Comparison of structure and mechanical properties of nodular cast irons after casting and after heat treatment

• Autorzy: Vaško A. , Belan J. , Kuchariková L.
• Języki publikacji: EN

Abstrakty

EN

The paper deals with the influence of charge composition on microstructure and mechanical properties of synthetic nodular cast irons after casting and after heat treatment (ferritizing annealing and isothermal heat treatment). Chemical composition of individual melts was regulated alternatively by carburizer and ferrosilicon (FeSi) or metallurgical silicon carbide (SiC). The results of experiments show that SiC additive positively influences the microstructure as well as mechanical properties of nodular cast iron, especially in specimens from the melts with higher ratio of steel scrap in the charge.

Słowa kluczowe

EN

nodular cast iron; ferritizing annealing; isothermal heat treatment

PL

żeliwo sferoidalne; wyżarzanie ferrytyczne; obróbka cieplna izotermiczna

• Wydawca: Oficyna Wydawnicza Stowarzyszenia Menedżerów Jakości i Produkcji
• Czasopismo: Zeszyty Naukowe. Quality. Production. Improvement
• Rocznik: 2017
• Tom: No. 1 (6)
• Strony: 31--38
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Vaško A.

• University of Žilina, Faculty of Mechanical Engineering, Department of Materials Engineering

autor

Belan J.

• University of Žilina, Faculty of Mechanical Engineering, Department of Materials Engineering

autor

Kuchariková L.

• University of Žilina, Faculty of Mechanical Engineering, Department of Materials Engineering

Bibliografia

• 1. BENECKE T., VENKATESWARAN S., SCHUBERT W. D., LUX B. 1994. Investigation of the influence of silicon carbide in the production of ductile cast iron. „Foundryman”. Vol. 87, No. 10, p. 355-360.
• 2. DORAZIL E. 1985. Vysokopevná bainitická tvárna liatina. Academia. Praha.
• 3. GEDEONOVÁ Z., JELČ I. 2000. Metalurgia liatin. HF TU. Košice.
• 4. KARSAY S. I. 1996. Tvárna liatina I. Výroba. Fompex. Trenčín.
• 5. SKOČOVSKÝ P., VAŠKO A. 2007. Kvantitatívne hodnotenie štruktúry liatin. EDIS. Žilina.
• 6. SKOČOVSKÝ P., BOKŮVKA O., KONEČNÁ R., TILLOVÁ E. 2014. Náuka o materiáli. EDIS. Žilina.
• 7. SKOČOVSKÝ P., PODRÁBSKÝ T. 2005. Grafitické liatiny. EDIS. Žilina.
• 8. VAŠKO A., SKOČOVSKÝ P. 2014. Vlastnosti a použitie kovových materiálov. EDIS. Žilina.
• 9. VENKATESWARAN S., WILFING J., SCHUBERT W. D., LUX B., BENECKE T. 1989. Influence of SiC and FeSi additions on the microstructure, cooling curve and shrinkage porosity of ductile iron. In: Physical metallurgy of cast iron. Tokyo, Japan, p. 171-178.

Uwagi

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).