Charakterystyka mikrostrukturalna i cieplna układu TeO2 – WO3
Języki publikacji
Abstrakty
In the present study, thermal behaviour and microstructure of the TeO2–WO3 system have been investigated. Different compositions of (1-x)TeO2 – xWO3 system (x = 0.02, 0.05, 0.15, 0.25 and 0.40 in molar ratio) were prepared. The samples waited at 750°C in a platinum crucible for 30 min and then quenched in a water bath. DTA studies were performed on glassy samples. Afterwards, all samples were heat-treated at 550°C for 24 h and furnace cooled to obtain phase equilibrium. XRD and SEM/EDS studies were performed on the crystallized samples for microstructural analysis.
W prezentowanej pracy zbadano zachowanie cieplne i mikrostrukturę tworzyw w układzie TeO2-WO3. Przygotowano różne składy układu (1-x)TeO2 – xWO3, gdzie x = 0.02, 0.05, 0.15, 0.25 i 0.40 w stosunku molowym. Próbki przebywały w 750°C w tyglu platynowym przez 30 min a potem szybko chłodziły się w wodzie. Badania DTA przeprowadzono na próbkach szklistych. Następnie, wszystkie próbki zostały wygrzane w . 550°C przez 24 h i schłodzone z piecem w celu osiągnięcia równowagi fazowej. Badania XRD i SEM/EDS przeprowadzono na krystalizowanych próbkach w przypadku analizy mikrostrukturalnej.
Wydawca
Czasopismo
Rocznik
Tom
Strony
556--559
Opis fizyczny
Bibliogr. 7 poz., rys., wykr.
Twórcy
autor
autor
autor
autor
autor
autor
- Istanbul Technical University, Department of Metallurgical and Materials Engineering, Istanbul, 34469, Turkey, miraycelikbilek@gmail.com
Bibliografia
- [1] El-Mallawany R. H.: Tellurite Glasses Handbook: Physical Properties and Data, (2002), CRC Press LLC.
- [2] Öveçoğlu M.L., Kabalcı I., Özen G., Öz B.: „Microstructural characterization of (1−x)TeO2 – xPbF2 (x = 0.10, and 0.25 mol) glasses”, J. Eur. Ceram. Soc., 27, (2006), 1801.
- [3] Blanchandin, S., Marchet, P., Thomas, P., Champarnaud-Mesjard, J.C., Frit, B., Chagraoui, A.: „New investigations within the TeO2–WO3 system: phase equilibrium diagram and glass crystallization”, J. Mater. Sci., 34, (1999), 4285.
- [4] Öveçoğlu M.L., Özen G., Cenk S.: „Microstructural characterization and crystallization behaviour of (1−x)TeO2 – xWO3 (x = 0.15, 0.25, 0.3 mol) glasses”, J. Eur. Ceram. Soc.,26, (2005), 1149.
- [5] Kosuge, T., Benino, Y., Dimitrov, V., Sato, R., Komatsu, T.: „Thermal Stability and Heat Capacity Changes at the Glass Transition in K2O–WO3–TeO2 Glasses”, J Non-Cryst. Solids, 242, (1998), 154.
- [6] Shaltout, I., Tang, Y.I., Braunstein, R., Abu-Elazm, A.M.: „Structural Studies of Tungstate – Tellurite Glasses by Raman Spectroscopy and Differential Scanning Calorimetry”, J. Phys. Chem. Solids, 56, (1994), 141.
- [7] Eds. By Vlasov A.G., Florinskaya V.A.: „Structure and Physicalo-Chemical Properties of Inorganic Glasses”, Khimiya, Leningrad, 1974, quoted by Safonov V.V.: „Interactions in the TeO2-TiO2-WO3 System”, Russion Journal of Inorganic Chemistry, 53, (2008), 460.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-AGH1-0025-0140