowana; technologia MULPIC

EN

steel plates; rolled plates; MULPIC technology

• Wydawca: Instytut Metalurgii Żelaza im. Stanisława Staszica
• Czasopismo: Prace Instytutu Metalurgii Żelaza
• Rocznik: 2008
• Tom: T. 60, nr 3
• Strony: 50--53
• Opis fizyczny: Bibliogr. 3 poz.

Twórcy

autor

Gawor J.

autor

Woźniak D.

autor

Garbarz B.

autor

Ujma J.

• Instytut Metalurgii Żelaza

Bibliografia

• 1. Ujma J.: Sprawozdanie ISD Huta Częstochowa z pracy wykonanej w ramach projektu celowego nr 6 ZR7 2005 C/o6636, zadanie 15, październik 2006.
• 2. Sprawozdanie Instytutu Spawalnictwa w Gliwicach Nr :IK/28/2007 dot. kwalifikacji technologii spawania wg DIN EN-ISO 15614-1 (rodzaj złącza i spoiny: BW).
• 3. Sprawozdanie Instytutu Spawalnictwa w Gliwicach Nr: IK/29/2007 dot. kwalifikacji technologii spawania wg DIN EN-ISO 15614-1 (rodzaj złącza i spoiny: FW).