Corrosion Resistance of High-Alloyed White Cast Iron

• Autorzy: Kawalec M. , Krawiec H.

Identyfikatory

DOI

10.1515/amm-2015-0048

Warianty tytułu

PL

Odporność na korozję wysokostopowego żeliwa białego

• Języki publikacji: EN

Abstrakty

EN

The paper presents the results of corrosion resistance tests carried out on high-alloyed white cast iron. Tests were performed in 0.1 M NaCl by the technique of linear voltammetry. The test material was collected from six high-vanadium cast iron melts with a variable content of carbon and vanadium, and thus with different microstructure. Studies have confirmed that the type of crystallised microstructure has a very important effect on the alloy corrosion resistance. The highest corrosion resistance showed the alloy with a ferritic matrix containing the spheroidal precipitates of vanadium carbide VC, while the lowest had the eutectic alloy with a pearlitic matrix.

PL

W pracy przedstawiono wyniki badań odporności na korozję wysokostopowego żeliwa białego. Badania przeprowadzono w 0,1M roztworze NaCl techniką woltamperometrii liniowej. Materiał do badań pobrano z sześciu wytopów żeliwa wysoko-wanadowego o zmiennej zawartości węgla i wanadu, a tym samym o różnej mikrostrukturze. Badania potwierdziły, że rodzaj wykrystalizowanej mikrostruktury ma bardzo istotny wpływ na odporność na korozję stopu. Najwyższą odporność na korozję wykazał stop o osnowie ferrytycznej ze sferoidalnymi wydzieleniami węglików VC, natomiast najniższą - eutektyczny stop o osnowie perlitycznej.

Słowa kluczowe

EN

corrosion resistance; white cast iron; microstructure; vanadium carbide; spheroidal carbide

PL

odporność na korozję; białe żeliwo; mikrostruktura; węglik wanadu; węglik sferoidalny

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 1
• Strony: 301--303
• Opis fizyczny: Bibliogr. 15 poz., rys., tab.

Twórcy

autor

Kawalec M.

• AGH University of Science and Technology, Faculty of Foundry Engineering, Al. A. Mickiewicza 30, 30-059 Kraków, Poland

autor

Krawiec H.

• AGH University of Science and Technology, Faculty of Foundry Engineering, Al. A. Mickiewicza 30, 30-059 Kraków, Poland

Bibliografia

• [1] H. Krawiec, Academic Press AGH, Krakow (2009).
• [2] E. Fraś, E. Guzik, Arch. of Metallurgy 25(4), 757-772 (1980).
• [3] E. Fraś, Crystallization of metals. WNT, Warsaw (2003).
• [4] E. Fraś, E. Guzik, W. Kapturkiewicz, H. F. Lopez, Mater. Sci. Tech. 13, 989-996 (1997).
• [5] M. Kawalec, E. Fraś, ISIJ Int. 48(4), 518-524 (2008).
• [6] E. Fraś, M. Kawalec, Mater. Eng. 29(2), 78-85 (2008).
• [7] D. Kopyciński, E. Guzik, S. Piasny, Arch. of Foundry Eng. 11, 61-66. (2011).
• [8] Y. Uematsu, K. Tokaji, T. Horie, K. Nishigaki, Mat. Sci. Tech. A 471, 15-21 (2007).
• [9] K. Tokaji, T. Horie, Y. Enomoto, Int. J. of Fatigue 28, 281-288 (2006).
• [10] M. Tanaka, K. Shimizu, D. Ito, T. Noguchi, Key Eng. Mater. 457, 279-284 (2011).
• [11] S. Nishiuchi, S. Yamamoto, T. Tanabe, T. Kitsudo, H. Mat-sumoto, Y. Kawano Trans. of the American Foundry Society, 831-844 (2003).
• [12] E. Guzik, The process of transforming cast iron - chosen questions. Archives of Foundry (2001).
• [13] M. Kawalec, Arch. of Foundry Eng. 11, 111-116 (2011).
• [14] M. Kawalec, E. Olejnik, Arch. of Foundry Eng. 12, 221-226 (2012).
• [15] M. Kawalec, M. Górny, Arch. of Foundry Eng. 12, 95-100 (2012).