The influence of GTAW processing parameters on a geometry of remelted of C45 steel

• Autorzy: Adamiak S.
• Języki publikacji: EN

Abstrakty

EN

The work presented test rcsults of voltage effect of electric arc current and the rate of flow in relation to the sample on geometry of the surface layer during remelting of 45 steel with concentrated heat flux using GTAW method. The remelting of surface layer of C45 steel with a stable feed rate of welding head equalling 200 mm/min and with the intensity of electric arc current ranging from 50 to 300A and stable intensity or electric arc current 300A, the rate of head feed was changed from the value of 200 mm/min to 800 mm/min. Depth, width and the area of obtained layers were measured. The interrelation between the intensity of electric arc current and the rate of its advance in relation to the treated material and the geometry of remelted layers was determined.

PL

W pracy przedstawiono wyniki badań wpływu natężenia prądu łuku elektrycznego oraz jego szybkości przesuwu względem próbki na geometrię warstwy wierzchniej podczas nadtapiania powierzchniowego stali 45 skoncentrowanym strumieniem ciepła z zastosowaniern metody GTAW. Dokonano nadtopienia warstwy wierzchniej stali C45 przy stałej szybkości przesuwu głowicy spawalniczej 200 mm/min i zastosowaniu natężenia prądu łuku elektrycznego od 50 do 300A oraz stałym natężeniu prądu łuku elektrycznego 300A zmieniano prędkość przesuwu głowicy od 200 mm/s do 800 mm/min. Wykonano pomiary głębokości, szerokości oraz pola powierzchni otrzymanych warstw. Wyznaczono zależność pomiędzy natężeniem prądu łuku elektrycznego i szybkością jego przesuwu względem obrabianego materiału, a geometrią nadtopionych warstw.

Słowa kluczowe

EN

C45 steel; surface layer remelting; GTAW method

PL

stal C45; przetapianie warstwy wierzchniej; metoda GTAW

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2008
• Tom: Vol. 8, iss. 1 spec.
• Strony: 9--12
• Opis fizyczny: Bibliogr. 8 poz., rys., tab., wykr.

Twórcy

autor

Adamiak S.

• Institute of Technics, University of Rzeszow, ul, Rejtana 16a, 35-111 Rzeszów, Poland

Bibliografia

• [1] A.W. Orłowicz, A. Trytek, Shaping of microstructure and service properties of cast iron castings by surface refinement with elektric arc plasma. Archives of Foundry, Vol. 7, No 23, 2007, (in Polish).
• [2] A.W. Orłowicz, A. Trytek, Effect of rapid solidification on sliding wear of iron castings, Wear 9258, 2002.
• [3] Z. Nitkiewicz, J. Iwaszko, The use of arc plasma in surface engineering. Material engineering, 6, 373-375, 2000. (in a Polish).
• [4] A.W. Orłowicz, M. Mróz, Thermal coefficients of the GTAW method. Archives of Foundry, Year 2003, no 3, 2003, (in Polish).
• [5] Y. Adonyj, R.W. Richardson, W.A. Beaslack, Investigation of arc force effects in surface GTAW welding. Welding Journal, 9, 35-44, 1996.
• [6] Z. Opiekun, A. Trytek, The influence of plasma-generating gas on the quantity of heat taken by surface layer partially remelted casts of the MAR-M509 alloy, Archives of Foundry, Year 2006, no 18(1/2), 401-406, 2006, (in Polish).
• [7] W. Orłowicz, M, Mróz, A. Trytek, Heating efficiency in the GTAW process. Acta Mctallurgica Slovaca, No 2, 539-543, 1999.
• [8] M. Mróz, A. Orłowicz, M. Tupaj. Thermal coefficients of the GTAW method, Archives of Foundry, Year 2005, no 17,217-224, 2005, (in Polish).