The Effect of Alloying on Mechanical Properties of Advanced High Strength Steels

• Autorzy: Kučerová L. , Jirkova H. , Mašek B.

Identyfikatory

DOI

10.2478/amm-2014-0206

Warianty tytułu

PL

Wpływ dodatków stopowych na właściwości mechaniczne zaawansowanych stali o dużej wytrzymałości

• Języki publikacji: EN

Abstrakty

EN

Quenching and partitioning process with incorporated incremental deformation was optimized for six high strength steels with various contents of carbon (0.4-0.6%), manganese (0.6-1.2), silicon (2-2.6%) and chromium (0.8-1.3%). The optimization was gradually done for each steel with respect to the final microstructures and properties. The effect of cooling rate, quenching and partitioning temperature on microstructure development was further investigated. Interesting combinations of mechanical properties were obtained, with tensile strength in the region of 1600-2400 MPa and ductility of 6-20%.

PL

Przeprowadzono optymalizacje procesu hartowania i partycjonowania węgla (Quenching and Partitioning – Q&P) w połączeniu ze stopniowymi przyrostami odkształcenia dla sześciu wysokowytrzymałych stali o różnej zawartości węgla (0, 4-0, 6%) manganu (0, 6-1, 2%), krzemu (2-2, 6%) oraz chromu (0, 8-1, 3%). Optymalizacje prowadzono dla kazdej stali stopniowo pod katem końcowej mikrostruktury i właściwości. Następnie przeprowadzono badania wpływ szybkości chłodzenia oraz temperatury hartowania i partycjonowania na rozwój mikrostruktury. W rezultacie otrzymano interesujące kombinacje właściwości mechanicznych stali o wytrzymałości na rozciąganie w zakresie 1600-2400 MPa oraz ciągliwości w zakresie 6-20%.

Słowa kluczowe

EN

quenching and partitioning process; retained austenite; martensite; incremental deformation

PL

proces hartowania; partycjonowanie; austenit szczątkowy; martenzyt; odkształcenia

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 3
• Strony: 1189--1192
• Opis fizyczny: Bibliogr. 11 poz., rys., tab.

Twórcy

autor

Kučerová L.

• University of West Bohemia, Pilsen, Czech Republic

autor

Jirkova H.

• University of West Bohemia, Pilsen, Czech Republic

autor

Mašek B.

• University of West Bohemia, Pilsen, Czech Republic

Bibliografia

• [1] S. Wiewiórowska, Archives of Metallurgy and Materials 58, 573-578 (2013).
• [2] D. V. Edmonds, et al. Materials Science and Engineering A 438-440, 25-34 (2006).
• [3] B. Mašek, et al. Journal of Iron and Steel Research International 18, 730-734 (2011).
• [4] L. Kučerová, et al.in, Annals of DAAAM for 2009, DAAAM International Vienna, 1035-1036, Vienna (2009).
• [5] B. Mašek, et al. Materials Science Forum 654-656, 94-97 (2010).
• [6] B. Paravicini, et al., Materials Science and Engineering: A 559, 486-495 (2013).
• [7] S. S. Nayak, et al., Materials Science and Engineering: A 498, 442-456 (2008).
• [8] L. Heping, et al., Scripta Materialia 64, 749-752 (2011).
• [9] H. Jirková, et al., Material Science Forum 706-709, 2734 (2012).
• [10] D. Aišman, et al., in: Annals of DAAAM for 2008, DAAAM International Vienna, 1035-1036, Vienna (2008).
• [11] H. Y. Li, et al., Materials Science and Engineering A 527, 6255-6259 (2010).