Influence of the filler on the density profile of wood polymer composites

• Autorzy: Borysiuk Piotr , Auriga Radosław , Kośka Paweł

Identyfikatory

DOI

10.5604/01.3001.0013.7734

• Języki publikacji: EN

Abstrakty

EN

Influence of the filler on the density profile of wood polymer composites. WPC panels with HDPE matrix composites made in two stages were tested: 1 - obtaining WPC granulate using the extrusion method, 2 - production of panels by flat pressing in the form. As a filler, sawdust was used with two degrees of fineness (about 10 - 35 mesh and below 35 mesh) and three levels of content (40, 50 and 60%). In total, 6 panel variants were created for which the density and density profile in the cross-section were determined. It was found that panels with a filler content of 40% are characterized by a uniform flat density profile. The increase in filler content (up to 50 - 60%) affects the density reduction in the core zone of the panel. The density and density profile of panels from WPC composites does not depend on the size of the filler particles.

PL

Wpływ napełniacza na profil gęstości kompozytów drzewno polimerowych. Przeprowadzono badania płyt z kompozytów WPC o matrycy HDPE wytworzonych dwuetapowo: 1 – pozyskanie granulatu WPC metodą extruzji, 2 – wytworzenie płyt metodą prasowania płaskiego w formie. Jako napełniacz zastosowano trociny o dwóch stopniach rozdrobnienia (ok. 10 – 35 mesh i poniżej 35 mesh) i 3 poziomach zawartości (40, 50 i 60%). Łącznie wytworzono 6 wariantów płyt dla których określono gęstość i profil gęstości na przekroju poprzecznym. Ustalono, że płyt o zawartości napełniacza na poziomie 40% charakteryzują się jednolitym płaskim profilem gęstości. Wzrost zawartości napełniacza (do 50 – 60%) wpływa na obniżenie gęstości w strefie środkowej płyty. Gęstość i profil gęstości płyt z kompozytów WPC nie zależy od wielkości cząstek napełniacza.

Słowa kluczowe

EN

WPC composite; sawdust; HDPE; density profile

• Wydawca: Wydawnictwo Szkoły Głównej Gospodarstwa Wiejskiego w Warszawie
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2019
• Tom: No. 106
• Strony: 31--37
• Opis fizyczny: Bibliogr. 12 poz., rys., tab.

Twórcy

autor

Borysiuk Piotr

• Faculty of Wood Technology, Warsaw University of Life Sciences – SGGW, 159 Nowoursynowska St., 02-787 Warsaw

autor

Auriga Radosław

• Faculty of Wood Technology, Warsaw University of Life Sciences – SGGW, 159 Nowoursynowska St., 02-787 Warsaw

autor

Kośka Paweł

• Faculty of Wood Technology, Warsaw University of Life Sciences – SGGW, 159 Nowoursynowska St., 02-787 Warsaw

Bibliografia

• 1. CHEN H. C., CHEN T. Y., HSU C. H., 2006: Effects of Wood Particle Size andMixing Ratios of HDPE on the Properties of the Composites. Holz als Roh- undWerkstoff, 64, 172-177.
• 2. DROUET T., 1992: Technologia płyt wiórowych, Wydawnictwo SGGW, Warszawa.
• 3. GEIMER R. L., CLEMONS C., WOOD J. E. Jr., 1993: Density range of compressionmoldedpolypropylene-wood composites. Wood and Fiber Science, 25 (2), 163-169.
• 4. KLYOSOV A.A., 2007: Wood-Plastic Composites. John Wiley & Sons Inc.,Hoboken, New Jersey.
• 5. MABIALA A., 1992: Wpływ wybranych parametrów technologicznych na rozkładgęstości na przekroju poprzecznym płyt wiórowych, maszynopis rozprawy doktorskiejwykonanej w Katedrze Tworzyw Drzewnych SGGW, Warszawa.
• 6. NIEMZ P., 1993: Physik des Holzes und Holzwerkstoffe, DRW-Verlag.
• 7. SAECHTLING H., 1999: Tworzywa sztuczne. Poradnik. WNT, Warszawa.
• 8. TREUSCH O., TRÖGER, WEGENER G., 2004: Einfluss von Rohdichte undBindemittelmenge auf das Rohdichteprofilvon einschichtigen Spanplatten, Holz RohWerkstoff, N. 62, s. 474 – 475.
• 9. WONG E., YANG M., ZHANG M., WANG Q., NAKAO K., KAWAI S., 2003:Analysis of the effects of density profile on the bending properties of particleboardusing finite element method (FEM), Holz als Roh- und Werkstoff, N. 61, s. 66 – 72.
• 10. WONG E., ZHANG M., WANG Q., KAWAI S., 1998: Effects of mat moisturecontent and press closing speed on the formation of density profile and properties ofparticleboard, Journal of Wood Science, No. 44, p. 287 – 295.
• 11. WONG E., ZHANG M., WANG Q., KAWAI S., 1999: Formation of the densityprofile and its effects on the properties of particleboard, Wood Science andTechnology Vol. 33, September, p. 327 – 340.
• 12. ZAJCHOWSKI S., GOZDECKI C., KOCISZEWSKI M., 2005: Badania właściwościfizycznych i mechanicznych kompozytów polimerowo-drzewnych (WPC).Kompozyty, 5, 45-50.

Uwagi

Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).