Adhesion of organic coatings to hot-dip galvanized steel

• Autorzy: Miszczyk A.

Warianty tytułu

PL

Adhezja powłok organicznych do powierzchni stali ocynkowanej zanurzeniowo

• Języki publikacji: EN

Abstrakty

EN

Duplex systems provide long-time corrosion protection, much longer than the sum of the lifetimes of zinc and paint used individually. However loss of adhesion between coating and zinc substrate is often found in practice. Different methods of zinc surface preparations are used in the field. The aim of this study was to examine and compare coating protection when the old zinc surface, stored during long-time period (15 years) in laboratory conditions, was painted. Adhesion and impedance studies using epoxy coating systems on galvanized steel substrate, which had been prepared by different methods, were performed.

PL

System duplex zapewnia długoletnią ochronę stali przed korozją, znacznie dłuższą niż sumaryczny okres ochrony zapewniany osobno przez powłokę cynkową i zestaw powłokowy. Jednakże, w praktyce często spotyka się utratę przyczepności pomiędzy powłoką a podłożem cynkowym. Stosuje się różne sposoby przygotowania powierzchni cynku przed zastosowaniem powłoki ochronnej. Celem niniejszej pracy było zbadanie i porównanie właściwości ochronnych powłoki nałożonej na starą powierzchnię cynku, przechowywaną przez długi okres czasu (15 lat) w warunkach laboratoryjnych. Wykonano badania przyczepności oraz impedancyjne powłoki epoksydowej na podłożu stali ocynkowanej zanurzeniowo, przygotowanej przez użyciu różnych metod.

Słowa kluczowe

EN

organic coatings; hot-dip galvanized steel; adhesion; Duplex system

PL

powłoki ochronne; stal ocynkowana; cynkowanie zanurzeniowe; adhezja; system duplex

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Ochrona przed Korozją
• Rocznik: 2013
• Tom: nr 3
• Strony: 71--73
• Opis fizyczny: Bibliogr. 11 poz., rys., wykr.

Twórcy

autor

Miszczyk A.

• Gdansk University of Technology, Faculty of Chemistry, Department of Electrochemistry, Corrosion and Material Engineering, Gdansk, Poland

Bibliografia

• 1. Uhlig’s Corrosion Handbook, R. W. Revie (ed.), 3rd edition, John Wiley & Sons, 2011.
• 2. X.G. Zhang, Corrosion and Electrochemistry of Zinc, Springer, 1996.
• 3. Handbook of Hot-dip Galvanization, P. Maaß and P. Peißker (eds.), John Wiley & Sons, 2011.
• 4. I. Cabanelas, A. Collazo, M. Izquierdo, X. R. Nóvoa, C. Pérez, Influence of galvanised surface state on the duplex systems behaviour, Corr. Sci. 49 (2007) 1816–1832.
• 5. S. Maeda, Surface chemistry of galvanized steel sheets relevant to adhesion performance, Prog. Org. Coat., 28 (1996) 227-238.
• 6. C. Pérez, A. Collazo, M. Izquierdo, P. Merino, X.R. Nóvo, Comparative study between galvanised steel and three duplex systems submitted to a weathering cyclic test, Corr. Sci., 44, (2002) 481–500.
• 7. B. Del Amo, L. Véleva, C.I. Elsner, A.R. di Sarli, Performance of coated steel systems exposed to different media: part I. Painted galvanized steel, Prog. Org. Coat. 50 (2004) 179–192.
• 8. B. Ramezanzadeh, M.M. Attar, M. Farzam, Corrosion performance of a hot-dip galvanized steel treated by different kinds of conversion coatings, Surf. Coat. Tech., 205 (2010) 874–884.
• 9. I.S. Cole, T.H. Muster, N.S. Azmat, M.S. Venkatraman, A. Cook, Multiscale modeling of the corrosion of metals under atmospheric corrosion, Electrochim. Acta, 56 (2011) 1856–1865.
• 10. Y. Chen, P. Schneider, A. Erbe, Investigation of native oxide growth on zinc in different atmospheres by spectroscopic ellipsometry, Phys. Status Solidi A 209 (2012) 846–853.
• 11. K. Schaefer, A. Miszczyk, Improvement of electrochemical action of zinc-rich paints by addition of nanoparticulate zinc, Corr. Sci. 66 (2013) 380-391.