Gelcasting of alumina with application of new monomer synthesised from xylitol

• Autorzy: Szudarska A. , Guryniuk D. , Mizerski T. , Szafran M.

Identyfikatory

DOI

10.2478/amm-2013-0162

Warianty tytułu

PL

Odlewanie żelowe tlenku glinu z zastosowaniem nowego monomeru zsyntezowanego z ksylitolu

• Konferencja: Composites and Ceramic Materials - Technology, Application and Testing (13 ; 13-15.05.2013 ; Białowieża, Poland)
• Języki publikacji: EN

Abstrakty

EN

A new monomer for application in the gelcasting process has been designed and synthesized, following the green chemistry trend to use non toxic and renewable compounds. Xylitol was the main substrate for the synthesis that included 3 stages. The final product, named 1-O-acryloylxylitol, was tested regarding its effectiveness as the processing agent for fabrication of alumina elements by gelcasting method. Rheological properties of the ceramic slurries were studied as well as the properties of shaped elements before and after sintering. The results are compared to those obtained by applying commercial monomer 2-hydroxyethyl acrylate.

PL

Podążając za trendem „zielonej chemii", zakładającym m.in. wykorzystywanie nietoksycznych i odnawialnych surowców w technologii, zaprojektowano i zsyntezowano nowy monomer przeznaczony do zastosowania w procesie odlewania żelowego. Wyjściowym substratem trójetapowej syntezy był ksylitol, a finalnym produktem 1-O-akryloiloksylitol. Otrzymana pochodna została sprawdzona pod względem efektywności polimeryzacji in situ w ceramicznej masie lejnej na bazie tlenku glinu. Zbadano jej wpływ na właściwości neologiczne stosowanych zawiesin. Odlano serie kształtek, dla których wyznaczono podstawowe parametry w stanie surowym oraz po spiekaniu. Wyniki porównano stosując równolegle komercyjnie dostępny monomer akrylan 2-hydroksyetylu.

Słowa kluczowe

EN

alumina; gelcasting; low-toxic monomers; xylitol

PL

tlenek glinu; odlewanie żelowe; monomery nietoksyczne; ksylitol

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2013
• Tom: Vol. 58, iss. 4
• Strony: 1299--1303
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Szudarska A.

• Warsaw University of Technology, Faculty of Chemistry, 3 Noakowskiego Str., 00-664 Warszawa, Poland

autor

Guryniuk D.

• Warsaw University of Technology, Faculty of Chemistry, 3 Noakowskiego Str., 00-664 Warszawa, Poland

autor

Mizerski T.

• Warsaw University of Technology, Faculty of Chemistry, 3 Noakowskiego Str., 00-664 Warszawa, Poland

autor

Szafran M.

• Warsaw University of Technology, Faculty of Chemistry, 3 Noakowskiego Str., 00-664 Warszawa, Poland

Bibliografia

• [1] O. O. Omatete, M. A. Janney, S. D. Nunn, J. Eur. Ceram. Soc.17, 407 (1997).
• [2] A. C. Young, O. O. Omatete, M. A. Janney, P. A. Menchhofer, J. Am. Ceram. Soc. 74, 612 (1991).
• [3] J. Yang, J. Yu, Y. Huang, J. Eur. Ceram. Soc. 31, 2569 (2011).
• [4] P. Bednarek, Y. Sakka, M. Szafran, T. Mizerski, J. Eur. Ceram. Soc. 30, 1795 (2010).
• [5] P. Falkowski, P. Bednarek, A. Danelska, T. Mizerski, M. Szafran, J. Eur. Ceram. Soc. 30, 2805 (2010).
• [6] M. Szafran, P. Bednarek, A. Szudarska, Advances in Science and Technology 62, 163 (2010).
• [7] A. Szudarska, T. Mizerski, M. Szafran, Archives of Metallurgy and Materials 56, 1211 (2011).
• [8] C. Tallon, D. Jach, R. Moreno, M. I. Nieto, G. Rokicki, M. Szafran, J. Am. Ceram. Soc. 90, 1386 (2007).
• [9] J. R. Capua Proveti, G. Michot, Int J Fract. 139, 455 (2006).