Study on the Photochromic Properties of Coloured Luminous Fibres Based on PA6

• Autorzy: Yan Y. , Zhu Y. , Ge M.

Identyfikatory

DOI

10.5604/12303666.1196610

Warianty tytułu

PL

Badanie fotochromicznych właściwości barwionych luminescencyjnych włókien PA6

• Języki publikacji: EN

Abstrakty

EN

Coloured PA6 luminous fibres were prepared by adding luminous material and inorganic pigments. The morphology and optical properties of the coloured PA6 luminous fibres were characterized. The results revealed that luminous materials were dispersed uniformly in the fibres without obvious agglomerates. The yellow inorganic pigment and luminous material might induce a reduction in the PA 6 fibre crystallization degree. The luminous fibres emitted long-lasting phosphorescence with an excitation peak at 360 nm and emission peak at 515 nm. However, the excitation spectrum of the PA6-Y exhibited three peaks. The decay curves revealed that the yellow inorganic pigment enhanced the brightness of PA6 luminous fibres. The PA 6 luminous fibres had low colour purities and a high colour rendering index. There was no obvious difference among the emissive colours of the luminous fibres, and the colours of luminous fibres were similar to those of the pigments added.

PL

Barwione luminescencyjne włókna PA6 przygotowano przez dodanie materiałów luminescencyjnych i pigmentów nieorganicznych. Scharakteryzowano właściwości morfologiczne i optyczne barwionych luminescencyjnych włókien PA6. Wyniki wykazały, że materiały luminescencyjne były rozproszone równomiernie we włóknach bez widocznych aglomeratów. Żółte pigmenty nieorganiczne i materiał luminescencyjny mogą powodować obniżenie stopnia krystalizacji włókien PA6. Włókna luminescencyjne emitowały długotrwałą fosforescencję z pikiem drgań przy 360 nm. Krzywe zaniku wykazały, że żółty pigment nieorganiczny zwiększa jasność luminescencyjnych włókien PA6. Luminescencyjne włókna PA6 charakteryzowały się niską czystością kolorów i wysokim współczynnikiem oddawania barw. Nie stwierdzono żadnej różnicy pomiędzy kolorami emisji luminescencyjnych włókien; barwy luminescencyjnych włókien były podobne do barwy dodanych pigmentów.

Słowa kluczowe

EN

SrAl2O4; Eu2+; Dy3+; luminous fibre; luminescent property; colour characterization

PL

SrAl2O4; Eu2+; Dy3+; włókno luminescencyjne; charakterystyka kolorów

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2016
• Tom: Vol. 24, no. 3 (117)
• Strony: 38--43
• Opis fizyczny: Bibliogr. 15 poz., rys., tab.

Twórcy

autor

Yan Y.

• School of Fashion Design & Engineering, Zhejiang Sci-Tech University (ZSTU), Zhejiang, P. R. China

autor

Zhu Y.

• College of Textiles and Garments, JiangNan University, WuXi, P. R. China

autor

Ge M.

• College of Textiles and Garments, JiangNan University, WuXi, P. R. China

Bibliografia

• 1. Katsumata T, Nabae T, Sasajima K and Matsuzawa T. Growth and characteristics of long persistent SrAl2O4- and CaAl2O4-based phosphor crystals by a floating zone technique. Journal of Crystal Growth 1998; 183(3): 361-365.
• 2. Dong Wang, Qingrui Yin and Yongxiang Li et al. Conentration quenching of Eu2+ in SrO2 ·Al2O3: Eu2+ phosphor. Journal of Luminescence 2002; (97): 1-6.
• 3. Ren Chen, Yinhai Wang, Yihua Hu, Zhengfa Hu and Cheng Liu. Modification on luminescentproperties of SrAl2O4:Eu2+, Dy3+ phosphor by Yb3+ ions doping. Journal of Luminescence 2008; 128(7): 1180-1184.
• 4. Jishu Zhang and Mingqiao Ge. A study of an anti-counterfeiting fiber with spectral fingerprint characteristics. The Journal of The Textile Institute, 2011, 102(9): 767-773.
• 5. Siggel A, Potrawa T and Langheim H. Luminescent fibers, method for producing same and their use. Patent application CN19998002369 19990122, Germany. Priority number: DE 19981002588 19980123; Page bookmark: CN1289377(A).
• 6. Shirai T, Sakakura H, Shimizu Y, Ogura A and Goto T. Highly bright luminous fiber and method for producing the same and woven or knitted fabric comprising the same. Patent application 205343 Japan, 2001, Publication 194623, 2002.
• 7. Shuji M and Shiro S. Polyester fibers containing luminescent substances and their manufacture. Patent application: 285806, 2003, Japan.
• 8. Shim E, Pourdeyhimi B and Little TJ. Luminescence and mechanical properties of photoluminescent core bicomponent fibers. Textile Res J 2004; 74: 982– 988.
• 9. Ge Mingqiao and Yu Weiguo. The manufacturing method of rare earth luminous fiber with colorful light. Patent application 200410044898.9, China.
• 10. Ge Mingqiao, Tang Guoliang, and Yu Weiguo. Rare earth luminous fiber with colorful light and the manufacturing method of the luminous fiber. Patent application 200810019749.5, China
• 11. Yanna Xu and Mingqiao Ge. Study on the friction and wear resistant of luminous fiber. Knitting Industries 2008; (4): 17-19.
• 12. Wang L H, Wang W, Zhang W G, Kang E T and Huang W. Synthesis and luminescence properties of novel Eu-containing copolymers consisting of Eu(III)-acrylate-β-diketonate complex monomers and methyl methacrylate. Chem. Mater. 2000; 12(8): 2212.
• 13. Xiao LÜ, Sun Meng, Zhang Junying and Wang Tianmin. Effect of mixing process on the luminescent properties of SrAl2O4:Eu2+, Dy3+ long afterglow phosphors. Journal of RareEarths. 2010; 28(1): 150-152.
• 14. Du Haiyan, Li Gengshen and Sun Jiayue. Preparation of Non-Grinding Long Afterglow SrAl2O4:Eu2+,Dy3+Material by Microwave Combustion Method [J]. Journal of Rare Earths 2007; 25(1): 19-22.
• 15. Qin Xiao, Liyuan Xiao, Yingliang Liu, Xiaobo Chen and Yidong Li. Synthesis and luminescence properties of needle-like SrAl2O4:Eu, Dy phosphor via a hydrothermal co-precipitation method. Journal of Physics and Chemistry of Solids 2010; 71( 7): 1026-1030.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.