The role of metallurgical defects and microstructure on failure formation in roll necks of cast iron rolls

• Autorzy: Krawczyk J. , Pacyna J.

Warianty tytułu

PL

Rola wad metalurgicznych oraz mikrostruktury w powstawaniu uszkodzeń czopów żeliwnych walców hutniczych

• Języki publikacji: EN

Abstrakty

EN

This work presents the examples of structural reasons for failure of the necks of cast iron rolls. The most common reason for damage of metallurgical roll necks is a presence of shrinkage porosity in their volume. Moreover, a high fraction of ledeburitic cementite can lead to the formation of a continuous net of eutectic carbides, which facilitate cracking. Even very thin net of secondary carbides, formed on the boundaries of former grain of austenite, can significantly facilitate propagation of the crack. Continuous net of ledeburitic cementite, in the case of its precipitation in a form of bands and existence of hardened areas in the alloy matrix can lead to roll neck fracture relatively easy. The use of flake graphite cast iron for metallurgical rolls increases a risk of the fracture of roll neck.

PL

W niniejszej pracy przedstawiono przykłady strukturalnych przyczyn uszkodzeń czopów w żeliwnych walcach hutniczych. Najczęstszą przyczyną uszkodzeń czopów walców hutniczych jest zaleganie w nich obszarów rzadzizn. Ponadto duży udział cementytu ledeburytycznego może prowadzić do powstania ciągłej siatki węglików eutektycznych, która tworzy drogę łatwego pękania. Nawet bardzo cienka siatka węglików drugorzędowych utworzona na granicach pierwotnego ziarna austenitu może w znaczący sposób ułatwiać rozwój pęknięcia. Ciągła siatka cementytu ledeburytycznego, w przypadku jego wydzielania w postaci pasmowej oraz występowanie w osnowie obszarów podhartowanych, może doprowadzić do łatwego złamania czopa walca. Zastosowanie na walce hutnicze żeliwa z grafitem płatkowym zwiększa niebezpieczeństwo złamania czopa.

Słowa kluczowe

EN

cast iron; mill rolls; shrinkage porosity; ledeburite; secondary cementite; graphite

PL

żeliwo; walce hutnicze; rzadzizna; ledeburyt; cementyt drugorzędowy; grafit

• Wydawca: AGH University of Science and Technology Press
• Czasopismo: Metallurgy and Foundry Engineering
• Rocznik: 2007
• Tom: Vol. 33, no. 2
• Strony: 89--96
• Opis fizyczny: Bibliogr. 5 poz., rys., tab.

Twórcy

autor

Krawczyk J.

• Faculty of Metals Engineering and Industrial Computer Science, AGH University of Science and Technology, Cracow, Poland

autor

Pacyna J.

• Faculty of Metals Engineering and Industrial Computer Science, AGH University of Science and Technology, Cracow, Poland

Bibliografia

• [1] Pacyna J. Wybrane problemy materiałowe i eksploatacyjne walców hutniczych. III Konferencja Naukowa: Walcownictwo 2005: Procesy-Narzędzia-Materiały, Ed. Andrzej Nowakowski, Ustroń, 19—21 październik 2005, 49-60
• [2] Pacyna J., Krawczyk J., Zając G: Nowa technologia obróbki cieplnej żeliwa sferoidalnego chromowo -niklowego. IX Konferencja Naukowo-Techniczna, 120 lat Huty Buczek S.A. „Kierunki rozwoju produkcji walców" Wisła - Malinka 13-15. III 2002, 9-17
• [3] Krawczyk J., Pacyna J., Kokoszą A.: Fracture toughness of cast materials for mili rolls. Proceedings of the 6 International Conference for Mesomechanics, Multiscaling in Applied Science and Emerging Technology, Fundamentals and Applications in Mesomechanics, 31 May — 4 June, 2004, Patras, Greece, p. 203—207
• [4] Głownia J. Rola segregacji w procesie pękania walców staliwnych. Zeszyty Naukowe AGH nr 1163, Metalurgia i Odlewnictwo, z. 111, 1987, 215-223
• [5] Guzik E. Procesy uszlachetniania żeliwa, wybrane zagadnienia. Archiwum Odlewnictwa, Monografia nr IM, 2001