Deposit attack in tubes of power plant steam boilers

• Autorzy: Balitskii A. , Ripey I. , Chmiel J.

Warianty tytułu

PL

Zniszczenia podosadowe rur energetycznych kotłów parowych

• Języki publikacji: EN

Abstrakty

EN

This article presents the results of the inspection of damaged tubes of steam boilers, the damage being a result of deposit attack. Changes in the chemical composition of feedwater, i.e. its hardness increased due to leaks in brass tubes of the turbine condenser, result in the formation of scale on the tube material, followed by corrosion, overheating and numerous defects. Only during one of the necessary stops, damage of varying degree to over 20 tubes was detected, from a pit (or crack initiation) to fractures of a few tubes. The results of visual inspection and mechanical and metallographic tests of the damaged tubes are given.

PL

W pracy przedstawiono wyniki badań uszkodzeń rur kotłów parowych, interpretowanych jako wynik procesów korozji podosadowej. Jako główne przyczyny uszkodzeń wskazuje się obecność w wodzie kotłowej związków żelaza (III) oraz związków miedzi (pochodzących z układu skraplacza turbiny), których osady stanowią obszary katodowe, stymulujące rozwój wżerów stanowiących anody. Przedstawiono wyniki inspekcji wizualnej rur, badań właściwości mechanicznych, badań mikrostruktury oraz analiz chemicznych.

Słowa kluczowe

EN

steam boiler; tubes; deposit attack; overheating; structure

PL

kocioł parowy; rura; korozja podosadowa; przegrzanie; mikrostruktura

• Wydawca: Wydawnictwo Naukowe Instytutu Technologii Eksploatacji - Państwowego Instytutu Badawczego
• Czasopismo: Problemy Eksploatacji
• Rocznik: 2010
• Tom: nr 4
• Strony: 79--89
• Opis fizyczny: Bibliogr. 8 poz., rys., tab.

Twórcy

autor

Balitskii A.

autor

Ripey I.

autor

Chmiel J.

• West-Pomeranian University of Technology, Szczecin, Poland

Bibliografia

• 1. Foulds J., Viswanathan R. Small Punch Testing for Determining the Material Toughness of Low Alloy Steel Components in Service. // Journal of Engineering Materials and Technology. - 1994 - Vol. 116, N 4, October - P. 457-464.
• 2. Viswanathan R. Damage Mechanisms and Life Assessment of High-Temperature Components, ASM International, Metal Park. Ohio 44073. - 1989. - 497 p.
• 3. Khajavi M.R., Abdolmalki A.R., Adibi N., Mirfendereski S. Failure analysis of bank front boiler tubes // Engineering Failure Analysis. - 14 (2007) - P. 731-738.
• 4. Ray A.K., Sahay S.K., Goswami B. Assesment of service exposed boiler tubes // Engineering Failure Analysis. - 10 (2003) - P. 645-654.
• 5. Baoyou Zhang, Zhonghong Lai, Yuexian Cui, Xigang Fan Analysis of a boiler pipe rupture // Engineering Failure Analysis. - 13 (2006) - P. 75-79.
• 6. Khalil Ranjbar Failure analysis of boiler cold and hot reheater tubes // Engineering Failure Analysis. - 16 (2005) - P. 621-625.
• 7. Fracture mechanics and strength of materials: Reference book, Editor-in-chief V.V. Panasyuk. V. 8. Strength of materials and durability of structural elements of nuclear power plants, A.I.Balitskii, O.V. Makhnenko, O.A. Balitskii, V.A. Grabovskii, D.M. Zaverbnyi, B.T. Timofeev. Editor A.I. Balitskii - Kyiv: PH ”Akademperiodyka”, 2005. - 544 p., ISBN 966-360-035-7.
• 8. Ripey I.V.: The influence of hardening of 12Cr18Ni12Ti steel on the mechanical-technological properties and susceptibility of tubes to intergranular corrosion // Proc. of 20th Conf. of Young Scientists of PhMI NAS of Ukraine, Lviv, 2007. - P. 33-37.