Cerium doped yttrium aluminium garnet modified by silicon and nitrogen

• Autorzy: Michalik D. , Plewa J. , Sopicka-Lizer M. , Justel T.

Warianty tytułu

PL

Granat itrowo-glinowy domieszkowany cerem i modyfikowany krzemem oraz azotem

• Języki publikacji: EN

Abstrakty

EN

Compound according to the general composition Y3Al(5-x)SixO(12-x)Nx, which are formally derived from the yttrium aluminium garnet Y3AI5O12 (YAG) due to the substitution of oxygen by nitrogen, are of high interest for material research and application. The required charge compensation due to the replacement of oxygen by nitrogen is achieved by the appropriate substitution of aluminum by silicon. This paper deals with the solid state synthesis and optical properties of Y3Al(5-x)SixO(12-x)Nx, samples doped by trivalent cerium and more specifically with the effect of the O/N and Al/Si ratio on the optical properties. It turned out that the incorporation of Si and N yields a red shift of the 5d-4f emission band of Ce(3+), whereby the extent of the red shift can be correlated to the composition of the host lattice.

PL

Interesującym materiałem na luminofory jest związek Y3Al(5-x)SixO(12-x)Nx, który stanowi pochodną granatu YAG z podstawieniem azotu w miejsce tlenu. Dla niezbędnego skompensowania ładunku spowodowanego tym podstawieniem zastąpiono krzemem część atomów glinu. W artykule opisany został sposób syntezy związków Y3Al(5-x)SixO(12-x)Nx , z trójwartościowym cerem jako aktywator oraz wpływ podstawień O/N i Al/Si na własności optyczne. W wyniku takiego podstawienia występuje przesunięcie emisji promieniowania w stronę większej wartości długości fali.

Słowa kluczowe

EN

YAG; optical properties; luminescence

PL

YAG; właściwości optyczne; luminescencja

• Wydawca: Polskie Towarzystwo Ceramiczne
• Czasopismo: Materiały Ceramiczne
• Rocznik: 2008
• Tom: T. 60, nr 4
• Strony: 225--228
• Opis fizyczny: Bibliogr. 10 poz., rys., wykr.

Twórcy

autor

Michalik D.

autor

Plewa J.

autor

Sopicka-Lizer M.

autor

Justel T.

• University of Applied Science Muenster, Germany; Silesian University of Technology, Katowice,

Bibliografia

• [1] Mares J.A., Nikł M., Beitlerowa A., Solovieva N., D'Ambrosio C, Blazek K., Mały R, Nejezchleb K., Fabeni R, Pazzi G.P.: Nuclear Instruments and Methods in Physics Research A, 537 (2005)271-275.
• [2] Dong Y, Zhou G„ Xu J., Zhao G., Su F., Su F., Su L., Zhang G., Zhang D., Li H., Si J.: Materials Research Bulletin, 41 (2006) 1959-1963.
• [3] Yang Z., Li X., Yang Y, Li X.: Journal of Luminescence, 122-123 (2007) 707-709.
• [4] Edited by Ronda C; Juestel T. chapter; Luminescence form theory to applications; Wiley-vch 2008.
• [5] Sopicka-Lizer M., Piekarczyk J.: Key Engineering Materials, 206-213(2001)429-432.
• [6] Xie R.-J., Hirosaki N., Mimoto M., Yamamoto Y, Suehiro T.: J. Phys. Chem. B, 108 (2004) 12027-12031 Barrg R.; Glass, 68 (1991) 32-35.
• [7] Krevel W.H.: J. Solid State Chem., 165 (2002) 19-24.
• [8] Dong Y, Zhou G., Xu J., Zhao G., Su F., Su L., Li H., Si J.,Qian X., Li X., Shen J.: Journal of Crystal Growth, 286 (2006) 476-480.
• [9] Li J.G., Ikegami T., Lee J.H., Mori T.: J. Am. Ceram. Soc, 83 [4] 961-63 (2000).
• [10] Sopicka-Lizer M.: SIALON ceramics from carbothermally derived powder - psychical chemistry of manufacturing and properties; WPS, 2000.