Method of evaluation of degradation of bio-mechanical tooth-composite filling system

• Autorzy: Niewczas A. , Pieniak D. , Niewczas A. M.

Warianty tytułu

PL

Metoda oceny degradacji systemu biomechanicznego ząb - wypełnienie kompozytowe

• Języki publikacji: EN

Abstrakty

EN

This paper describes a method of an enhanced life evaluation of dental fillings based on the observation of the enlargement of the marginal fissure between the filling and hard tissue of the tooth. A width of marginal fissure was considered as the functional parameter of the whole tooth-filling system in the conducted tests. In this study development of the fissure influenced by the cyclic changes of thermal loads was analyzed. The extracted human teeth were used in the tests. In which a model lesions with microhybrid composite fillings were applied. All tests were conducted on the dedicated test stand. After performance of fatigue tests, measurements of the width of marginal fissure were taken by means of SEM electron scanning microscope and optical microscope with computer image analyzer. On this basis a risk of functional unfitness of the tooth-filling system was estimated.

PL

W artykule opisano metodę przyspieszonej oceny trwałości wypełnień stomatologicznych na podstawie obserwacji rozbudowy szczeliny brzeżnej pomiędzy wypełnieniem a twardą tkanką zęba. W warunkach prowadzonych badań jako miarę zdatności czynnościowej całego systemu ząb - wypełnienie przyjęto szerokość szczeliny brzeżnej. Autorzy przeprowadzili analizę rozwoju szczeliny pod wpływem cyklicznie zmiennych obciążeń cieplnych. Do badań wykorzystano usunięte zęby ludzkie. W zębach wypreparowano modelowe ubytki i założono wypełnienia z kompozytu mikrohybrydowego. Badania zostały przeprowadzone na specjalnie opracowanym stanowisku badawczym. Po wykonaniu testów zmęczeniowych przeprowadzano pomiary szerokości badanej szczeliny brzeżnej, wykorzystując elektronowy mikroskop skaningowy SEM. Na tej podstawie oszacowano ryzyko niezdatności użytkowej układu ząb - wypełnienie.

Słowa kluczowe

EN

reliability; laboratory testing; dental composite

PL

niezawodność; test laboratoryjny; kompozyt stomatologiczny

• Wydawca: Polskie Towarzystwo Diagnostyki Technicznej
• Czasopismo: Diagnostyka
• Rocznik: 2010
• Tom: nr 2(54)
• Strony: 51--58
• Opis fizyczny: Bibliogr. 21 poz., rys., tab.

Twórcy

autor

Niewczas A.

autor

Pieniak D.

autor

Niewczas A. M.

• Technical University of Lublin, Department of Combustion Engines and Transport, Lublin 20-608, Nadbystrzycka Str. No 36,

Bibliografia

• [1] Achilias D.S., Karabela M.M., Sideridou I.D. Thermal degradation of light-cured dimethacrylate resins Part I. Isoconversional kinetic analysis. Thermochemica Acta (2008) 472, p.74-83.
• [2] Braga R.R., Boaro L.C.C., Kuroe T., Azevedo C.L.N., Singer J.M. Influence of cavity dimensions and their derivatives (volume and ‘C’ factor) on shrinkage stress development and microleakage of composite restorations. Dental Materials (2006) 22, p.818-823.
• [3] Calheiros C.F., Sadek F.T., Boaro L.C.C., Braga R.R. Polymerization stress related to radiant exposure and its effect on microleakage of composite restorations. Journal of Dentistry (2007) 35, p.946-952.
• [4] Chan K.C, Swift E.J. Marginal seal of new generation dental bonding agents. Journal of Prosthet. Dent. (1994) 72, p.420-423.
• [5] Fleming G.J.P., Hall D.P., Shortall A.C.C., Burke F.J.T. Cuspal movement and microleakage in premolar teeth restored with posterior filling materials of varying reported volumetric shrinkage values. Journal of Dentistry (2005) 33, p.139-146.
• [6] Geis-Gerstorfer J. In vitro corrosion measurements of dental alloys. Journal of Dentistry (1994) 22, p.247-51.
• [7] Gale M.S., Darvell B.W. Thermal cycling procedures for laboratory testing of dental restorations. Journal of Dentistry 27 (1999), p.89-99.
• [8] Hunicz J, Niewczas A, Kordos P, Pieniak D. Experimental test stand for analysis of composite dental fillings degradation. Eksploatacja i Niezawodnosc - Maintenance and Realiability (2007) 2, p.37 - 43.
• [9] Joyston-Bechal A., Kidd E., Joyston-Bechal S. Essentials of dental caries: the disease and its management. 2nd ed. Oxford: Oxford University Press (1998), p. 66-78.
• [10] Kendall M. G., Buckland W. R. Słownik terminów statystycznych, wyd. PWN, Warszawa (1986).
• [11] Migdalski J (red.). Inżynieria niezawodności. Poradnik. Wyd. ATR and ZETOM, Warszawa (1992).
• [12] Neimitz A. Mechanika pękania, wyd. PWN, Warszawa (1999).
• [13] Walczak M., Niewczas A., Hunicz J. Propagacja szczeliny brzeżnej w kompozytach stomatologicznych - próba laboratoryjnej symulacji cyklu żucia. Przegląd Mechaniczny (2007) 5, p. 149-151.
• [14] Piemjai M., Watanabe A., Iwasaki Y., Nakabayashi N. Effect of remaining demineralised dentine on dental microleakage accessed by a dye penetration: how to inhibit microleakage?. Journal of Dentistry (2004) 32, p.495-501.
• [15] Qingshan L., Jepsen S., Albers H.K., Eberharda J. Flowable materials as an intermediate layer could improve the marginal and internal adaptation of composite restorations in Class-V-cavities. Dental Materials (2006) 22, p.250-257.
• [16] Rosin M., Urban A.D., Gartner C., Bernhardt O., Spleith C., Meyer G. Polymerization shrinkage-strain and microleakage in dentin - border cavites of chemical and light-cured restorative materials, Dental Materials (2002) 18, p.521-528.
• [17] Szenowski H., Kupka T., Twardawa H., Skaba D. Analiza szczelności brzeżnej materiałów do wypełnień stałych zewnętrznych. Stomatologia Zachowawcza (1997) 2, p.15 - 19.
• [18] Volk W. Statystyka stosowana dla inżynierów wyd. WNT, Warszawa (1973).
• [19] Sanders-Tavares da Cunha Mello F., Feilzer A.J., de Gee A.J., Davidson C.L. Sealing ability of eight resin bonding systems in a Class II restoration after mechanical fatiguing. Dental Materials (1997) 13, p.372-376.
• [20] Wilder Jr. A.D., Swift Jr. E.J., May Jr. K.N., Thompsona J.Y., McDougal R.A. Effect of finishing technique on the microleakage and surface texture of resin-modified glass ionomer restorative materials. Journal of Dentistry (2000) 28, p.367-373.
• [21] Yoshida K., Matsumura H., Atsuta M. Monomer composition and bond strength of light-cured 4-META opaque resin. Journal of Dental Restoration (1990) 69, p.849-851.