Highsilicone Austempered Ductile Iron

• Autorzy: Kochański A. , Krzyńska A. , Radziszewski T.

Identyfikatory

DOI

10.2478/afe-2014-0013

• Języki publikacji: EN

Abstrakty

EN

Ductile iron casts with a higher silicone content were produced. The austempering process of high silicone ductile iron involving different austempering times was studied and the results presented. The results of metallographical observations and tensile strength tests were offered. The obtained results point to the fact that the silicone content which is considered as acceptable in the literature may in fact be exceeded. The issue is viewed as requiring further research.

Słowa kluczowe

EN

austempered ductile iron; silicone content; matrix structure; ultimate tensile strength

PL

żeliwo sferoidalne; właściwości mechaniczne; wytrzymałość na rozciąganie

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2014
• Tom: Vol. 14, iss. 1
• Strony: 55--58
• Opis fizyczny: Bibliogr. 20 poz., rys., tab., wykr.

Twórcy

autor

Kochański A.

• Institute of Technology, Faculty of Production Engineering Warsaw University of Technology Narbutta 85, 02-524 Warszawa POLAND

autor

Krzyńska A.

• Institute of Technology, Faculty of Production Engineering Warsaw University of Technology Narbutta 85, 02-524 Warszawa POLAND

autor

Radziszewski T.

• Institute of Technology, Faculty of Production Engineering Warsaw University of Technology Narbutta 85, 02-524 Warszawa POLAND

Bibliografia

• [1] Janowiak, J. F. & Gundlach, R. B. (1983). Development of ductile iron for commercial austempering. AFS Transactions. 86, 377.
• [2] Röhrig, K. (1983). Zwischenstufenvergütetes Gusseisen mit Kugelgraphit. Giesserei-Praxis. 1/2, 1-13.
• [3] Gundalach, R. B. & Janowiak, J. F. (1983). Development of a ductile iron for commercial austempering. AFS Transactions. 94, 377-388.
• [4] Harding, R. A. & Gilbert G. N. J. (1986). Why the properties of ductile irons should interest engineers. Br Foundryman. 79. 489-496.
• [5] Johansson, M. (1977). Austenitic bainitic ductile iron. AFS Trans. 85, 117-122.
• [6] Putatunda, S. K., Bartosiewicz, L., Alberts, F. A. & Singh, I. (1993). Influence of microstructure on high cycle fatigue behavior of austempered ductile cast iron. Mater Charact. 30, 221-234.
• [7] Shanmugam, P., Rao, P. P., Udupa, K. R. & Venkataraman, N. (1994). Effect of microstructure on the fatigue strength of an austempered ductile iron. J MaterSci. 29, 4933-4940.
• [8] Bartosiewicz, L., Duraiswamy, S., Sengupta, A. Putatunda, S. K. (1991). Near-threshold fatigue crack growth behavior of austempered ductile cast iron. Morris Fine Symposium, (pp. 135-138). Detroit: TMS.
• [9] Bartosiewicz, L., Krause, A. R., Duraiswamy, S., Sengupta, A. Putatunda, S. K. (1990). Relationship between fatigue threshold and fatigue strength in austempered ductile cast iron. International Symposium for Testing and Failure Analysis, (pp. 323-336), vol. 16. ISTFA, ASM.
• [10] Rao, P. P. & Putatunda, S. K. (1997). Influence of microstructure on fracture toughness of austempered ductile cast iron. Metal Mater Trans A. 28, 1457-1470.
• [11] Putatunda, S. K. & Singh, I. (1995). Fracture toughness of unalloyed austempered ductile cast iron. J. Test. Eval. 23(5), 325-332.
• [12] Rao, P. P. & Putatunda, S. K. (1998). Dependence of fracture toughness of austempered ductile cast iron on austempering temperature. Meta.l Mater. Trans. A(29), 3005-3016.
• [13] Doong, J. L. & Chen, C. (1989). Fracture toughness of bainitic-nodular cast iron. Fatigue Fract Eng Mater Struct. 12, 155-165.
• [14] Dorazil, E. Holzman, M. (1991). Fracture behavior of austempered ductile iron. Proceedings of the World Conference on Austempered Ductile Iron, March 1991, (pp. 32-66). Bloomingdale, IL.
• [15] Schmidt, I. & Schuchert, A. (1987). Unlubricated wear of austempered ductile cast iron. Z Metal. 78, 871-875.
• [16] Bradenberg, K. R., Lee, I., Maxwell, D., Newman P. (2002). Independent Trailer Suspension Utilizing Unique ADI Bracket, SAE Technical Paper 2002-01-0674.
• [17] Seaton, P.B., Xiao-Ming, L. (2002). An ADI Alternative for a Heavy Duty Truck Lower Control Arm.
• [18] Laino, S., Sikora, J. & Dommarco, R. C. (2011). Advances in the Development of Carbidic ADI, Key Engineering Materials. 457, 187-192.
• [19] Raghavendra, H., Bhat, K. L., Rajendra Udupa, K., Rajath Hegde, M. M. (2010). Grinding Wear Behavior of Stepped Austempered Ductile Iron as Media Material During Comminution of Iron Ore in Ball Mills, International Conference on Advances in Materials and Processing Technologies, AMPT, Conference Proceedings eds.: Chinesta F., Chastel Y., and El Mausori M.
• [20] Myszka, D., Kaczorowski, M., Tybulczuk, J. (2003). Austempered ductile cast iron directly isothermal tempered. Wyd. Instytutu Odlewnictwa, Kraków.