The Study of the Tensile Strength of AlSi21CuNiMg Silumin in the Final Stage of Solidification and the Initial Stage of Cooling

• Autorzy: Romankiewicz Remigiusz

Identyfikatory

DOI

10.7494/jcme.2019.3.3.57

• Języki publikacji: EN

Abstrakty

EN

The paper presents the results of tensile strength tests of AlSi21CuNiMg silumin made on a test stand. Silumin was under examination in an unmodified state and after modification with AlCu19P1.4 master alloy in quantity of 0.2% in relation to the mass of the alloy. Using a scanning microscope, the surface fractures obtained from tensile tests were tested. The structure and profiles of fractures were examined using an optical microscope. Modification of the tested silumin resulted in a favorable fragmentation and regular distribution of the crystals of the primary silicon in the alloy structure, which led to an almost twofold increase in the strength of the silumin samples at the final solidification stage from 3.5 to 6.6 MPa. As a result of these changes, the resistance of silumin to hot cracks should increase, which is of great importance when casting hypereutectic silumin in a metal mould that strongly inhibits the shrinkage of the castings.

Słowa kluczowe

EN

silumin; solidification; modification; tensile strength

• Wydawca: AGH University of Science and Technology Press
• Czasopismo: Journal of Casting & Materials Engineering
• Rocznik: 2019
• Tom: Vol. 3, no. 3
• Strony: 57--61
• Opis fizyczny: Bibliogr. 7 poz., fot, rys., wykr.

Twórcy

autor

Romankiewicz Remigiusz

• University of Zielona Góra, Faculty of Mechanical Engineering, Licealna St. 9, 65-417, Zielona Góra

Bibliografia

• [1] Górny Z. (1992). Odlewnicze stopy metali nieżelaznych. Warszawa: Wydawnictwa Naukowo-Techniczne.
• [2] Höner K.E. (1982). Die thermische Analyse als Kontrollverfahren für die Wirksamkeit einer Schmelzebehandlung von Aluminium-Gusslegierungen durch Veredelung oder Kornfeinung. Giessereiforschung, 34(1), 1–10.
• [3] Pietrowski S. (2001). Siluminy. Łódź: Wydawnictwo Politechniki Łódzkiej.
• [4] Poniewierski Z. (1989). Krystalizacja, struktura i właściwości siluminów. Warszawa: Wydawnictwa Naukowo-Techniczne.
• [5] Velten B., Rasche C. & Herold-Schmidt U. (1989). Bildung und Ausbreitung von Thermoschockrissen in einer Aluminium-Gusslegierungen. Practical Metallography – Special Edition, 20, 271–280.
• [6] Mutwil J., Romankiewicz R. & Kujawa K. (2005). Nowa wersja stanowiska do badania wytrzymałości na rozciąganie krzepnących metali i stopów. Archive of Foundry Engineering, 5(17), 183–190.
• [7] Romankiewicz R. (2011). Badania nad możliwością szybkiej oceny właściwości technologicznych siluminów w końcowym etapie krzepnięcia i początkowym etapie stygnięcia. Doctoral Dissertation. University of Zielona Góra.