Influence of Hydration on Transport and Storage of Spinel-Based Refractory Raw Materials

• Autorzy: Jastrzębska I. , Szczerba J. , Prorok R. , Śnieżek E.

Warianty tytułu

PL

Wpływ hydratacji na transport i składowanie surowców ogniotrwałych na bazie spinelu

• Języki publikacji: EN

Abstrakty

EN

This work concerns the hydration resistance of spinel MgAl2O4-based aggregates which comprise the common raw materials for the production of refractories. A sintered product along with the melted one were taken for the investigation. The starting materials were characterized in terms of their chemical and phase composition by XRF and XRD methods, respectively. Subsequently, the samples were subjected to hydration test according to ASTM C 554-92. The after-hydration samples were analyzed by XRD and SEM/EDS methods. It was found that sintered spinel aggregates enriched in Mg2+ ions and containing free MgO are highly susceptible to water exposure.

PL

Praca dotyczy badania i oceny odporności na hydratację spiekanych i topionych kruszyw na bazie spinelu MgAl2O4, które stanowią grupę surowców szeroko stosowanych do produkcji formowanych i nieformowanych materiałów ogniotrwałych. Wyjściowe materiały zbadano pod względem ich składu fazowego (XRD) i chemicznego (XRF). Następnie przeprowadzono badanie hydratacji metodą autoklawizacji według normy ASTM C 554-92. Próbki po hydratacji poddano analizie składu fazowego (XRD) i mikrostruktury (SEM/EDS). Badania wykazały, iż kruszywa spinelowe wzbogacone w spinel o nadmiarze jonów Mg2+ i zawierające wolny MgO wykazują największą zdolność do hydratacji.

Słowa kluczowe

EN

hydration; spinel; MgAl2O4; MgO; refractories; transport; storage

PL

hydratacja; spinel; MgAl2O4; MgO; transport; przechowywanie

• Wydawca: Sieć Badawcza Łukasiewicz - Poznański Instytut Technologiczny
• Czasopismo: Logistyka
• Rocznik: 2014
• Tom: nr 4
• Strony: 4372--4379, CD6
• Opis fizyczny: Bibliogr. 7 poz., rys., zdj.

Twórcy

autor

Jastrzębska I.

• AGH University of Science and Technology, Kraków, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractories

autor

Szczerba J.

• AGH University of Science and Technology, Kraków, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractories

autor

Prorok R.

• AGH University of Science and Technology, Kraków, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractories

autor

Śnieżek E.

• AGH University of Science and Technology, Kraków, Faculty of Materials Science and Ceramics, Department of Ceramics and Refractories

Bibliografia

• [1] Chen M., Wang N., Yu J., Yamaguchi A.: Effect of porosity on carbonation and hydration resistance of CaO materials, Journal of European Ceramic Society, 27/2007.
• [2] Chen S., Chen G., Cheng J.: Effect of additives on the hydration resistance of materials synthesized from the magnesia-calcia system, Journal of American Ceramic Society, 83/2000.
• [3] Hai-Doo K., Im-Sik L., Suk-Wong Kang, Jae-WoongK.: The formation of NaMg. Journal of Materials Science,29/1994. 2Al15O25 in an α-Al2O3 matrix and its effect on the mechanical properties of alumina,
• [4] Jastrzębska I., Szczerba J., Madej D.: Wpływ rodzaju surowców magnezjowych na właściwości fizyczne i termomechaniczne betonów zasadowych, Materiały Ceramiczne, 65/2013.
• [5] Jastrzębska I., Szczerba J., Prorok R., Madej D.: Efekty procesu hydratacji ogniotrwałych betonów zasadowych, Logistyka, 4/2013.
• [6] Salomão R., Pandolfelli V. C.: Magnesias inter hydration-dehydration behavior in refractory castables, Ceramics International, 34/2008.
• [7] Szymaszek M., Szczerba J., Zelik W.: Kierunki rozwoju materiałów ogniotrwałych dla przemysłu cementowo-wapienniczego, Materiały Ceramiczne 63/2011.