Application of technical diagnostic parameters for evaluation of serviceabilty forcible power plants high temperature pipelines

• Autorzy: Balitskii A. , Ripey I. , Garda V. , Eliasz J.

Identyfikatory

DOI

10.26357/BNiD.2017.024

Warianty tytułu

PL

Zastosowanie parametrów diagnostyki technicznej do oceny zdolności do pracy wysoko-temperaturowych rurociągów elektrowni cieplnych

• Języki publikacji: EN

Abstrakty

EN

Technical diagnostic parameters that are used to assess operability of high temperature pipelines thermal power plants has concidered. It was found the sensitivity of these parameters to assess the metal degradation in the steam during a long operation. It has been propose the approaches to assess the residual life of steam pipelines, taking into account parameters that are structurally vulnerable to degradation of metal.

PL

Analizie poddano parametry diagnostyki technicznej stosowane w ocenie zdolności do pracy wysokotemperaturowych rurociągów elektrowni cieplnych. Określono przydatność tych parametrów do oceny stanu degradacji metali stosowanych w wysokotemperaturowych rurociągach, w warunkach długotrwałego, eksploatacyjnego oddziaływania pary wysokotemperaturowej. Zaproponowano sposób oceny tzw. resztkowego czasu eksploatacji parociągów, oparty o parametry diagnostyki technicznej pozwalające na określenie tzw. strukturalnej podatności na uszkodzenia, prowadzące do degradacji metalu wskutek oddziaływania wysokotemperaturowej pary technologicznej.

Słowa kluczowe

EN

reliability; technical diagnosis; pipeline; structure; damage; serviсeability

PL

niezawodność; diagnostyka techniczna; rurociąg; struktura; zniszczenie materiału; zdolność do eksploatacji

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Badania Nieniszczące i Diagnostyka
• Rocznik: 2017
• Tom: nr 1-2
• Strony: 39--42
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Balitskii A.

• Karpenko Physicomechanical Institute, Ukrainian National Academy of Science, Lviv, Ukraine

autor

Ripey I.

• Halremenergo PJSC "DTEK Zakhidenergo'', Lviv, Ukraine

autor

Garda V.

• Halremenergo PJSC "DTEK Zakhidenergo'', Lviv, Ukraine

autor

Eliasz J.

• West Pomeranian University of Technology, Szczecin, Poland

Bibliografia

• [1] Praul R. Dongre, Vibhav B. Rakhunde. Residual life assessment in high temperature zones of power plant components // Int. J. of Mechanical and Production Engineering, Vol. 1, Issue- 2, Aug-2013. – P. 43–49.
• [2] Jirı Janovec, Daniela Polachova, Michal Junek Lifetime Assessment of a Steam Pipeline // Acta Polytechnica. – Vol. 52. – No. 4/2012.– P. 74–79.
• [3] A. Zieliński, J. Dobrzański, T. Joźwik Assessment of loss in life time of the primary steam pipeline material after longterm service under creep conditions // J. of Achievements in Materials and Manufacturing Engineering. – V. 54. – Issue, 1. – September, 2012. – P. 67–74.
• [4] Balyts’kyi O.I., Ripey I.V., Protsakh Kh.A. Reliability of steam pipelines of thermal power plants in the course of long-term operation // Materials Science (Springer).– 2006, No 4, vol.42.- P. 421–424.
• [5] Balyts’kyi O.I., Ripey I.V., Onyshak Ja.D. Variations of impact toughness of 12Kh1MF steel in operating steam pipelines of thermal power plants // Materials Science (Springer).– 2009, vol. 45, N 6. p.826-830.
• [6] Ostash O. P., Kondyr A. I., Vol’demarov O. V., Hladysh P. V., Kurechko M. V. Structural microdamageability of steels of the steam pipelines of thermal power plants // Materials Science. – Vol. 45. – No. 3. – 2009. – P. 340–350.
• [7] Foulds J. and Viswanathan R. Small Punch Testing for Determining the Material Toughness of Low Alloy Steel Components in Service // Journal of Engineering Materials and Technology. – 1994 – Vol. 116. – N 4, October.– P. 457–464.
• [8] Hong Xu, Xue-Kun Huang, Zhen Yang, Ji-ti Pan Property changes of 12Cr1MoV with 10CrMo910 main steam piping after long-term high-temperature service // Engineering Failure Analysis. – 10 (2003) – P. 245–250.
• [9] Balitskyi O., Ripey I., Eliasz J. Estimation of metal bends of high temperature pipelines according to hardness measuring results // Bulletin of Kharkov National Automobile and Highway University. Collection of Scientific Works – Kharkov. - 2011. – Issue 54. – P. 18-22.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).