The Influence of Strontium on the Microstructure of Cast Magnesium Alloys Containing Aluminum and Calcium

• Autorzy: Rzychoń T. , Dybowski B. , Kiełbus A.

Identyfikatory

DOI

10.1515/amm-2015-0026

Warianty tytułu

PL

Wpływ strontu na mikrostrukturę odlewniczych stopów magnezu z dodatkiem aluminium i wapnia

• Języki publikacji: EN

Abstrakty

EN

The structure of Mg-9Al-2Ca-xSr alloys is composed of a-Mg grains and the Al₂Ca and Al₄ Sr phases in the interdendritic areas. These phases are formed as a result of eutectic reactions. Globular particles of the Al8Mn5 phase are observed within the interior of the grains. The addition of strontium to Mg-9Al-2Ca-0.4Mn alloys causes the formation of the Al₄Sr phase and increase of its volume fraction with increasing strontium levels. Moreover, increase of the strontium amount causes a decrease of aluminum content in the a-Mg solid solution.

PL

W artykule przedstawiono wyniki badań wpływu strontu na mikrostrukturę odlewniczych stopów magnezu zawierających aluminium i wapń. Jakościową analizę fazową przeprowadzono za pomocą rentgenowskiej analizy fazowej i metody EBSD. Do ilościowej analizy fazowej zastosowano metody analizy obrazu. Po odlewaniu mikrostruktura stopów zawierających 9% mas. aluminium, 2% mas. wapnia, 0,3% mas. strontu i 0,4% mas. manganu składa się z roztworu stałego α-Mg oraz wydzieleń faz międzymetalicznych Al₂Ca, Al₄Sr i Al₈Mn₅. Zwiększenie zawartości strontu do 2% mas. powoduje zwiększenie udziału objętościowego fazy Al₄Sr i zmniejszenie stężenia aluminium w roztworze stałym α-Mg.

Słowa kluczowe

EN

magnesium alloys; microstructure; cast Mg-Al-Ca-Sr alloys

PL

stopy magnezu; mikrostruktura; odlewnicze stopy magnezu

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 1
• Strony: 167--170
• Opis fizyczny: Bibliogr. 11 poz., rys., tab.

Twórcy

autor

Rzychoń T.

• Silesian University of Technology, Katowice, Poland

autor

Dybowski B.

• Silesian University of Technology, Katowice, Poland

autor

Kiełbus A.

• Silesian University of Technology, Katowice, Poland

Bibliografia

• [1] B. Jing, S. Yangshan, X. Shan, X. Feng, Z. Tianbai, Mater. Sci. Eng. A 419, 181-188 (2006).
• [2] E. Aghion, B. Bronfin, F. Von Buch, H. Friedrich, S. Schumann, JOM 55(11), 30-33 (2003).
• [3] K. U. Kainer, Magnesium Alloys and Technologies, Wiley-VCH 2003.
• [4] ASM Speciality Handbook, Magnesium and magnesium alloys, ASM International 1999.
• [5] T. Rzychoń, J. Szala, A. Kiełbus, Arch. Metall. Mater. 57, 254-262 (2012).
• [6] L. Wojnar, K. J. Kurzydłowski, J. Szala, Praktyka analizy obrazu, Polskie Towarzystwo Stereologiczne, Kraków 2002.
• [7] T. Rzychoń, A. Kiełbus, Arch. Metall. Mater. 53, 901-907 (2008).
• [8] A. Suzuki, N. D. Saddock, L. Riester, E. Lara-Curzio, J. W. Jones, T. M. Pollock, Metall. Mater. Trans. A 38A, 420-427 (2007).
• [9] S. M. Liang, R. S. Chen, J. J. Blandin, M. Suery, E. H. Han, Mater. Sci. Eng. 480, 365-372 (2008).
• [10] D. W. Zhou, J. S. Liu, P. Peng, L. Chen, Y. J. Hu, Mater. Lett. 62, 206-210 (2008).
• [11] A. Suzuki, N. D. Saddock, J. W. Jones, T. M. Pollock, Acta Mater. 53, 2823-2834 (2005).