Influence of Weave Design and Yarn Types on Mechanical and Surface Properties of Woven Fabric

• Autorzy: Azeem M. , Ahmad Z. , Wiener J. , Fraz A. , Siddique H. F. , Havalka A.

Identyfikatory

DOI

10.5604/01.3001.0010.7795

Warianty tytułu

PL

Wpływ wzoru tkackiego i rodzaju przędzy na mechaniczne i powierzchniowe właściwości tkaniny

• Języki publikacji: EN

Abstrakty

EN

The purpose of this study was to examine the effect of spinning technologies and weave design on fabric mechanical and surface properties. For this purpose, ring spun (combed, carded) and open-end (OE) techniques were used to manufacture yarns of polyester cotton (50:50) which were used in the weft, and 100% cotton yarn in the warp. Plain, twill, and satin weave designs were selected to construct woven samples on a projectile loom. The variation in fabric tensile strength is obvious with respect to weave designs. Higher interlacing of yarn produces more crimp in the load bearing, which may cause lower breaking strength and fewer broad floats. The mechanical and surface properties of these fabric samples were investigated and statistical analysis was performed, which showed a significant effect of the spinning technique and weave design on these properties.

PL

Celem tego badania było zbadanie wpływu technologii przędzenia i splotu na właściwości mechaniczne i powierzchniowe tkaniny. Przy zastosowaniu systemu obrączkowego i bezwrzecionowego wytworzono przędzę bawełniano-poliestrową(50:50) i przędzę w 100% bawełnianą. Następnie na krośnie chwytakowym wytworzono tkaniny o splotach płóciennym i atłasowym. Różnice w wytrzymałości na rozciąganie tkanin są oczywiste w odniesieniu do wzorów splotów. Większe przeplatanie przędzy powoduje więcej karbikowania, co może powodować niższą wytrzymałość na zerwanie. Zbadano mechaniczne i powierzchniowe właściwości próbek tkanin i wykonano analizę statystyczną, która wykazała istotny wpływ techniki przędzenia i rodzaju splotu na właściwości mechaniczne i powierzchniowe tkanin.

Słowa kluczowe

EN

PC yarn; ring spun; open-end; weave design; abrasion; pilling

PL

przędza PC; system obrączkowy; splot płócienny; splot atłasowy; wytrzymałość na zerwanie

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2018
• Tom: Vol. 26, no. 1 (127)
• Strony: 42--45
• Opis fizyczny: Bibliogr. 15 poz., rys., tab.

Twórcy

autor

Azeem M.

• Technical University of Liberec, Faculty of Textile Engineering, Studenstska 2, Liberec, Czech Republic

autor

Ahmad Z.

• Technical University of Liberec, Faculty of Textile Engineering, Studenstska 2, Liberec, Czech Republic

autor

Wiener J.

• Technical University of Liberec, Faculty of Textile Engineering, Studenstska 2, Liberec, Czech Republic

autor

Fraz A.

• University of Management and Technology, School of Textile and Design, C-2 Johar Town, Lahore, Pakistan

autor

Siddique H. F.

• Technical University of Liberec, Faculty of Textile Engineering, Studenstska 2, Liberec, Czech Republic
• Faculty of Textile Engineering, Technical University of Liberec, Liberec, Czech Republic

autor

Havalka A.

• Technical University of Liberec, Faculty of Textile Engineering, Studenstska 2, Liberec, Czech Republic

Bibliografia

• 1. Realff ML, Seo M, Boyce MC, Schwartz P, Backer S. Mechanical Properties of Fabrics Woven from Yarns Produced by Different Spinning Technologies: Yarn Failure as a Function of Gauge Length. Textile Research Journal 1991; 61(9): 517-530.
• 2. Mohamed MH, Lord PR. Comparison of physical properties of fabrics woven from open-end and ring spun yarns. Textile Research Journal 1973; 43(3): 154-166.
• 3. Lord P. The structure of open-end spun yarn. Textile Research Journal 1971; 41(9): 778-784.
• 4. Jameel NA, Khan AH, Reshamwala IH, Aghai MS. Strength of yarn spun by ring and openend spinning in cotton varieties, B-557 and AC-134 as influenced by fibre quality. Pakistan Journal of Agricultural Research 1982; 3(2): 112-121.
• 5. Rameshkumar C, Anandkumar P, Senthilnathan P, Jeevitha R, Anbumani N. Comparative studies on ring rotor and vortex yarn knitted fabrics. Autex Research Journal 2008; 8(4): 100105.
• 6. Kaynak HK, Topalbekiroğlu M. Influence of fabric pattern on the abrasion resistance property of woven fabrics. Fibers & Textiles in Eastern Europe 2008; 16(1): 54-56.
• 7. Özdil N, Özdoğan E, Öktem T. Effects of enzymatic treatment on various spun yarn fabrics. Fibres & Textiles in Eastern Europe 2003; 11(43): 58-61.
• 8. Lord P. A comparison of the performance of open-end and ring spun yarns in terry toweling. Textile Research Journal 1974; 44(7): 516-522.
• 9. Paek SL. Pilling, abrasion, and tensile properties of fabrics from open-end and ring spun yarns. Textile Research Journal 1989; 59(10): 577-583.
• 10. Malik ZA, Tanwari A, Sheikh H. Influence of plain and Twill (3/1) weave designs on the tensile strength of PC blended fabrics. Mehran University Research Journal of Engineering and Technology 2011; 30(1): 23-28.
• 11. Alpay HR, Becerir B, Akgun M. Assessing reflectance and color differences of cotton fabrics after abrasion. Textile Research Journal 2005; 75(4): 357-361.
• 12. Mirjalili A. Using Electromagnetic Force in Weft Insertion of a Loom. Fibres & Textiles in Eastern Europe 2005; 13, 3(51): 67-70.
• 13. Ferdous N, Rahman MS, Kabir RB, Ahmed AE. A Comparative Study on Tensile Strength of Different Weave Structures. International Journal of Scientific Research Engineering & Technology 2014; 3(9): 1307-1313.
• 14. Gabrijelčič H, Černoša E, Dimitrovski K. Influence of Weave and Weft Characteristics on Tensile Properties of Fabrics. Fibres & Textiles in Eastern Europe 2008; 16, 2(67): 45-51.
• 15. Barella A, Manich A. Relation Between Twist and Abrasion Resistance of Rotor Spun Yarns. Part II: Polyester and Blend Yarns. Textile Research Journal 1984; 54(5): 314-317.

Uwagi

PL

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).