Energetistic criterion of longitudinal welding in hot extrusion of aluminium alloys

• Autorzy: Patejuk A. , Piwnik J.

Warianty tytułu

PL

Eergetyczne kryterium spajania wzdłużnego strug w procesach wyciskania na gorąco stopów aluminium

• Języki publikacji: EN

Abstrakty

EN

Theoretical criteria are proposed for the plastic cohesion of aluminum alloys during hot extrusion. It is postulated that the governing influence is the tangential force field at the surfaces in contact. The critical value of the energy liberated at the surfaces by the action of these forces depends on the temperature, the pressure, the yield stress and the physical state and degree of intimacy of the contacting surfaces. A mathematical formulation is proposed, which is a function of the temperature, the yield stress, the normal stress field at the surface, the deformation rate and certain parameters describing the geometry and the physical state of the surface.

PL

W pracy przedstawiono energetyczne kryterium wzdłużnego spajania strug plastycznych podczas wyciskania stopów aluminium na gorąco. Analizowane kryteria mogą być efektywnie wykorzystane w wielu sytuacjach projektowania procesów technologicznych. Ułatwiają również ustalenia warunków eksperymentu przy symulacji numerycznej procesu. Chodzi tu o ułatwienie oszacowania pól prędkości i naprężeń w obszarze płynięcia plastycznego.

Słowa kluczowe

EN

longitudinal welding; theoretical criteria; hot extrusion; aluminum alloy

PL

spawanie wzdłużne; wyciskanie na gorąco; stop aluminium

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archiwum Odlewnictwa
• Rocznik: 2006
• Tom: R. 6, nr 18/1
• Strony: 161--166
• Opis fizyczny: Bibliogr. 7 poz., rys.

Twórcy

autor

Patejuk A.

• Technical University, st. Wiejska 45C, Białystok, Poland

autor

Piwnik J.

• Technical University, st. Wiejska 45C, Białystok, Poland

Bibliografia

• [1] Giljdengorn, M. S. et al., „Pressovanie so svarkoj poljih izdelij iz Aljominievljih splavov” (Extrusion of Hollow Aluminium Sections with Welds). Metalurgija, Moscow, 1975.
• [2] Plata M., Piwnik J.: Theoretical and experimental analysis of seam weld formation in hot extrusion of aluminium alloys. Report, Alusuisse Technology Center. 2000.
• [3] Arif A. F. M., Sheikh A. K., Qamar S. Z.: A study of die failure mechanisms in aluminium extrusion, Journal of Materials Processing Technology, 134, (2003) 318–328.
• [4] Akeret, R., „Extrusion Welds – Quality Aspects are Now Center Stage”, Proceedings of 5th International Aluminium Extrusion Technology Seminar ET’92, Chicago, Vol. I (1992) 319-336.
• [5] Misiolek, W. Z. and Kelly, R. M., „Dead Metal Zones in Extrusion of Complex Shapes”, Proceedings of 5th International Aluminium Extrusion Technology Seminar ET’92, Chicago, Vol. I (1992) 315-318.
• [6] Valberg, H. and Groenseth R. A., „Deformation and Metal Flow when Extruding Hollow Aluminium Profiles”, Int. J. Mat. & Prod. Techn. Vol. 8, No. 1, (1993) 235-239.
• [7] Skorulski G., Patejuk A.: Pękanie utwardzonej warstwy przejściowej w procesie wyciskania współbieżnego. III Sympozjum Mechaniki Zniszczenia Materiałów i Konstrukcji. Augustów (2005) 377-380.